Your search resulted in 70 documents. Displaying 25 entries per page.
Fumigation of New Zealand grown western red cedar for export markets
2001 - IRG/WP 01-30262
The objective of this study was to demonstrate that methyl bromide fumigant penetrates into the centre of western red cedar (Thuja plicata L.) timber to meet the standard for export markets. Kiln dried western red cedar was used and a cavity (50x 30 x 13mm3) was prepared into the centre of each sample board (500 x 200 x 26 mm3 thick). An absorbent sachet used in industry for cross checking that th...
B Kreber, G Durbin, D Wilson
Water-Borne Copper Naphthenate: An Emerging Wood Preservative
2002 - IRG/WP 02-30280
Waterborne copper naphthenate (WB Cu-N) was used to treat southern yellow pine (Pinus spp) and red maple (Acer rubrum) stakes. The treated stakes were exposed in test sites located in Florida, Michigan and Mississippi for 3 to 6 years. Copper Chromium Arsenate (CCA),
Ammoniacal Copper Quat (ACQ) and Oil-borne Copper Naphthenate (OB Cu-N) were also used to treat some stakes for comparison. Results...
P Nzokou, D P Kamdem, M H Freeman
Leachability of didecyldimethylammonium chloride (a quaternary ammonium compound) from four wood species
1982 - IRG/WP 3204
Sapwood blocks prepared from red pine, ponderosa pine, southern yellow pine and hem-fir (a commercial mixture of western hemlock and amabilis fir) were treated with didecyldimethylammonium chloride, (an alkylammonium compound, AAC). After oven drying the blocks were vacuum impregnated with distilled water and subjected to a static leach cycle for 48 hours. The leachate was analyzed and the amount ...
J N R Ruddick, A R H Sam
Effect of climate, species, preservative concentration and water repellent on leaching from CCA-treated lumber exposed above ground
2001 - IRG/WP 01-50178
Few studies have examined leaching of chromated copper arsenate (CCA) from treated wood in above ground exposures due to the assumption that leaching is less severe compared to wood in continuous contact with soil or water. However, a significant portion of CCA treated wood is used for above ground applications, exposing considerable volumes of the preservative to precipitation and potential leach...
J L Taylor, P A Cooper
The efficacy of polymer/preservative treatments in soil-bed exposure
1992 - IRG/WP 92-3729
Southern pine was treated with CCA, CCB, sodium borax/boric acid, or disodiumoctaborate, alone or in combination with an acrylic polymer system containing a water repellent. Treated samples were subjected to an unsterile soil burial test. The addition of polymer reduced the weight loss in borontreated samples at the lower retentions but not at the higher retention. Results with borates indicate th...
R J Murphy, H M Barnes, S M Gray
Oxidation of wood components during CCA-C fixation
1993 - IRG/WP 93-30024
Pre-extracted radial sections of southern yellow pine sapwood were treated with CCA-C and analyzed by X-ray photoelectron spectroscopy (XPS). The ratio of C1 (carbon bonded to carbon and/or hydrogen) to C2 (carbon bonded to one oxygen) in XPS Cls spectra was taken as a measure of the progress of oxidation of wood components during CCA fixation. This ratio was 0.82 before CCA treatment and increase...
M Kaldas, P A Cooper
Step-wise pressure process for reducing surface roughness in Japanese cedar timber
2003 - IRG/WP 03-40256
Sixteen dried sawn-timber (10.5 x 10.5 x 360 cm) were cut into half. The half of them was treated by step-wise pressure process with 2.5 MPa maximum, and the other half was treated by conventional pressure process with 2.5 MPa maximum. Average DDAC preservative absorption was 461 kg/m3 in the former and 525 kg/m3 in the later. Surface roughness was expressed as the profile element height of collap...
K Yamamoto, M Nozoki
Effect of substrate type and moisture requirements in relation to colony initiation in two carpenter ant species
1999 - IRG/WP 99-10320
Conditions necessary for optimal colony initiation or the rate of initial colony expansion by early brood in the carpenter ant species Camponotus modoc and C. vicinus on various substrates conditioned to different moisture contents were studied. Camponotus modoc and Camponotus vicinus queens were placed in Douglas-fir, western red cedar and Styrofoam® blocks conditioned in sealed chambers at 70% ...
M E Mankowski, J J Morrell
Microdistribution of Copper in Copper-Ethanolamine (Cu-EA) Treated Southern Yellow Pine (Pinus spp.) related to density distribution
2004 - IRG/WP 04-40270
The relationship between copper absorption and density distribution in wood cell walls was investigated in this study. The density distribution on layer level was obtained from two approaches: (1) calculation by using data obtained from literature; (2) microdistribution of carbon and oxygen atoms in the wood cell. The microdistribution of carbon and oxygen in untreated southern yellow pine (Pinus ...
Jinzhen Cao, D P Kamdem, E Pasek
Imaging fungal deterioration of wood using x-ray microtomography
1997 - IRG/WP 97-10240
Nondestructive tomographic images of solid Southern yellow pine (SYP) wood and SYP during deterioration by wood decay fungi were obtained by using a new class of synchrotron X-ray computed microtomography (CMT). The CMT images will provide information about spatial relationship between degrading fungi and wood structures. Wood samples were scanned with synchrotron-generated X-rays at high resoluti...
B Illman, B A Dowd
Microwave modification of Yellow Stringybark (Eucalyptus Muelleriana) posts for impregnation with Copper-Chrom-Arsenic (CCA) preservatives
2000 - IRG/WP 00-40185
Yellow Stringybark posts with diameters ranging from 60-100 mm were microwave conditioned using a 60 kW microwave (MW) generator. A substantial improvement in heartwood penetration of preservatives and relaxation of growth stresses was indicated such that there was no split formation following drying of the posts. High preservative absorption of copper-chrome-arsenic (CCA) was achieved ranging fro...
G Torgovnikov, P Vinden
Evaluation of white-rot fungal growth on Southern Yellow pine wood chips pretreated with blue-stain fungi
2000 - IRG/WP 00-10349
White-rotting basidiomycetes do not colonize on southern yellow pine. This study seeks to reduce the resinous extractive content of southern yellow pine by treating it with blue stain fungi. The mycelial growth of wood-inhabiting ligninolytic white-rot fungi can be achieved on pretreated southern yellow pine wood. Aureobasidium, Ceratocystis, and Ophiostoma spp. removed 70% to 100% of the extracti...
S C Croan
Accelerated testing for out of ground contact using natural biological preconditioning
1996 - IRG/WP 96-20088
Small blocks made of Scots pine sapwood were treated, buried in vermiculite and exposed to natural microbial colonisation during outdoor exposure prior to laboratory decay testing. Periodic microbial isolations, moisture content, permeability and weight loss tests were also conducted. Bacteria and moulds colonised the vermiculite and miniblocks well. Aureobasidium pullulans was common on TnBTO tre...
S Molnar, D J Dickinson, R J Murphy
Microbial ecology of treated lap-joints exposed at Hilo, Hawaii for 12 months
1996 - IRG/WP 96-20089
Lap-joints made from Southern yellow pine treated with ACQ, DDAC or Propiconazole were exposed and sampled over 12 months. TnBTO treated Lap-joints were later exposed as a standard treatment. The moisture content of the joint area remained at 23% to 28%, but, away from the joint, varied between 20% to over 30%. Untreated samples had higher moisture contents and there was little difference between ...
S Molnar, D J Dickinson, R J Murphy
Amine copper reaction with wood components: acidity versus copper adsorption
1997 - IRG/WP 97-30161
The bonding sites for copper in wood from CCA, as well as ammoniacal/amine based systems, has long been a topic of investigation. Both phenolic and carboxylic functional groups have been discussed as potential bonding sites for copper. However, no consensus on the adsorption mechanism has been realized. Thus, the selective adsorption of copper in southern yellow pine from ethanolamine-copper solut...
S M Thomason, E A Pasek
Removing Cu, Cr and As from CCA treated yellow pine by oleic acid
2003 - IRG/WP 03-50202
In this study, CCA treated yellow pine utility poles were cut into three different dimensions and 4 different pH levels (2, 2.5, 3.5 and 5) of Oleic acid was used. The leached wood samples were collected at the end of the 1, 3, 7 and 14 days to determine the remaining Cu, Cr and As concentrations. The concentrations of Cu, Cr and As were determined by X-RF. The effects of pH, dimension and duratio...
E D Gezer, Ü C Yildiz, S Yildiz, E Dizman, A Temiz
CCA type C depletion of Southern yellow pine utility poles
1995 - IRG/WP 95-50049
Depletion and redistribution of preservative components were evaluated on five CCA-C treated poles in service for over six years in Conley, Georgia. A statistical approach was taken in which retentions below ground were compared to retentions above ground due to a lack of initial data on individual poles. It was hypothesized that the below ground retentions should be lower than the corresponding a...
P D Osborne, R F Fox
Comparative studies of natural durability of Japanese cedar (Cryptomeria japonica D. Don) among the geographic cultivates
2006 - IRG/WP 06-10592
Variation of natural durability of Japanese cedar (Cryptomeria japonica D. Don) (also known as Sugi) was investigated by accelerated tests for decay (Fomitopsis palustris (Berk. et Curt.) Murr.) and termite (Reticulitermes speratus Kolbe) attacks on 13 clones of Sugi trees from Kyushu-Okinawa Region (Fukuka, Ooita, Saga, Miyazaki, Kagoshima). For this purpose, 57 twenty-five years old Sugi trees o...
I Usta, K Takata, S Doi
Molecular characterization of M’jej, decaying agent of cedar forests in Morocco
2006 - IRG/WP 06-10593
Cedar wood is well appreciated since thousand years even though its economical importance is limited because of its world distribution restricted to some Mediterranean countries and Himalaya. The most important species, Cedrus atlantica have its biggest population in Morocco (130 000 ha) where it is submitted to fungal diseases. Among them, the locally named “M’jej” reduced notably saw mile ...
A Zaremski, S Bakkali-Yakhlef, C Chaintreuil, Y Abbas, Y Prin, M Abourouh, M Ducousso
Corrosion of metal fasteners in contact with copper preservative treated wood
2007 - IRG/WP 07-20370
The corrosion rates of metal fasteners in contact with alkaline copper quat (ACQ) treated wood with or without commercially available water repellent was compared to that of cedar. In this experiment, fasteners were sandwiched between two pieces of treated wood and exposed to a humid environment at a slightly elevated temperature. The use of a “sandwich” design allowed periodic examination of ...
BaekYong Choi, J N R Ruddick
Effects of heat treatments on decay resistance and material properties of ponderosa pine and yellow poplar
2007 - IRG/WP 07-40374
The potential for using heat treatment to improve the properties of North American fenestration species was evaluated on ponderosa pine (Pinus ponderosa L) and yellow poplar (Liriodendron tulipifera L) treated using the ThermoWood process at various treatment temperatures and times. Soil block tests using Gloeophyllum trabeum, Postia placenta, or Trametes versicolor showed that durability was enh...
C Vidrine, C Freitag, J Nicholson, J J Morrell
Development of a Weatherometer to Accelerate the Surface Checking of Wood
2008 - IRG/WP 08-20388
There is significant interest in developing preservatives that are better at preventing wood from checking. Currently, however, there is no accepted test methodology for accelerating the development of checks in wood samples so information on the effectiveness of treatments at restricting checking can be obtained more quickly. This paper describes the development of a new type of weatherometer (Ac...
R Ratu, P D Evans
Surface Characteristics of Southern pine treated with Eastern red cedar oil
2008 - IRG/WP 08-40393
Treatment of wood with various chemicals play an important role on their surface characteristics including as roughness and hardness for further processing such as finishing and machining. The objective of this study is to evaluate surface roughness of Southern pine (Pinus taeda L.) treated
with oil extracted from eastern redcedar (Juniperus viginiana L.). Both tangential and radial surfaces of...
S Hiziroglu
Effects of bleaching process on the roughness values of wood surfaces of Lebanon cedar (Cedrus libani A. Rich.) and Black poplar (Populus nigra L.) using NaOH (sodium hydroxide), H2O2 (hydrogen peroxide) and Ca(OH)2 (calcium hydroxide)
2008 - IRG/WP 08-40403
Technical progress in the wood industry has been rapid in recent times. In this case, the quality assurance of the consumer products aligned with aesthetics value appears as one of the most important parameters. Because of the outer appearance of goods exert an effect on customers, interest in production of high quality surfaces of wooden commodities has increased essentially based on the surface ...
I Usta, E Aydinlar
Improvement of the Fungal Resistance of Japanese Cedar by the ThermoWood Process
2008 - IRG/WP 08-40422
The effect of the ThermoWood Process on sapwood of the Japanese cedar, Cryptomeria japonica, was investigated. Seven matched specimens were cut from a sapwood board of Japanese cedar and subjected to thermal treatments according to the ThermoWood Process.
The decay resistance and chemical and physical properties of the treated specimens and untreated specimen were investigated. The decay test wa...
I Momohara, T Morita, S Shouho, A Yamaguchi