Remedial ground-line treatment of CCA poles in service. A progress report after 28 months' testing
1988 - IRG/WP 3481
Remedial treatments of CCA-treated poles in service with incipient soft rot were carried out with boron rods, boron/glycol solution, boric acid paste, copper/creosote paste and a commercial product (DFCK paste) respectively. The micro-flora before remedial treatment and 6 months after as well as the spread of chemicals in the poles were reported in Document No: IRG/WP/3388. In this progress report...
B Henningsson, H Friis-Hansen, A Käärik, M-L Edlund
Chemical and biological investigations of double-vacuum treated windows after 5 years in service
1983 - IRG/WP 3219
In 1980 The Swedish Wood Preservation Institute initiated an investigation to study the degradation of TBTO and possible fungal attack in double-vacuum treated window joinery in service during 5 years. A hospital in Gothenburg was chosen that was built during 1969 to 1976. Both untreated and double-vacuum treated windows of Pinus sylvestris were used. A brown alkyl oil type paint (Nordsjö system ...
J Jermer, M-L Edlund, B Henningsson, W Hintze, S V Ohlsson
Leaching from field test stakes. Part 2: The distribution in and leaching from different parts of test stakes
1994 - IRG/WP 94-50026
Field test stakes treated with Boliden K33 (copper, chromium and arsenic) and Cuprinol Tryck (CT86) (copper and N-alkylbenzyldimethylammoniumchloride) respectively were exposed in ground contact at two different test fields in Sweden and rejected due to decay after 2 to 28 years. Stakes treated with the same preservatives were also exposed during 7 years above ground. The test stakes have been ana...
F G Evans, B Nossen, M-L Edlund
Tilting and vacuum treatment - two methods to obtain a non-dripping freshly treated timber
1989 - IRG/WP 3535
Modern impregnation plants are designed to prevent spread of impregnation solutions from the plant through leakage, etc. It is also important that freshly treated timber does not spread solutions through dripping on the storage area. To prevent this, the impregnation procedure is terminated with a vacuum period. In many plants in Sweden this period is minimized or even excluded to gain time. Inste...
I Johansson, M-L Edlund
Inorganic preservative levels in soil under treated wood decks after 8 years natural exposure in Borås, Sweden
2005 - IRG/WP 05-50233
Inorganic preservative components (Cu, Cr and As) were measured to a depth of 150 mm under deck structures made with Scots pine lumber treated with several different wood preservatives and installed in Borås Sweden 8 years ago. Higher contaminant levels were observed mainly under the drip lines and in the top 50 mm of soil. Under CCA treated decks, soil arsenic concentrations increased from ba...
P A Cooper, Y T Ung, M-L Edlund, J Jermer
Laboratory versus field tests for evaluating wood preservatives: A scientific view
1995 - IRG/WP 95-20076
The relative merits of field tests versus laboratory tests for evaluating wood preservatives are discussed. Many of the problems involved in interpretation of the results are similar for both types of test. One major problem is to select field sites or laboratory tests that are representative for the practical use of treated timber in ground contact. Decay tests with treated wood in unsterile soil...
T Nilsson, M-L Edlund
Evaluation of wood preservatives for Nordic wood preservation class AB
2002 - IRG/WP 02-30297
In the Nordic countries there are restrictions in the use of wood preservatives based on chromium and arsenic. For above ground use, class AB according to the Nordic system, only
copper based preservatives are allowed in Sweden. Thus several new preservatives, copper based or metal free are now used. They have been approved by the Nordic Wood Preservation Council after passing laboratory tests ag...
M-L Edlund, J Jermer
Chemical and biological investigations of double-vacuum treated windows after 7½ years in service
1985 - IRG/WP 3339
Earlier investigations of double-vacuum treated windows after five years in service have shown that tributyltin oxide (TBTO) degrades to di- and monobutyltin compounds and that the resistance of the wood against decay decreases. An investigation 2.5 years later of the same windows shows that the degradation of TBTO proceeds fast. After 7.5 years in service only 15-35% of the remaining organotin co...
M-L Edlund, J Jermer, B Henningsson, W Hintze
Exposure of preservative treated wood to terrestrial microcosms, pure cultures of fungi and in the field
1997 - IRG/WP 97-20114
Small stakes (5x10x100 mm3) of treated and untreated Pinus sylvestris sapwood were exposed in terrestrial microcosms with different soils, two taken from test fields in Sweden, one soil from a conifer forest and one garden compost soil. Stakes of the same size were also exposed to pure cultures of the brown and white rot fungi, Postia placenta and Phanerochaete chrysosporium. After exposure, weigh...
M-L Edlund
Durability of some alternatives to preservative treated wood
2004 - IRG/WP 04-30353
The environmental discussion in Sweden has lead to an increasing use of naturally durable domestic wood species and wood treated according to alternative methods for use above ground. A number of these alternatives have been tested according to field- and laboratory tests and compared to wood treated with preservatives for above ground use. Seven untreated wood species, four alternative wood treat...
M-L Edlund
Pretreatment decay in poles of Pinus sylvestris
1987 - IRG/WP 1329
Storage damage by blue stain and decay in poles before impregnation has been increasingly observed during recent years and there have been reports that salt-impregnated poles today are of lower quality because of incipient decay being increasingly common. The attacks may have started at the time of cutting and then continued during the period of seasoning at the plant, which could be as long as tw...
H Lundström, M-L Edlund
Leaching from field test stakes. Results from two different methods of analysis
1993 - IRG/WP 93-50013
Field test stakes treated with Boliden K33 containing copper, chromium and arsenic exposed at three different fields in Sweden and rejected due to decay, have in two studies been analysed regarding leaching and remaining preservatives. The stakes have been exposed during 20 to 43 years. The density of the stakes and content of copper, chromium and arsenic have been determined in the top part of th...
F G Evans, M-L Edlund
Acoustic technique for assessing decay in preservative treated wood
1998 - IRG/WP 98-20138
This study investigated the suitability of vibration techniques to assess the performance of wood preservatives in ground contact. Small stakes (10 x 5 x 100 mm3) of treated and untreated Scots pine sapwood were exposed to decay in lab-scale terrestrial ecosystems. Tests were conducted using three different soils including a garden compost soil, and soils obtained from a test field and a conifer f...
L Machek, M-L Edlund, R Sierra-Alvarez, H Millitz
Testing durability of treated wood according to EN 252. Interpretation of data from Nordic test fields
2006 - IRG/WP 06-20341
To evaluate the effectiveness of new wood preservatives intended for treated wood in ground use there is a European standard, EN 252. The test shall run for five years before any formal interpretation of the results can be made.
Due to environmental concerns, the use of wood preservatives based on copper, chromium and arsenic (CCA) has been restricted in recent years. As a consequence of restrict...
M L Edlund, F G Evans, K Henriksen, T Nilsson
Wood plastic composites from modified wood. Part 2 - Durability in laboratory decay tests
2006 - IRG/WP 06-40353
The decay resistance of wood plastic composites, WPCs, was tested according to modified versions of AWPA E10 (soil-block test) and ENV 807 (tests in three un-sterile soils, terrestrial microcosms, TMCs). The WPC materials were conically extruded profiles with 30% polypropylene content. The 70% wood content was untreated Scots pine sapwood, acetylated pine and heat treated Norway spruce, respective...
M Westin, P Larsson Brelid, M L Edlund, G Alfredsen
Durability of some alternatives to preservative-treated wood. Progress report 2: Results from field tests after 5 years’exposure
2007 - IRG/WP 07-30442
A number of alternatives to preservative-treated wood have been tested according to EN 252 (stake test) and a specially designed ground-proximity field test, the latter in Sweden as well as in Hawaii, USA. Seven untreated wood species and four alternative wood treatments labelled as environmentally friendly (acetylation, linseed oil, heat treatment, vinyl polymer) were included in the study. Four ...
M-L Edlund, J Jermer
Field trials of wood preservatives in UC3 retention. Part 1. Durability results after 13 years in and above ground
2010 - IRG/WP 10-30548
In 1996 an extensive field trial program was set up in order to obtain more data on wood treated with chromium and arsenic free preservatives in Use Class 3 retention. Apart from durability in and above ground, other features were also assessed, e.g. discoloration by staining fungi, depletion of active ingredients, weathering and corrosion of fasteners in con¬tact with the treated wood. Wood spec...
M Westin, J Jermer, M-L Edlund, P Larsson Brelid, I Johansson
Durability of alternatives to CCA-treated wood - Results from field tests after 11 years exposure
2013 - IRG/WP 13-30633
The present study was initiated as a consequence of restrictions against the use of CCA-type
wood preservatives in Sweden in the 1990s. New copper-based formulations were introduced on
the market and to some extent, also alternatives to preservative-treated wood, such as thermally
and chemically modified and linseed oil treated wood as well as heartwood of non-tropical
naturally durable wood s...
P Larsson Brelid, M-L Edlund