The secondary treatment of creosoted electricity poles with fused boron rods
1988 - IRG/WP 3485
After preliminary trials selected poles were treated at the groundline with fused boron rods. Early samplings showed that movement was slow in the dry heartwood but after six years the distributions obtained indicate that the system has merit for the treatment of the heartwood of poles in service....
D J Dickinson, P I Morris, B Calver
Treatment of Douglas fir heartwood with disodium octaborate tetrahydrate (Tim-BorÒ ) to prevent attack by the Formosan subterranean termite
1991 - IRG/WP 1487
Toxicity of disodium octaborate tetrahydrate (Tim-BorÒ) to Coptotermes formosanus Shiraki (Isoptera: Rhinotermitidae), and termite feeding on treated Douglas-fir heartwood were evaluated in laboratory and field tests. Feeding on filter papers impregnated with Tim-BorÒ solutions reduced but did not eliminate termite gut protozoan populations. In a forced-feeding laboratory assay, Douglas-fir hear...
M Tamashiro, R T Yamamoto, J K Grace
Developments in wood preservation processing techniques in New Zealand
1980 - IRG/WP 3143
P Vinden, A J McQuire
The effects of heat treatment on anatomical changes of beech wood
2004 - IRG/WP 04-40284
The effects of heat treatment on anatomical changes of beech wood (Fagus orientalis) naturally grown and intensively used in forest products industry in Turkey were studied.
The wood samples were cut into 2x2x3 cm and than conditioned at 25 °C and 65 % relative humidity for 3 weeks. Heat treatment was than applied to the wood samples at four different temperatures (130 °C, 150 °C, 180 °C and ...
Ü C Yildiz, Z Gerçek, B Serdar, S Yildiz, E D Gezer, E Dizman, A Temiz
Evaluation of a solid remedial wood preservative containing boron and fluorine
1993 - IRG/WP 93-30022
The fungicidal and termiticidal effectiveness of a new rod form of diffusible remedial wood preservative, containing disodium octaborate tetrahydrate/sodium fluoride and marketed as Polesaver Rod, was evaluated in laboratory tests against three species of basidiomycete fungi (Coniophora olivacea, Pycnoporus coccineus, Perenniporia tephropora) and two species of subterranean termites (Coptotermes a...
K J McCarthy, J W Creffield, L J Cookson, H Greaves
The Effect of Heat on the Retention of Ammoniacal Copper Quat (ACQ-AB) onto Scots Pine (Pinus Sylvestris L.) Wood
2008 - IRG/WP 08-40390
In this study, the sapwood of Scots pine (Pinus sylvestris L.) were treated with ammonical copper quat type (ACQ-AB), which is one of the environmentally friendly wood preservatives, by using soaking method as a functions of various temperatures and time. The results indicated that the retention behaviour of ACQ onto the wood was considerably affected by temperature of ACQ solution and treatment t...
M Hakki Alma, A Mukremin Kara
Study on the treatment of construction timbers by diffusion methods
1983 - IRG/WP 3252
Several species of timber that could be used for constructional purposes have to be pressure impregnated before such use. Pressure impregnation requires expensive equipment, and needs specialized trained operators, etc, which is not possible in most parts of India. Some timbers cannot be pressure impregnated, but can be treated by diffusion. Diffusion treatments could protect these timbers with si...
V R Sonti, B Chatterjee
Heat treated timber in Finland
2000 - IRG/WP 00-40158
Heat treatment permanently changes the physical and chemical properties of wood by means of high temperatures (150 - 240°C). Heat treatment darkens the colour of the wood. Heat treatment improves the equilibrium moisture content of the wood and the shrinkage and swelling of the wood is reduced. Very high temperatures improve the resistance to rot and also reduce the susceptibility to fungal decay...
T Syrjänen, E Kangas
Radio frequency heating times for sterilization radiata pine solid piles
2017 - IRG/WP 17-40815
In this work was sterilized wood packaging material of radiata pine, stacked as solid piles without stickers, for determining the heating times using radiofrequency treatment. The experiments were performed in a radio frequency semi-industrial equipment. The results showed that the radio frequency heating times increases with wood volume and that radio frequency treatments were faster than convent...
H Esquivel, V Sepúlveda, J Torres, L Salvo, R A Ananías
Ancillary properties of vapor boron-treated composites
2001 - IRG/WP 01-40210
This paper discusses the water absorption, thickness swelling, and internal bond strength of North American composites treated using a vapor boron treatment process. For oriented strandboard, high boron loadings led to lower internal bond strength and lower thickness swelling. Water absorption results were variable but no deleterious effect of treatment was noted. For medium density fiberboard, th...
W A Jones, H M Barnes, R J Murphy
Heat treatment of wood strands for OSB production: Effect on the mechanical properties, water absorption and dimensional stability
2002 - IRG/WP 02-40238
The effect of heat treatment on the mechanical and physical properties of commercial OSB strands was evaluated. Heat treatment was applied under inert atmospheric conditions to wood strands. The aim of this study was to examine the heat treatment parameters to achieve significant reduction of thickness swelling (upon exposure to moisture in service) without causing excessive
reductions in stren...
G J Goroyias, M D C Hale
Investigation of some technical properties of heat-treated wood
2003 - IRG/WP 03-40266
The objective of this study was to investigate some technical properties of heat-treated wood.
Wood heat-treated according to a process intended for wood in above-ground end-uses (European hazard class 3) was subject to the following:
· A delamination test according to EN 391 with glulam beams made of heat-treated pine (Pinus sylvestris) and spruce (Picea abies) laminations, assembled with PR...
C Bengtsson, J Jermer, A Clang, B Ek-Olausson
Vapour boron treatment of wood based panels: Further studies on mechanical properties
1993 - IRG/WP 93-30028
Samples of medium density fibreboard, chipboard and oriented strandboard were treated to two retentions of boric acid by vapour phase methods. The results of short term mechanical tests on this material were discussed by Hashim et al. (1992). The present paper discusses results with long term studies on bending and impact resistance with panel types. Long term tests of impact resistance showed no ...
R Hashim, R J Murphy, D J Dickinson, J Dinwoodie
Treating Eucalyptus tereticornis wood with boron: Optimizing treatment conditions
2005 - IRG/WP 05-40309
Even though Eucalyptus tereticornis wood is suitable for small timber purposes, being non-durable, it needs to be treated with preservative chemicals. As it is a heavy, hard and difficult to treat species, the possibility of using diffusible boron compounds was investigated. The present study explored the effect of impregnation conditions such as treatment schedule, concentration of treatment solu...
T K Dhamodaran, R Gnanaharan
Novel wood modification processes for window and cladding products
2004 - IRG/WP 04-40285
Because of the low natural durability and low dimensional stability of European wood species, the usage of wood for window frames has decreased dramatically during the last decade. In a joint project of several German research institutes and the window industry, following wood modification systems were compared.
heat treatment (3 different materials from 2 companies)
acetylation (pine sapwood an...
A Krause, C Hof, H Militz
Effects of artificial UV weathering and soft rot decay on heat treated wood
2005 - IRG/WP 05-40302
Oil and inert gas oven heat treated pine wood strips 100 µm thick were mildly heat treated (200°C, 30 mins linseed oil, 120 mins oven). Following treatment, specimens were exposed to UV weathering (300 hours) and decay by the soft rot fungus, Chaetomium globosum. The effects of each treatment were assessed by zero span tensile testing, microscopy and by FTIR.
Tensile testing of heat treated s...
M D C Hale, S C Ghosh, M J Spear
The hydrolysis of organo-boron compounds in treated particleborard
2000 - IRG/WP 00-40180
Standard particleboard (manufactured for interior applications) was treated with trimethylborate and modified trimethylborate and then left to hydrolyse for specified periods. The percentage residual trimethylborate was determined by placing samples in kerosene and analysing the kerosene for boron after 3 days of leaching. There was a significant correlation between the percentage hydrolysis of tr...
K M Filcock, P Vinden
Vapour boron treatment of wood based panels: Mechanism for effect upon impact resistance
1994 - IRG/WP 94-40036
Samples of medium density fibreboard, chipboard and oriented strandboard (OSB) were treated to two retentions of boric acid by a vapour phase treatment. The results of a range of mechanical tests were reported by Hashim et al. (1992, 1993) in which a small reduction in impact resistance was observed. Several investigations were carried out to study how and where this loss in impact resistance occu...
R Hashim, R J Murphy, D J Dickinson, J Dinwoodie
Effects of heat treatment on water repellence and anti-swelling efficiency of beech wood
2002 - IRG/WP 02-40223
The heating of solid wood to higher temperatures is the simplest and the cheapest means for stabilizing its dimensions. For the investigation of the effect of thermal treatment on water repellency effectiveness and anti-swelling efficiency of beech wood (Fagus orientalis Lipsky), air-seasoned samples of beech wood were heated in presence of air at temperatures of 130 C, 150 C, 180 C and 200 C for ...
S Yildiz
Decrease of the antidecay resistance of beech wood treated with organotin fungicides after its natural ageing
1998 - IRG/WP 98-30185
The antidecay resistance of beech-wood samples (120 x 8.5 x 8.5 (MM)) treated with tributyltin fungicides gradually decreased due to prolongation of their natural ageing:
tributyltin fungicides (TBTO, TBTS, TBTCA, TBT-DEDTK were applied by pressure impregnation technique in ethanole solutions (c = 0. 1%, 0.33% or 1%);
treated beech-wood samples were naturally aged without their contact with grou...
L Reinprecht
Study of the degradation of retified wood through ultrasonic and gravimetric techniques
1994 - IRG/WP 94-40030
One of the non-polluting processes that increase the natural durability of wood is a thermal treatment in an atmosphere poor in oxygen, producing what is normally denominated "retified wood". In this study the validity of a non-destructive technique (ultrasound) in order to determine the biodegradation suffered by wood across time has been studied. For this reason, the behavior of a wood species (...
D T De Troya, A M Navarrete
Treatment of wood-based panel products with volatile borate
1990 - IRG/WP 3616
The paper presents recent developments in the use of volatile borate esters for the preservative treatment of wood based board materials. Several advances on previous reports are discussed. In laboratory studies, treatment times of approximately ten minutes at 20°C on boards at equilibrium moisture content provided full penetration and retentions of 1% wt/wt boric acid. Biological tests have been...
P Turner, R J Murphy, D J Dickinson
Incorporation of phenyl boronic acid treatment with vapor phase formalization
1997 - IRG/WP 97-40083
Phenylboronic acid (PBA) treatment was incorporated with vapor phase formalization (VPF) in order to increase dimensional stability and boron fixation as well as enhancement of biological resistance. Five and ten hours VPF were applied after PBA treatment as 0.34, 0.50, 1.00 and 2.00% concs. aqueous solutions. Anti swelling efficiency (ASE) attended to 71% in specimens impregnated with 0.50% PBA s...
M K Yalinkilic, S Yusuf, T Yoshimura, W-Y Su, K Tsunoda, M Takahashi
Natural exposure weathering tests: Their role in the assessment of wood preservative efficacy
1993 - IRG/WP 93-20006
Previous work has demonstrated the potential and usefulness of natural ageing procedures in e evaluation of wood preservative efficacy. This results from the combination of physico-chemical influences and microbiological interactions with both substrate and wood preservative. In this paper, results are presented for a range of biocide types. Discussions are centred on the value of natural exposure...
G R Williams, J Brown
Lifetime of impels in poles maintenance cycles for utility poles
2001 - IRG/WP 01-30258
In 1992-98 15.000-20.000 utility poles in Denmark received remedial treatment against decay with fused Boron-rods (IMPEL®). Economically simple, the Impel-rods are placed with the PillarTreat Method as concentrated depots in the ground-line. From there it is distributed by diffusion through the natural moisture in the wood, which ensures that it reaches moist wood in that parts of the pole where ...
A Peylo, C G Bechgaard