Effect of fire retardants (monoammonium phosphate and diammonium phosphate, mixture of monoammonium phosphate and borax and ammonium sulphate) on beech wood with dipping and Lowry methods
2006 - IRG/WP 06-40350
In this study, the possibilities of using four kinds of chemicals as fire retardants with 12% concentration for beechwood (Fagus orientalis Lipsky) was surveyed. Providing testing samples that are related to the measurement of fire resistance properties according to JIS A-1321-1975 standard were evaluated. Wood samples were impregnated with Lowry and dipping methods. In this study, samples impregn...
M Akhtari, D Parsapajouh, M Arefkhani
Effect of fire retardants (monoammonium phosphate and diammonium phosphate, mixture of monoammonium phosphate and borax and ammonium sulphate) on beech wood with dipping and Lowry methods
2006 - IRG/WP 06-40350
In this study, the possibilities of using four kinds of chemicals as fire retardants with 12% concentration for beechwood (Fagus orientalis Lipsky) was surveyed. Providing testing samples that are related to the measurement of fire resistance properties according to JIS A-1321-1975 standard were evaluated. Wood samples were impregnated with Lowry and dipping methods. In this study, samples impregn...
M Akhtari, D Parsapajouh, M Arefkhani
Investigation of chemical changes in acetylated beech wood during weathering
2009 - IRG/WP 09-40460
In this study Beech wood (Fagus orientalis) acetylated and has been subjected to a variety of artificial weathering conditions (water only, light only, water and light together)in difference times (0,50,150 and 300 h), then wood surface analyzed using Fourier Transform Infrared spectroscopy (FTIR).Results shown that weathering process affected the functional groups on the wood surface. Light and w...
M Akhtari, M Arefkhani
Application of Nanotechnology in Wood Preservation
2010 - IRG/WP 10-30542
Nanotechnology can enable the development of a wide range of new or enhanced wood-based materials and products that offer cost-effective substitutes for nonrenewable . Wood and other lignocelluloses are heterogeneous natural polymer composites with large variations in physical and chemical properties. These natural materials are composed of cellulose, lignin, and hemicelluloses. The potential use ...
M Akhtari, M Arefkhani
Evaluation effect of kiln schedule on Warp, Twist, Bow and surface checks in Poplar Wood
2011 - IRG/WP 11-40565
In this research, to establish a kiln-drying schedule for poplar (Populus nigra) lumber with 75 mm thickness that cut down from North Khorasan province in Iran, with three schedules T5-D2 (Forest Product Laboratory), T5-D3 and T8-D5 were adapted for drying the lumbers down to the final moisture content of 8±2%. primary dry bulb temperature each three schedules was adjusted at 49,49 and 54°C and ...
M. Akhtari, M.Arefkhani
Effect of Nano and Micronized Particles as Wood Preservatives for Termite Control
2013 - IRG/WP 13-30620
Subterranean termites are a major factor in the biodegradation of wood constructor products. In this study the efficacy of wood treated with micronized copper, zinc oxide and their mixture was compared to that of wood treated with soluble amine copper oxide with subterranean termites in a laboratory test. All of the formulations tested were effective in controlling wood degradation by the termites...
M Akhtari, D Nicholas, A Rowlen, M Arefkhani
Effect of Nano and Micronized Particles as Wood Preservatives for Termite Control
2013 - IRG/WP 13-30620
Subterranean termites are a major factor in the biodegradation of wood constructor products.
In this study the efficacy of wood treated with micronized copper, zinc oxide and their
mixture was compared to that of wood treated with soluble amine copper oxide with
subterranean termites in a laboratory test. All of the formulations tested were effective in
controlling wood degradation by the term...
M Akhtari, D Nicholas, A Rowlen, M Arefkhani
The effect of acetylation on physical properties of beech (Fagus orientalis) and Alder (Alnus subcordata) wood
2016 - IRG/WP 16-40759
In this study the effect of acetylation on physical properties such as water absorption, volumetric swelling and anti-shrink efficiency (ASE) of beech and alder were investigated. After 24 hours soaking in acetic anhydride, in order to achieving two surface of weight gains, acetylated samples were heated in oven at 120 0C for 90 and 360 minutes. Then water absorption and dimensional stability in...