Dimensational stabilisation of wood
1981 - IRG/WP 3171
A review is given of the studies on the dimensional stabilisation of wood which have been carried out in the laboratory 5.14 "Wood Technology" since 1967. All stabilisation methods known have first been compiled from the available literature. Practical studies were then started. Wood was treated with monomers (styrene, methyl metacrylate, isocyanate), formaldehyde, tannin and sugar. Despite a sati...
A Burmester
Characteristics of thermally modified wood in vacuum
2004 - IRG/WP 04-40287
In commercial thermal wood modification processes nitrogen, steam or oil has been used for the reduction of oxygen content in the reactor atmosphere. In present study no special heating medium, but an initial vacuuming step has been used for this purpose. Mass loss, resistance to fungal decay, dimensional stability, bending strength and modulus of elasticity of heat treated wood were evaluated and...
G Rep, F Pohleven, B Bucar
Effect of aqueous polymer treatments on wood properties. Part 1: Treatability and dimensional stability
1990 - IRG/WP 3610
Partially air-dried sapwood of sweetgum (Liquidambar styraciflua) and southern pine (Pinus spp.) was treated with either aqueous polyacrylate or aqueous dimethyloldihydroxyethyleneurea (DMDHEU) solutions. Tests for dimensional stability were conducted on matched treated and untreated pieces. Measurement of the antishrink efficiency indicated that DMDHEU was a better stabilizer than the polyacrylat...
Z Ashaari, H M Barnes, R C Vasishth, D D Nicholas, D E Lyon
Impregnation of timber with tannin as a mean of improving its dimensional stability
1992 - IRG/WP 92-3695
The results of a joint project carried out at the Timber Division of LNEC under the 2nd research programme of the CEC DGXII - "Wood as a renewable raw material" entitled "Stabilization of wood by impregnation processes" is presented. Pieces Maritime pine timber was impregnated with tannin under pressure to see if the treatment with tannin improved the behavior of wood regarding its dimensional sta...
J S Machado
A new process for in situ polymerization of vinyl monomers in wood to delay boron leaching
1998 - IRG/WP 98-40110
Efforts were accelerated on effective use of boron compounds in wood preservation owing to their environmentally safe characteristics and relatively low costs in addition to their well-known high bioactivity and fire resistant properties. Although having these unique favorable properties, they are readily leachable from treated wood at humid conditions. Therefore, they had limited market for exter...
M K Yalinkilic, W Dwianto, Y Imamura, M Takahashi
Effects of heat treatments on decay resistance and material properties of ponderosa pine and yellow poplar
2007 - IRG/WP 07-40374
The potential for using heat treatment to improve the properties of North American fenestration species was evaluated on ponderosa pine (Pinus ponderosa L) and yellow poplar (Liriodendron tulipifera L) treated using the ThermoWood process at various treatment temperatures and times. Soil block tests using Gloeophyllum trabeum, Postia placenta, or Trametes versicolor showed that durability was enh...
C Vidrine, C Freitag, J Nicholson, J J Morrell
Water repellency and dimensional stabilIty of wodd treated with waterborne resin acids/TOR
2007 - IRG/WP 07-40364
Wood used in above ground applications such as decking undergoes undesired dimensional changes leading to the lumber warping, cupping, splitting, etc. This is a major concern to consumers but it can be reduced by treating lumber with a water repellent. The ability of resin acids, hydrophobic compounds naturally present in southern yellow pines, was examined as a possible water repellent. A wate...
T P Schultz, D D Nicholas, J Shi
Multivariate analysis of infrared spectra for the prediction of the mechanical performance and dimensional stability of thermally modified wood
2007 - IRG/WP 07-40367
The use of calibrated mid-infrared Fourier transform (FTIR) spectroscopy for predicting the main bending strength parameters of thermally modified wood is described for the first time. The analysis is based on the handling of OSC-filtered FTIR data from control and treated wood samples, using partial least squares (PLS) regression.
Sets of Norway spruce, Scots pine and Beech wood samples were th...
M M González-Peña, M D C Hale
The Effect of Heat Treatment on Water Absorption and Dimensional Stability of Anatolian Chestnut (Castanea sativa Mill.) wood
2008 - IRG/WP 08-40407
The heat treatment of wood is an environment-friendly method for wood preservation. This process improves wood’s resistance to decay and its dimensional stability. However, mechanical properties decrease in different ration because of density loss as a result of heat treatment. In this study, the effect of heat treatment on water absorption and dimensional stability at different relative humidit...
G Gunduz, D Aydemir
Material properties of acetylated beech plywood
2008 - IRG/WP 08-40425
The effect of acetylation process on dimensional stability and mechanical properties of plywood made by Oriental beech layers (Fagus orientalis Lipsky) were studied. The layers cut into sizes of 200×200×2 mm and acetylated in 120°C for 30 and 60 min.
Thickness swelling (TS%), water absorption (WA%) and anti-swelling¬ efficiency (ASE%) of specimens were measured. Mechanical properties (MOE, MO...
A Talaei
Improving the Dimensional Stability and Fire Resistance of OSB by Roller-Coating Panels with UV-Curable Finishes
2008 - IRG/WP 08-40434
Oriented strandboard was sanded and roller-coated with UV-cured finishes. The effects of these treatments on the surface roughness, dimensional stability and fire resistance of OSB were assessed. Sanding reduced the average roughness of OSB, but it had a smaller effect on maximum roughness because sanded boards still contained surface voids between some strands. Sanded boards absorbed less than ha...
P D Evans, I Cullis
Dimensional Stability of Nine Tropical Hardwoods from Cameroon
2009 - IRG/WP 09-10687
This study investigated the swelling behavior, rate of swelling and dimensional stability of nine tropical hardwood species from Cameroon, namely ayous (T. scleroxylon), bilinga (N. diderrichii), bubinga (G. tessmannii), iroko (C. excelsa), Makore (M. heckelii), moabi (B. toxisperma), movingui (D. benthamianus), teak (T. grandis) and zingana (M. brazzavillensis). Continuous swelling was monitored ...
S R Shukla, D P Kamdem
Evaluation of Water Repellency of Treated Wood Using Several Alternative Methods
2009 - IRG/WP 09-20419
In this study, the results of water repellency testing using a digital swellometer method for water-borne organic-preservative systems with water repellent additives are reported. The findings suggest that the traditional method of using matched untreated controls as a reference developed from historic solvent-based treatments for determination anti-swelling efficacy (ASE) may underestimate the a...
L Jin, A F Preston
Weathering of Wood Modified with the N-Methylol Compound 1,3‑dimethylol-4,5-dihydroxyethyleneurea (DMDHEU)
2009 - IRG/WP 09-40467
Scots pine (Pinus sylvestris L.) sapwood boards were treated with a methylated 1,3‑dimethylol-4,5-dihydroxyethyleneurea (mDMDHEU) causing weight gains of approx. 25% and exposed to weathering for 18 months. Compared to untreated boards, treatment with mDMDHEU reduced surface discoloration mainly caused by staining fungi. Boards treated with mDMDHEU exhibited clearly lower moisture content th...
C Mai, Yanjun Xie, A Krause, K Urban, P D Evans, K Richter, H Militz
Properties of thermally modified wood of Eucalyptus globulus from Spanish plantations
2009 - IRG/WP 09-40469
This article provides the results of a study about the properties of thermally modified wood of the Southern blue gum (Eucalyptus globulus L.) from Spanish plantations. Although this specie is mainly used for chipping to obtain boards and paper pulp, its high mechanical and strength properties provide great potential for structural use or different solid wood products. A comparison of the properti...
Ó González Prieto, M C Touza
The effect of chemical changes on the wood-moisture relationships in thermally-modified wood
2009 - IRG/WP 09-40473
Small specimens of three wood species were thermally modified following twenty schedules in the 190-245°C temperature range for treatment times between 0.3 and 16 h. Five wood-moisture relations were subsequently determined, namely: anti-swelling efficiency (ASE), movement, hygroscopicity (adsorption and desorption), transversal swelling (radial and tangential directions), and equilibrium moistur...
M M González-Peña, M D C Hale
Effect of preservative treatment on dimensional stability of plywood made of treated simul (Bombax ceiba) veneer
2012 - IRG/WP 12-40575
The dimensional stability such as thickness swelling and water absorption of plywood made of treated simul (Bombax ceiba) veneers were investigated after 2 hours and 24 hours soaking under water. The veneers were treated with hot water and cold water solution of borax-boric acid (1:1), neem leaves and mahogany seeds of different concentration (1:10, 1:20, and 1:40) at different treatment duration....
K Akhter, M Mahabubur Rahaman, A Ara
Effects of nano-wollastonite impregnation on fire resistance and dimensional stability of Poplar wood
2012 - IRG/WP 12-40595
The fire-retardant properties of Nano-Wollastonite (NW) in poplar wood (Populus nigra) were determined in this study. Some physical properties such as water absorption, volumetric swelling and Anti-Swelling Efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 standard for the fire-retarding properties, and ASTM D4446-2002 standard for the physical properties. Imp...
A Karimi, A Haghighi Poshtir, H Reza Taghiyari, Y Hamzeh, A Akbar Enayati
Improvement of the biological performance and dimensional stability of two tropical woods by thermal modification
2012 - IRG/WP 12-40605
Pink cedar wood and rubberwood were thermally modified at 230°C in air for 4 h or for 8 h, and then subjected to bending, compression and hardness tests to evaluate the effect of the treatment on these mechanical properties. The biological performance of the modified wood was also determined, according to EN113, and the dimensional stability measured by means of the anti-swelling efficiency. The ...
M M González-Peña
The effect of nanozycosil on the water absorption and dimensional stability of Beech wood
2012 - IRG/WP 12-40606
Zycosil is a clear penetrating water repellent. This product works by penetrating into the substrate and modifying the surface tension to inhibit water intrusion. Beech wood (Fagus orientalis) was modified by treatment with nanozycosil. Then water absorption and dimensional stability in terms of volumetric swelling percent and anti-swelling efficiency were determined and found to be improved on t...
M Ghorbani, F Bavaneghi
Differences between heat treated Pinus pinaster heartwood and sapwood
2012 - IRG/WP 12-40617
Heat treatment is a well known process to improve the durability and dimensional stability of less noble woods. The treatment can be applied for heartwood unlike the traditional treatments based on impregnation due to the difficulty of impregnating heartwood.
Pure sapwood and pure heartwood samples were treated in an oven at 190ºC and 200ºC for 2h, 4h and 6h. Dimensional stability, measured a...
B Esteves, L Nunes, I Domingos, H Pereira
Improving dimensional stability of thermally treated wood by secondary modification – potential and limitations
2014 - IRG/WP 14-40664
The potential of treating thermally modified wood with melamine resin to improve the dimensional stabilization is tested in this research. Two different boards of poplar (Populus ssp.) were cut into two halves. One half of each board was thermally modified (T1 and T2) in a commercial process, the other half was used as untreated reference material. The material was thermally modified using the vac...
G Behr, K-C Mahnert, S Bollmus, H Militz
Leachability and Dimensional Stability of Nanosilver-Steamed Densified Poplar
2014 - IRG/WP 14-40684
This study was aimed to investigate leachability and dimensional stability of nanosilver impregnated poplar (Popolus alba), steamed before hot compression. Wood samples were impregnated with nanosilver suspension (200 and 400 ppm) under pressure of 4 bar for 20 minutes. Steam treatment was carried out at 150°C for 2 hours. Then samples were compressed (33%) radially in a hot press at 170°C for 3...
G Rassam, A Talaei, A Ahmadi
Effect of a wood stabilizer on checking of red oak log sections
2015 - IRG/WP 15-30664
Abstract: Reduced check development and dimensional stability can be important attributes in wood products used for decorative applications. The potential for using a silane-based stabilizer product to reduce checking was assessed on red oak stem and log sections. Pressure treatment produced the largest uptakes, although the levels suggested that the solution had failed to completely penetrate th...
C S Love, J J Morrell
Investigation of Dimensional Stability and Coating Performance of Different Heat-Treated Poplar Wood Before and After Accelerated Aging
2015 - IRG/WP 15-40702
In this investigation, coating performance of heat-treated poplar wood (Populus tremuloioes) in different environments, before and after accelerated aging was studied. Specimens with 150×100×20 mm and 20×20×20 mm in dimensions were prepared. Heat treatments were performed in air, steam and linseed oil media. Specimens were coated by alkyd based stain. Adhesion strength before and after aging, ...
A Talaei, D Ansari Movahed, G Rassam