Microwave treatment to Accelerated fixation of copper-ethanolamine (Cu-EA) treated wood
2004 - IRG/WP 04-40271
This study evaluated the use of microwave post-treatment to accelerate fixation of copper-ethanolamine (Cu-EA) treated 19 mm southern yellow pine sapwood cubes. Cubes were pressure treated at 3.2 and 6.4 kg/m3 Cu retention target, after which they were microwave post treated during different duration periods. An accelerated AWPA leaching test was conducted during 300 hours to determine the amount...
Jinzhen Cao, D P Kamdem
Microdistribution of Copper in Copper-Ethanolamine (Cu-EA) Treated Southern Yellow Pine (Pinus spp.) related to density distribution
2004 - IRG/WP 04-40270
The relationship between copper absorption and density distribution in wood cell walls was investigated in this study. The density distribution on layer level was obtained from two approaches: (1) calculation by using data obtained from literature; (2) microdistribution of carbon and oxygen atoms in the wood cell. The microdistribution of carbon and oxygen in untreated southern yellow pine (Pinus ...
Jinzhen Cao, D P Kamdem, E Pasek
Copper fixation in ACQ-D treated Chinese fir at various temperature and relative humidity conditions
2007 - IRG/WP 07-30436
In this study, the effect of different conditions of temperature, relative humidity, and duration of post-treatments on accelerating copper fixation in ACQ-D treated Chinese fir wood blocks was investigated. The conditions include the combination of three temperatures (21, 50, and 70?) and two relative humidity levels (20% and 80%), also include four temperatures (50, 70, 90, and 110?) without con...
Jinzhen Cao, Lili Yu
Primary Study on Compressed Preservative-treated Wood (CPW) for Outdoor Applications
2008 - IRG/WP 08-40412
In this study, the compressed wood samples pre-treated with hot water bath or water spraying were immersed in the ammoniacal copper quat –type D (ACQ-D) preservative solution to get compressed preservative-treated wood (CPW). The liquid absorption and the recovery rate of compression deformation of the compressed wood was determined, as well as the surface hardness, the distribution of density a...
Jinzhen Cao, Jia Mao
Accelerated fixation of ACQ-D treated Chinese fir with different post-treatments
2008 - IRG/WP 08-40400
With the enhanced focus on the environmental impact of the preservative-treated wood in recent years, it is necessary to perform some post treatments to prevent contamination of soil and ground water and reduce copper losses from ACQ treated wood in service. In this study, the potential of hot air, hot water, steaming and microwave post treatments to accelerate the fixation of copper in ACQ-D trea...
Lili Yu, Jinzhen Cao, P A Cooper
Accelerated weathering of nine tropical wood species from Cameroon
2009 - IRG/WP 09-10705
The natural durability of tropical species for building components has been a subject of recent concern and questioning, mainly the resistance to weathering. Weathering resistance of nine tropical species from Cameroon, namely Azobe, Bilinga, Bubinga, Teak, Dousie, Moabi, Musanga, Sipo and Padauk were evaluated using an accelerated weatherometer for 2016 hours. Measurement of moisture fluctuation,...
S Pankras, Jinzhen Cao, D P Kamdem
Leaching performance, decay and termite resistance of wood treated with boron compounds incorporated with phenol-formaldehyde resin
2009 - IRG/WP 09-30503
A resol-type phenol-formaldehyde (PF) resin was synthesized and designed to penetrate wood incorporated with boron compounds in order to immobilize boron in wood. The leaching performance, decay and termite resistance of treated wood was investigated. Three kinds of boron compounds, that is, boric acid (BA), borax (BX) and disodium octaborate tetrahydrate (DOT), were selected to mix with PF and tw...
Liping Yu, Jinzhen Cao
Properties of strand board bonded with ammonium pentaborate (APB) modified phenol formaldehyde resin
2009 - IRG/WP 09-40455
Ammonium pentaborate (APB) is combined with phenol formaldehyde (PF) resin in this study to develop a high-performance wood-based composite. The effect of APB and its combination with polyethylene glycol (PEG) on the physical, mechanical properties as well as formaldehyde emission of strand board were tested and compared with disodium octaborate tetrahydrateand (DOT) and zinc borate (ZB). The resu...
Wei Gao, Jinzhen Cao
Tensile stress relaxation of wood impregnated in different ACQ formulations at various temperatures
2009 - IRG/WP 09-40456
The reactions between ammoniacal copper quat (ACQ) constituents and wood components were investigated by tensile stress relaxation approach. Small wood samples were stressed and impregnated in ACQ solutions with different formulation including the ethanolamine (MEA) to copper molar ratio, copper (as copper oxide) to quat (as DDAC) weight basis, treatment temperature and also the solution concentra...
Lili Yu, Jinzhen Cao
Evaluation of ACQ-D treated Chinese fir and Mongolian Scots pine with different post-treatments after 20 months of exposure
2010 - IRG/WP 10-30530
The performance of alkaline copper quat-type D (ACQ-D) treated Chinese fir (Cunninghamia lanceolata Hook.) and Mongolian Scots pine (Pinus sylvestris Linn. var. mongolica Litv.) stakes after 20 months exposure in Chengdu and Guangzhou of southern China were evaluated according to AWPA standard E07-07. The ACQ-D treatments used two concentration levels (0.5 and 1.0%) and four different post-treatme...
Lili Yu, Jinzhen Cao, Wei Gao, Haitao Su
Effect of P/F ratio, PF concentration and treating method on boron leaching from wood treated with PF modified boron compounds
2011 - IRG/WP 11-30559
In order to immobilize boron in wood, three kinds of resol-type phenol-formaldehyde (PF) resin with different P/F ratios were synthesized in laboratory and incorporated with three types of boron compounds to treat wood. The used boron compounds included boric acid (BA), borax (BX) and disodium octaborate tetrahydrate (DOT). The leaching test of boron from wood blocks was performed according to the...
Liping Yu, Jinzhen Cao
Termite resistance of wood impregnated with phenol-formaldehyde (PF) modified boron compounds
2012 - IRG/WP 12-30604
In order to investigate the effect of phenol-formaldehyde (PF) modified boron compounds on termite resistance of two main plantation-grown wood species, namely, Masson pine (Pinus massoniana Lamb.) and Chinese fir (Cunninghamia lanceolata (Lamb.) Hook.), laboratory termite tests and field tests were carried out according to AWPA standard E1-97 and AWPC protocols/2007. Different concentrations of b...
Jinzhen CAO, Liping YU, Xuexiang HE
Hygroscopicity of wood after polyethylene glycol (PEG) impregnation and/or heat treatment
2013 - IRG/WP 13-40623
The hygroscopicity of wood after polyethylene glycol (PEG) impregnation and/or heat treatment was investigated by testing the water uptake, equilibrium moisture content (EMC) at various relative humidity levels, and contact angle of the poplar wood surface. The results showed that: (1) At the first moment, the heat treatment at temperatures lower than 160 ℃ did not reduce the water uptake be...
Weiyue Xu Yuan Zhu, Jinzhen Cao
Combined effects of thermal modification and ACQ-D impregnation on properties of southern yellow pine wood
2013 - IRG/WP 13-40637
In this study, samples of southern yellow pine sapwood were first thermally modified and then treated by the alkaline copper quat-type D (ACQ-D) wood preservative. Two heating temperature (180℃ and 220℃) and two concentrations of ACQ-D solution (0.9% and 1.35%) were used in the experiments. The combined effects of thermal modification and ACQ-D on leaching performance, mechanical prope...
Wang Wang, Yuan Zhu, Jinzhen Cao
Production of reactive oxygen species in the presence of oxidized iron and oxalate under conditions mimicking brown-rot fungal degradation of wood
2016 - IRG/WP 16-10861
The biochemical role of oxalate in the fungal solubilization of iron is well known, but additional information is needed on the role that oxalate plays in the brown-rot decay of lignocellulose. In this study iron sequestration from iron and iron oxide-hydroxides was assessed with regard to the function of a chelator-mediated Fenton (CMF) reaction and the generation of reactive oxygen species (ROS)...
Yuan Zhu, Liangpeng Zhuang, B Goodell, Jinzhen Cao, J Mahaney
A Comparison on Penetration of Silica Sol in Scots pine and Southern pine wood
2016 - IRG/WP 16-40722
Penetration is one of the most important issues to be considered in wood impregnation with various kinds of chemicals in liquid form. Scots pine (Pinus sylvestris) and Southern pine (Pinus spp.) are two frequently used wood species for treatment, such as preservative treatment. With the development of treating systems, some micro- or nano-sized aqueous modifiers are emerging in the market, which p...
Mingyang Sun, Jinzhen Cao
Modifying wood with paraffin wax emulsion impregnation and thermal modification: hydrophobization effect and mechanism of the combined treatment
2016 - IRG/WP 16-40726
The aim of this study was to enhance the water repellency of wood by a combined treatment of paraffin wax emulsion (PWE) impregnation and thermal modification. Two different treating procedures were used to modify the southern pine (pinus spp.). One is first PWE impregnation and then thermal modification, another is first thermal modification and then PWE impregnation. The treated samples were imm...
Wang Wang, Jinzhen Cao, Cong Chen
Fabrication and characterization of MicroPCMs filled wood-plastic composites: Effects of polyethylene glycol on melamine–formaldehyde shell material
2016 - IRG/WP 16-40728
Microencapsulated phase change materials (MicroPCMs) containing dodecanol were fabricated using melamine-formaldehyde (MF) or polyethylene glycol 200 modified melamine-formaldehyde (PMF) resin as the shell materials by in situ polymerization. Wood flour/high-density polyethylene (WF/HDPE) composites with MF shell MicroPCMs (MF-MicroPCMs) or PMF shell MicroPCMs (PMF-MicroPCMs) were prepared, respec...
Xi Guo, Jinzhen Cao
Effect of Particle Size on Wax Distribution in Paraffin Wax Emulsion Impregnated Wood
2017 - IRG/WP 17-40779
Paraffin wax emulsion impregnation has been a common eco-friendly approach for improving water repellency of wood. In this study, southern pine (Pinus spp.) and Scots pine (Pinus sylvesteris L.) samples were impregnated with paraffin wax emulsions of different solid contents and particle sizes, and then the time domain nuclear magnetic resonance (TD-NMR) was used to elucidate the influence of part...
Wang Wang, Jinzhen Cao, Yiheng Huang
Thermodynamic properties of furfurylated wood during moisture adsorption process
2018 - IRG/WP 18-40828
Furfurylation of wood seems a promising wood modification method considering the wide raw material source of furfuryl alcohol (FA) and overall performance of FA modified wood. However, the modification mechanism of furfurylation is still not clear and needs further investigation. In this study, poplar (Populus cathayana Rehd.) samples with the size of 1(R) mm × Ф4 mm, were impregnated with ...
J Wang, J Cao, T Yang, E Ma, W Wang
A Synergistically Stabilized Oil-in-Water Paraffin Pickering Emulsion Used in Wood Treatment
2018 - IRG/WP 18-40840
Pickering emulsions (emulsions stabilized by solid particles) are attractive as they have strong similarities with traditional surfactant-stabilized emulsions. In this study, an oil-in-water (O/W) paraffin Pickering emulsion system with satisfying stability and small droplet size distribution was developed by hydrophilic silica particles and traditional surfactants as mixed emulsifiers. The drople...
J Jiang, J Cao
Dimensional stability and decay resistance of montmorillonite- furfuryl alcohol modified wood
2019 - IRG/WP 19-40856
Poplar (Populus cathayana) wood was impregnated successively by organo-montmorillonite (OMMT; in concentration of 2%) and furfuryl alcohol (FA, in concentrations of 15%, 30% and 50%) in a two-step method to prepare OMMT-FA modified wood. The modified wood samples were characterized using X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). Moreover, wood physical and a...
L Zhang, J Cao
The anti-weathering mechanism of extractives in thermally modified Scots pine
2019 - IRG/WP 19-40880
Results from the electron spin-resonance spectroscopy (ESR) analysis indicated that thermally modification of wood can inhibit the generation of phenoxyl radicals during UV irradiation and consequently lead to the increase of the color stability of wood. In order to clarify the evolution and role of extractives in thermally modified wood during the process of weathering, the compositions of aceton...
H Shen, J Cao