The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen


The performance of metal-chromium-arsenic formulations after 32 to 38 years' in-ground exposure in Australia
2000 - IRG/WP 00-30240
Two trials of metal-chromium-arsenic preservatives were exposed in-ground in Australia. In Trial 1, Pinus radiata stakes treated with Boliden K.33, Boliden S.25, Celcure A, Tanalith C and Tanalith CA were installed at Sydney and Narrandera in 1961/1962. In Trial 2, P. radiata and Eucalyptus regnans sapwood were treated with Celcure A, Celcure A21-N, Celcure A 21-O and Tanalith CA (new) and install...
G C Johnson, J D Thornton, J Beesley


Leaching from field test stakes. Part 2: The distribution in and leaching from different parts of test stakes
1994 - IRG/WP 94-50026
Field test stakes treated with Boliden K33 (copper, chromium and arsenic) and Cuprinol Tryck (CT86) (copper and N-alkylbenzyldimethylammoniumchloride) respectively were exposed in ground contact at two different test fields in Sweden and rejected due to decay after 2 to 28 years. Stakes treated with the same preservatives were also exposed during 7 years above ground. The test stakes have been ana...
F G Evans, B Nossen, M-L Edlund


Investigation of temperature effect on fixation of Celcure preservative (ACC) in Hornbeam (Carpinus betulus I)
2003 - IRG/WP 03-30304
In this research, the fixation speed of Celcure 2 % (ACC) preservative salt, under temperature of 30 ºC, 40 ºC and 50 ºC on intact wood specimens of hornbeam was investigated. For this purpose, blocks of wood with 2Í 2 Í2 cm dimensions of hornbeam were prepared and saturated with 2% ACC concentration by full-cell process. The specimens were put in three incubators at the above-mentioned temperatures. For measuring the percentage of fixation through time, the specimens were extracted by using hydraulic pressure equipment, under 70 Mpa pressure. The PH of extraction was measured with the method of Diphenyl Carbazid and by using spectrophotometer. This measurement was done continuously and the amount of 6-valence chromium concentration present in the extract was compared with the amount of chromium concentration in the primary solution and then the percentage of fixation was calculated. The results showed that the decrease in 6-valence chromium is accompanied with increase of PH, this due to absorption of positive hydrogen ion by 6-valence chromium for reduction to 3-valence chromium and also ion –exchange of active components with wood during the primary phase of fixation. Also, the time necessary for reaching complete fixation in intact wood in the fixation temperature conditions of 30, 40, 50 ºC were 98, 52, 24 hours, respectively. In general, the results showed that temperature has effective role accelerating of fixation process.
R Imani, R E Majdar, A Karimi


Leachability of active ingredients from some CCA treated and creosoted poles in service. A progress report after 10 years testing
1990 - IRG/WP 3627
CCA K33 TYPE B treated or creosoted poles, 10 pieces of each treatment type, have been monitored from the treatment plant to an electricity line, which was build up in Southern Finland in 1978. Preservative retention was determined by taking borings at four different levels: 1.5 m from the top end, 1 m above ground line, ground line and 0.5 m below ground. Determinations were made before setting u...
A J Nurmi


Leaching from field test stakes. Results from two different methods of analysis
1993 - IRG/WP 93-50013
Field test stakes treated with Boliden K33 containing copper, chromium and arsenic exposed at three different fields in Sweden and rejected due to decay, have in two studies been analysed regarding leaching and remaining preservatives. The stakes have been exposed during 20 to 43 years. The density of the stakes and content of copper, chromium and arsenic have been determined in the top part of th...
F G Evans, M-L Edlund