The effect of treatment temperature on the biological performance of CCA treated wood
1990 - IRG/WP 3624
Birch and Scots pine sapwood blocks were treated with several concentrations of CCA at three different temperatures: 5, 20 and 35°C. The treated wood was maintained at the appropriate temperature for the fixation period. Leached and unleached samples were then exposed in a soft rot monoculture test using Chaetomium globosum and a brown rot monoculture test using Coniophora puteana. The treatment ...
S M Gray
Visualization of inorganic element distribution in preservative treated wood by SEM-EDXA
2001 - IRG/WP 01-40208
SEM-EDXA was found to be an effective way of visualizing inorganic element distribution in wood as it was possible to examine some inorganic elements at the same time and map the concentration differences in color. Japanese cedar sapwoods were impregnated by vacuum treatment with CuAz or by pressure treatment with CCA preservatives and then distribution of Cu, Cr and As elements in wood were exami...
H Matsunaga, R Matsumura, K Oda
Effect of EDTA on removal of CCA from treated wood
2002 - IRG/WP 02-50182
Since substantial amounts of chromated copper arsenate (CCA) remain in the wood for many years, the disposal of CCA-treated wood causes escalating environmental concerns. Additionally, wood waste is generated when treated wood is put into service, for which environmentally benign disposal technologies need to be developed. Novel approaches to remove copper, chromium, and arsenic from CCA-treated w...
S N Kartal
Comparison of the effect of different soil sources on the type and rate of decay of CCA-treated pine exposed in a soil-bed
1984 - IRG/WP 2213
The types of decay observed in CCA-treated pine posts in horticultural situations in New Zealand can be reproduced using a soil-bed exposure. Radiata pine stakelets, untreated or treated to 1.4, 2.7, or 5.4 kg/m³ with Tanalith NCA, were exposed to six different soil sources. The local nursery soil used for all standard laboratory tests was found to represent the greatest decay hazard to untreated...
J A Drysdale
Marine performance of preservative treated Southern pine panels. Part 2: Exposure at Mourilyan Harbour, Queensland, Australia
2000 - IRG/WP 00-10337
Southern yellow pine panels treated with ACQ type B, ACQ type A, CCA type C, creosote, and copper naphthenate have been exposed at Mourilyan Harbour, north Queensland, Australia for almost 6 years. These panels have been inspected and rated for fouling and attack by Teredinid, Limnoria, Martesia, and Sphaeroma during this exposure. After 70 months exposure, overall performance of ACQ type B was eq...
A R Zahora, A F Preston, K J Archer, S Kleinschmidt
Testing a diffusion and reaction model for the leaching of CCA components from unfixed CCA-treated wood
2002 - IRG/WP 02-50193
A previously described physical model applicable to the leaching of any substance undergoing a first-order fixation reaction with wood is applied to the leaching of CCA components from unfixed wood. Using this model and laboratory leaching experiments with small wood samples immersed in water, the diffusion coefficients and reaction rate constant of Cr6+, total Cr, Cu and As in unfixed CCA-treated...
L Waldron, P A Cooper
Highly virulent wood-rotting Basidiomycetes in cooling tower timbers
1995 - IRG/WP 95-10125
Over the past ten years most industrial cooling towers changed their water treatment systems in order to meet environmental requirements. Since this alterations wood rot attack has been reported more frequently. Several Basidiomycete fungi were isolated and determined. Amongst the most important ones are strains of Physisporinus vitreus (Pers.:Fr.) P. Karst., Phellinus contiguus (Fr.) Pat. and Don...
J Van Acker, M Stevens, V Rijckaert
Leaching of copper, chromium and arsenic from CCA-treated slash pine heartwood
1994 - IRG/WP 94-50020
Drying green slash pine with any of three high temperature drying schedules produced a product in which both the sapwood and the heartwood could be penetrated with CCA using a modified Bethell treatment schedule. Required H3 retentions were achieved in both sapwood and heartwood, from 200 litres per m³ charge uptake. Post-treatment fixation/drying was accomplished by three different regimes, incl...
M J Kennedy, G Palmer
Bending properties of treated western hemlock plywood
1996 - IRG/WP 96-40064
This study investigated the mechanical properties of western hemlock plywood after treatment with waterborne preservatives and redrying. Unlike previously reported results for southern pine plywood, western hemlock plywood was more sensitive to redrying temperature than to preservative treatment. Generally, western hemlock plywood was affected by temperature and other variables. Losses in mechanic...
H M Barnes, A Khouadja, D E Lyon
Isolation and identification of bacteria from CCA-treated eucalypt power transmission poles
1987 - IRG/WP 1317
Bacteria have been isolated from CCA treated Eucalyptus maculata poles which possessed characteristic bacterial decay patterns. Cultures were isolated on a number of different media which had been inoculated with a splinter of degraded wood. Primary tests indicated that most isolates belonged to the genera Pseudomonas and Bacillus. The species Pseudomonas cepacia was most frequently isolated....
G A Willoughby, A C Hayward, L E Leightley
Leaching of CCA preservative from treated timber in marine environment
2001 - IRG/WP 01-30254
Knowledge on the amount of preservatives leaching out of treated wood is essential to optimise the chemical loading in various species of timber required for different end uses. In order to gain more insight into this aspect, the residual CCA content in 40 treated timber panels belonging to 14 species removed on destruction by marine organisms from a series of durability tests conducted in Kochi w...
M V Rao, V Kuppusamy, K S Rao, L N Santhakumaran
Volumes and weights of different CCA-C treated wood poles, anchor logs and crossarms of REB at air dry condition
1996 - IRG/WP 96-40073
Researches revealed the unit volumes and weights at air-dry condition (12% MC) of different poles, anchor logs and crossarms species of REB from this world. The softwood products are lighter than hardwood products. Inversely the unit volumes of softwood poles are higher than those of hardwood poles. Red pine (Pinus resinosa), radiata pine (Pinus radiata), blue pine (Pinus wallichiana), fir (Abies ...
A K Lahiry
Leaching of CCA components from treated wood under acidic conditions
1993 - IRG/WP 93-50004
The leaching of CCA components from treated wood under acidic conditions were investigated. Western hemlock treated with three types of CCA and two levels of target retention was subjected to leaching at four different levels of pH. After leaching tests, leached samples were subjected to laboratory decay and soft rot tests. The amount of CCA components leached was dependent on acidity of leaching ...
Jae-Jin Kim, Gyu-Hyeok Kim
Comparative environmental impact analysis of telecommunication utility poles: Treated wood and fibreglass
1999 - IRG/WP 99-50136
This study is aimed at providing the information necessary to assess the main environmental implications of different materials utilised in construction of utility poles. The study was performed on fibreglass and CCA treated poles timber. The work has been carried out by identifying and quantifying energy and materials used and wasted released during the entire life of the pole. The interactions w...
A Cugliandolo, M Onofrio, A Quaglino
Chromium on the surface of CCA-treated wood
1978 - IRG/WP 386
Chromium in solutions of CCA preservatives is predominantly in the hexavalent state (Cr VI). It is well known that Cr VI is associated with dermatitis and skin ulceration in workers handling chromium containing products and processes. When reduced to the trivalent state, however, chromium is considerably safer. An essential part, therefore, of safety procedures in any chromium - using industry is ...
C R Coggins, P Hiscocks
Comparisons of differences in electrical conductivity and corrosivity between CCA-oxide and CCA-salt treated wood
1981 - IRG/WP 3178
CCA preservatives have served well in many applications throughout the world. In developed areas it is the preservative in demand for clean dry paintable surfaces with long durability. In developing areas it is widely used for economic and logistical reasons. With the current emphasis on energy resources, the CCA preservatives are gaining greater acceptance as a substitute for hydrocarbon-related ...
J A Taylor
Examination of the Pilodyn as a non-destructive test method for detecting decay in CCA treated eucalypt poles
1982 - IRG/WP 2177
Below groundline condition of 274 CCA treated eucalypt poles comprising 13 different species was examined using 6 and 12 Joule Pilodyn units with 2 and 2.5 mm diameter pins. The data obtained was used to calculate regressions of density on pin penetration. A decrease in density was accompanied by an increase in pin penetration. The best correlation was found using the 6 Joule, 60 x 2.5 mm² diamet...
L E Leightley
The volatilization of arsenic on burning copper-chrome-arsenic (CCA) treated wood
1978 - IRG/WP 3111
Small scale burning experiments are described involving copper-chrome-arsenic treated wood. Approximately 20 per cent of the arsenic was volatilised when the wood was burned in air but 60 per cent when burned in an oxygen-enriched atmosphere, this increase is attributed to an increase in combustion temperature. Although a small increase in arsenic evolution was found with an increased concentratio...
A-J Dobbs, C Grant
Initial microbial colonisation of CCA-treated, creosote-treated and untreated Pinus sylvestris L. blocks in seawater
1996 - IRG/WP 96-10171
CCA-treated, creosote-treated and untreated Pinus sylvestris sample blocks were immersed in a seawater through-flow system for periods of between 1 and 265 hours. Samples were fixed immediately on removal and examined both qualitatively and quantitatively using the scanning electron microscope. This study of primary microbial colonisation showed differences between treatments in the diversity of m...
K Sturgess, A J Pitman
Ultrastructure of degraded, CCA-treated Pinus radiata wood from a marine pile
1990 - IRG/WP 1461
During an inspection of marine piles, 12 years after installation, severe degradation was noted on one of them in the vicinity of a corroded eye-bolt. The wood was dark brown in colour and tended to crumble easily. Wood fragments were examined by light microscopy and scanning and transmission electron microscopy and were also analysed for carbohydrates and lignin. Light microscopy showed numerous ...
A P Singh, M E Hedley
Moisture condition in treated wood exposed outdoors. A progress report after 5 years
1992 - IRG/WP 92-3720
Wood treated with water-borne preservatives, mainly CCA (copper, chromium and arsenic) and CCB (copper, chromium and boron) is often said to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed (Johansson 1977). In 1986 a project was started to compare water absorption during outdoor exposure between wood stakes of pine, Pinus sylvestris L, and spruce, P...
M-L Edlund
Mechanical resistance of Pinus radiata CCA treated and face jointed with PVA adhesive
1999 - IRG/WP 99-40140
Due to the increased use of Pinus radiata timber composites (laminated structural members, panels, etc), its low natural durability and the toxicity of phenol-formaldehyde type adhesives, a PVA (polyvinyl acetate) adhesive was evaluated in machined and rough CCA treated and untreated face joint samples under DIN 68602 (EN 204-205) standard for groups of requirement 3 and 4. The results showed that...
M C Rose, L Reyes, P León
A comparative study of CCA type C and B treated poles in service
1993 - IRG/WP 93-50001-05
CCA K33 type B and C treated utility poles, 9 pieces of each treatment type, were analyzed for preservative retention after 11 years in use. Borings were taking 1 m above and 0.3 m below the ground line. Also total amount of copper, chromium and arsenic was determined in soil surrounding the poles. The solubility of these active components in soil was monitored by using different leaching procedur...
A J Nurmi
Premature decay of CCA-treated pine posts in horticultural soils - An overview
1984 - IRG/WP 1241
The recent discovery in New Zealand of early decay in CCA-treated pine posts set in horticultural soils led to the establishment of a comprehensive research programme. The objectives and outline of this programme are presented together with an overview of research progress to date. Results suggest that premature decay of CCA-treated timber is restricted to material placed in highly cultivated soil...
J A Butcher
Sampling variation in a copper chrome arsenic treated power transmission pole
1990 - IRG/WP 2351
The Queensland Forest Service routinely samples poles treated at all treatment plants throughout the State. Each treatment plant is issued with a Certificate of Registration and the accompanying documents list the different levels of preservative retention required for performance in various service conditions. The posted levels represent the.minimum permissible, and it is to these concentrations ...
J Norton