Studies on the resistance of DMDHEU treated wood against white-rot and brown-rot fungi
2005 - IRG/WP 05-10566
Beech wood (Fagus sylvatica) modified with the textile finishing agent 1,3 dimethylol-4,5-dihydroxyethylen urea (DMDHEU) has shown to improve durability against the white-rot fungus Trametes versicolor. In a mini-block test, the weight loss over eight weeks of incubation decreased with increasing weight percent gain (WPG) of DMDHEU. At 25% WPG, no significant weight loss was observed, while untrea...
P Verma, C Mai, A Krause, H Militz
Protection of wood for above ground application through modification with a fatty acid modified N-methylol/paraffin formulation
2007 - IRG/WP 07-40378
Hydrophobic chemical modification can be regarded as an alternative approach to conventional wood preservation using biocides in order to protect wood in hazard class 3 according the European Standard EN 335-1.
A formulation containing fatty acid modified N-methylol/paraffin and an aluminium salt catalyst was used to change the material properties of wood in order to protect wood from fungal dec...
Nguyen Hong Minh, H Militz, C Mai
The efficacy of commercial silicones against blue stain and mould fungi in wood
2008 - IRG/WP 08-30471
Scots pine (Pinus sylvestris L.) wood samples were vacuum pressure impregnated with quatsilicone micro emulsion (<40 nm particle size), aminosilicone macro emulsion (110 nm) and silicone macro emulsion with alkyl modified side groups (740 nm) and the resulting material properties were studied. Quatsilicone micro emulsion resulted in maximum bulking (4.8%) and anti-swelling efficiency (21.8%) in...
S C Ghosh, C Mai, H Militz
Effectos de la intemperización artificial sobre la madera de mezquite (Prosopis laevigata)
2008 - IRG/WP 08-40430
The effects of artificial weathering on Prosopis laevigata wood were studied on eight replicates (150 x 72 x 15mm (l x t x r)) free of knots, cracks and resin. The samples were exposed tangentially to UV light and to water spray during three cycles (1 cycle corresponded 1 week of artificial weathering). The conditioning time between each cycle was thirty days. The effects were measured according t...
A Carrillo-Parra, F Hapla, C Mai
Degradation of wood veneers by Fenton’s reagents: effects of low molecular weight phenolic compounds on hydrogen peroxide decay and tensile strength loss
2009 - IRG/WP 09-20400
Pine wood (Pinus sylvestris) veneers strips were incubated in acetate buffer containing hydrogen peroxide and iron to mimic mechanisms of brown rot decay and assess the degradation of cellulose through analysis of the tensile properties of the decayed wood. The tensile properties of thin wood strips treated with Fenton system reagents or precursors were determined and correlated to weight loss as ...
Yanjun Xie, R Well, Zefang Xiao, B Goodell, J Jellison, H Militz, C Mai
Weathering of Wood Modified with the N-Methylol Compound 1,3‑dimethylol-4,5-dihydroxyethyleneurea (DMDHEU)
2009 - IRG/WP 09-40467
Scots pine (Pinus sylvestris L.) sapwood boards were treated with a methylated 1,3‑dimethylol-4,5-dihydroxyethyleneurea (mDMDHEU) causing weight gains of approx. 25% and exposed to weathering for 18 months. Compared to untreated boards, treatment with mDMDHEU reduced surface discoloration mainly caused by staining fungi. Boards treated with mDMDHEU exhibited clearly lower moisture content th...
C Mai, Yanjun Xie, A Krause, K Urban, P D Evans, K Richter, H Militz
Protection mechanisms of modified wood against decay by white and brown rot fungi
2010 - IRG/WP 10-10713
The resistance of beech and pine wood blocks treated with 1,3-dimethylol-4,5-dihydroxyethylene urea (DMDHEU) against T. versicolor and C. puteana increased with increasing WPG. Full protection (mass loss below 3%) was reached at WPGs of approximately 15% (beech) and 10% (pine). Metabolic activity of the fungi in the wood blocks was assessed as heat or energy production determined by isothermal mic...
C Mai, P Verma, Yanjun Xie, J Dyckmans, H Militz
The Use of Micro-Tensile Testing to Assess Weathering Decay and Oxidative Degradation of Wooden Items
2010 - IRG/WP 10-20433
This paper presents a method to study the weathering performance of wooden items and to assess the oxidative degradation of wood via the Fenton reaction. Weathering resistance and photo-stability of wood was tested using pine wood (Pinus sylvestris) veneer strips measuring approximately 60 µm in thickness. The veneer strips were treated using a reactive chemical to impart surface protection. The ...
C Mai, Yanjun Xie, Zefang Xiao, P D Evans, H Militz
Termite resistance of wood modified with short- and long-chain siloxanes
2014 - IRG/WP 14-40660
Scots pine (Pinus sylvestris L.) sapwood specimens modified with short- and long-chain amino-functional siloxane emulsions were exposed to subterranean termites (Reticulitermes flavipes Kollar). Laboratory choice and no-choice tests following the standard EN 117 (2013) were conducted for 8 weeks in order to evaluate the influence of these silicon-based compounds on the termite resistance of treate...
P Gascón-Garrido, M-F Thévenon, H Militz, C Mai
Performance of some wood modification treatments against marine borers
2014 - IRG/WP 14-40668
Since some years, new treatment technology to protect wood against wood destroying fungi is introduced. Limited knowledge on their resistance to water organisms is available. Therefore, the resistance of chemically modified wood was assessed in a field test according to the European Standard EN 275 over a period of 3 resp. 5 years at sites in the North Sea and the Baltic Sea. Scots pine (Pinus syl...
A Klüppel, C Mai, H Militz, S Cragg