Your search resulted in 199 documents. Displaying 25 entries per page.
CCA Chemistry
1983 - IRG/WP 3268
A Pizzi
Checking of sodium pentachlorophenate fixation in wood
1990 - IRG/WP 3620
In order to estimate the volatilization of sodium pentachlorophenate from treated wood, wood samples treated with pentachlorophenate were analysed after various durations of an EN 73 weathering The results giving no clear evidence of volatilization, treated wood samples were put in a test chamber with precise climatic conditions, the air used in the experiment being analysed. The pentachlorophenat...
M Lamour, H Sageot
An Australian test of wood preservatives. - Part IV: The condition, after 35 years' exposure, of stakes treated with creosote oils and oilborne preservatives
2000 - IRG/WP 00-30241
This paper contains the first results dealing with creosote oils and oilborne preservatives from this in-ground field trial in Australia. The substrates impregnated with preservative were Pinus radiata D. Don sapwood and Eucalyptus regnans F. Muell. heartwood and sapwood. Data are reported from stakes exposed for 35 years at three Australian sites (Innisfail, Sydney, Walpeup). Comparisons were mad...
G C Johnson, J D Thornton
The variation in electrical resistance in the CCA-treated wood during the fixation
1989 - IRG/WP 3554
The curve commonly used in Scandinavia for describing the fixation period at different temperatures for CCA-impregnated wood is based on investigation by Dahlgren on the pH-variations in a mixture of sawdust and preservative solution. As far as we know there is no such investigation on solid wood. We have therefore measured the electrical resistance in CCA-treated solid wood to see if this will di...
F G Evans, B Nossen
Field Test Results after Nine Years for CCA and ACQ Preservative-treated Wood Fixed in Different Climates
2003 - IRG/WP 03-30303
During assessment of the ground contact stakes in the Norwegian test field, we have frequently found that the first visual rot attack is in the zone of the stakes, where the stakes have been in contact with each other during the fixation. These parts are usually light green, caused by the lack of light during fixation, compared to the rest of the stake surface, which has a darker colour.
To inves...
F G Evans
CCA fixation experiments. Part 2
1989 - IRG/WP 3505
CCA fixation in wood was measured by both squeezing solution from treated wood that had not been dried and analyzing the solution for copper, chromium and arsenic, as well as using a chromotropic acid test to detect the presence of chromium VI. Both methods provide useful information on the CCA fixation process and illustrate that chromium VI disappears as CCA becomes fixed within wood....
W S McNamara
Interaction mechanisms of F/Cr/As/B type preservative and wood
1981 - IRG/WP 3183
The paper reports results of investigations on the fixation of the components of a F/Cr/As/B preservative in wood and its lignin and cellulosic components....
N Ermush, I Andersone
Copper binding capacity of modified wood flour
1992 - IRG/WP 92-3709
Wood flour was modified by reaction with oxidising agents and CCA preservative. The copper chromium and arsenic were removed from the CCA treated wood flour by an acid leaching procedure. The modified wood flours were allowed to react with copper acetate solution and the level of copper fixation achieved was determined. The modified wood flours had greater affinity for copper ions present in solut...
N C Milowych, W B Banks, J A Cornfield
Effect of leaching temperature and water acidity on the loss of metal elements from CCA treated timber in aquatic conditions. Part 2: Semi-industrial investigation
1995 - IRG/WP 95-50040-13
In continuation of previous leaching research on the quantification and modelling of metal elements released from CCA treated timber, a series of experiments has been carried out dealing with the influence of temperature and pH of the relative aquatic environment. The leaching method used is the Dutch prestandard for building materials, a long term static leaching test simulating practical bank-sh...
G M F Van Eetvelde, W J Homan, H Militz, M Stevens
The use of zirconium as an inert fixative for borates in preservation
2001 - IRG/WP 01-30256
Stand-alone borates have been used in internal protected situations as wood preservatives for about 60 years. They have not been deemed acceptable for external situations because of their leaching characteristics. Work carried out to reduce the leachability of borates has been reviewed briefly here, and a specific fixation agent based on zirconium has been tested in standard leaching and decay tes...
J D Lloyd, J L Fogel, A Vizel
Literature survey on the permanence and distribution of salt-type wood preservatives
1969 - IRG/WP III 1B
The objective of this survey is generally to review some of the more important published work dealing with the distribution and permanence of salt-type waterborne wood preservatives in treated timber. The survey is limited to the major chrome-containing formulations and the classification system proposed by Becker (1964) has been adopted throughout.
CK - chromium, copper (copper, chrome); CKA - c...
Anonymous
Fixation of CCA in Pinus sylvestris after kiln-drying
1990 - IRG/WP 3594
Tanalith C Paste is 98% fixed and Tanalith Oxide C is 99% fixed irrespective of whether treated Pinus sylvestris is kiln or air dried. A schedule suitable for kiln drying of CCA treated Pinus sylvestris is described....
P Warburton, J A Cornfield, D A Lewis, D G Anderson
Co-operative field experiment. Performance of preservative-treated hardwoods with particular reference to soft rot: Report of condition of specimens installed in Victoria, Australia
1978 - IRG/WP 3118
J Beesley
Investigation of the fixation in wood of chromated zinc chloride and copperised chromated zinc chloride preservatives
1976 - IRG/WP 372
A biological method of evaluating the extent to which CZC and CCZC preparations are retained in wood in terms of the potential protection which they afford against destruction by Merulius lacrymans (dry rot) is given. CCZC is recommended for protection of wood under moderate leaching conditions, while the use of CZC under such conditions is not recommended....
V N Sozonova, D A Belenkov
Study on the treatment of construction timbers by diffusion methods
1983 - IRG/WP 3252
Several species of timber that could be used for constructional purposes have to be pressure impregnated before such use. Pressure impregnation requires expensive equipment, and needs specialized trained operators, etc, which is not possible in most parts of India. Some timbers cannot be pressure impregnated, but can be treated by diffusion. Diffusion treatments could protect these timbers with si...
V R Sonti, B Chatterjee
EPR investigations of interactions between ammoniacal Cu(II) octanoate and wood
1996 - IRG/WP 96-30110
Ammoniacal solutions of copper(II) octanoate [ C u . h l f . 2 . r h l f.(O2CC7H15)4], interactions of these solutions with wood and wood components, and leaching of copper(II) octanoate from impregnated wood samples, have been studied by electron paramagnetic resonance (EPR) method. It is still not clear if in the Cu(II) octanoate - water - ammonia system, Cu(II) remains in a (copper(II) octanoat...
F Dagarin, M Petric, F Pohleven, M Sentjurc
The influence of age on retention and fixation of CCA in pressure-treated Kenyan-grown Eycalyptus saligna: Summary of findings
2002 - IRG/WP 02-30296
The present study investigates the influence of age on retention and fixation of copper-chrome-arsenate (CCA) in Kenyan-grown Eucalyptus saligna. Samples for the study were obtained from sound trees aged 4, 8, 12, 16, 20 and 24 years.
Test samples were radially cut from round material to represent total sapwood and heartwood for each age class, and measured 50mm in thickness, 100mm long, with wi...
R Venkatasamy
The effect of treatment temperature on the biological performance of CCA treated wood
1990 - IRG/WP 3624
Birch and Scots pine sapwood blocks were treated with several concentrations of CCA at three different temperatures: 5, 20 and 35°C. The treated wood was maintained at the appropriate temperature for the fixation period. Leached and unleached samples were then exposed in a soft rot monoculture test using Chaetomium globosum and a brown rot monoculture test using Coniophora puteana. The treatment ...
S M Gray
4th Report on condition of panels at Sekondi, Ghana
1978 - IRG/WP 445
F F K Ampong
Ground contact performance of wood treated by the MSU process
1990 - IRG/WP 3609
Environmental concerns have prompted a renewed interest in accelerated fixation schemes for CCA-treated wood. Results from stake tests of southern pine (Pinus sp.) treated using a conventional Bethell cycle are compared with matched stakes treated using the MSU Process. The effects of adding boric acid to the preservative formulation are also discussed. Differences among test plots are discussed....
H M Barnes, T L Amburgey, R W Landers
The Chemical and Biological Properties of Polymeric Betaine
2009 - IRG/WP 09-30512
Didecyl polyoxyethyl ammonium borate (DPAB), also known as Polymeric Betaine, was developed as a co-biocide for chromium-free copper based wood preservatives in Europe in the 1980’s. DPAB as a wood preservative has been reported previously. This paper summarizes the chemical, physical, and biological properties of DPAB. ...
H Härtner, S Schmitt, Futong Cui, H M Barnes
Leaching of copper, chromium and arsenic from CCA-treated slash pine heartwood
1994 - IRG/WP 94-50020
Drying green slash pine with any of three high temperature drying schedules produced a product in which both the sapwood and the heartwood could be penetrated with CCA using a modified Bethell treatment schedule. Required H3 retentions were achieved in both sapwood and heartwood, from 200 litres per m³ charge uptake. Post-treatment fixation/drying was accomplished by three different regimes, incl...
M J Kennedy, G Palmer
Volumes and weights of different CCA-C treated wood poles, anchor logs and crossarms of REB at air dry condition
1996 - IRG/WP 96-40073
Researches revealed the unit volumes and weights at air-dry condition (12% MC) of different poles, anchor logs and crossarms species of REB from this world. The softwood products are lighter than hardwood products. Inversely the unit volumes of softwood poles are higher than those of hardwood poles. Red pine (Pinus resinosa), radiata pine (Pinus radiata), blue pine (Pinus wallichiana), fir (Abies ...
A K Lahiry
The course of fixation of Cu-Cr-As wood preservatives
1972 - IRG/WP 307
Copper-chrome-arsenic (CCA) preservatives in contact with wood result in an instant extensive increase of pH, because of ion-exchange and adsorption reactions with the wood. During precipitation of the active elements the pH continuously increases but reaches a maximum, when all chrome is consumed. Some of the early reaction products are unstable and slowly convert via dissolution into stable comp...
S-E Dahlgren
Chromium on the surface of CCA-treated wood
1978 - IRG/WP 386
Chromium in solutions of CCA preservatives is predominantly in the hexavalent state (Cr VI). It is well known that Cr VI is associated with dermatitis and skin ulceration in workers handling chromium containing products and processes. When reduced to the trivalent state, however, chromium is considerably safer. An essential part, therefore, of safety procedures in any chromium - using industry is ...
C R Coggins, P Hiscocks