Your search resulted in 563 documents. Displaying 25 entries per page.
Performance of Tebbacop in laboratory, fungus cellar and field tests
2000 - IRG/WP 00-30222
A novel organo-copper wood preservative ("Tebbacop") has been exposed to 12 years fungus cellar testing and 6 years above ground field testing. In the fungus cellar, Tebbacop at a retention of 0.053% Cu m/m oven dry wood out-performed CCA at a retention of 0.55% m/m oven dry wood. In above ground tests, L-joints treated to a Tebbacop retention of 0.012% Cu are performing as well as joints treated ...
M E Hedley, D R Page, B E Patterson
A new wood preservative based on polymerized complexes of aminotriazole with copper acetate
1998 - IRG/WP 98-30169
This paper presents the results of preliminary fungitoxicity tests as carried out on new polymerized complexes of aminotriazole with copper acetate (PCC) against Coniophora puteana and Trichoderma viride.
Laboratory tests on wood confirmed the findings arrived at in the screening test on agar medium. Deep penetration into pine wood of compounds studied was observed and particularly so at humidity...
K J Krajewski, A Lukasiewicz, J Wazny
Leaching of copper, chromium and arsenic from CCA-treated Scots pine exposed in sea water
2000 - IRG/WP 00-50149
A laboratory leaching trial combining a static and a flowing seawater system was carried out to measure the leaching rates of copper, chromium and arsenic from the surface of Scots pine panels vacuum-pressure treated to 3, 6, 12, 24, and 48 kgm-3 CCA. Untreated and treated panels were exposed in flowing seawater for up to 8 weeks followed by 2 weeks submersion in static seawater which was taken fo...
C J Brown, R A Eaton
Extracellular layers of wood decay fungi and copper tolerance
1983 - IRG/WP 1180
Extracellular layers around the hyphae of brown, white and soft rot fungi have been examined using electron microscopy. These layers were isolated for identification. Particular interest was directed towards the extracellular layers of copper-tolerant soft rot fungi....
D M Francis, L E Leightley
Collaborative field experiment: Analysis of copper and chromium in stakes of the four reference timbers
1982 - IRG/WP 3213
The stakes analysed belong to the Swedish set of the four reference timbers of the collaborative field experiment (Document No: IRG/WP/367). Before the field exposure 60 mm were cut off the end of each stake. This was done in order to be able to carry out chemical analyses as well as different types of testing. Some of the material has been used in softrot tests (Document No: IRG/WP/1151)....
T Nilsson
Report of meetings of remedial treatments Sub-group held in Madrid, Spain during 27-28 April 1988
1988 - IRG/WP 3502
J N R Ruddick
Reticulitermes lucifugus Rossi, and its damages in Turkey
1982 - IRG/WP 1152
The moist-wood termite, Reticulitermes lucifugus Rossi, is generally observed on the wood material which has a direct contact with the soil as trunks and fence stakes. It was reported to be found in some provinces in Turkey. The termite has been seen in these areas so far at the endemic level, but any considerable damage or epidemy has not yet been reported. Considerable damages were observed on t...
O A Sekendiz
Improved PEC preservatives with added biocides
1985 - IRG/WP 3322
Biocidal chemicals have been incorporated into formulations within the broad framework of pigment emulsified creosote (PEC) to provide novel potential multi-purpose preservatives. Preparations of PEC plus TCMTB, Boracol 40, copper ethanolamine nonanoate, Quatramine 80, arsenic trioxide, Troysan Polyphase, and CCA have been formulated and assessed for preserving ability in soil-jar and Accelerated ...
H Greaves, C-W Chin, J B Watkins
Testing of alkylammonium compounds
1981 - IRG/WP 2152
Following laboratory soil block tests which showed that Bardac 20 possessed a fungicidal threshold similar to that of chromated copper arsenate, treated ponderosa pine sapwood stakes were installed in a field test site near Vancouver, Canada. Two years after installation all the stakes show signs of fungal degradation. Seven stakes have been removed from the test due to total loss of strength afte...
J N R Ruddick
Leaching of Active Components from Preservative Treated Timber. Stage 1: Semi-Field Testing
2004 - IRG/WP 04-20302
The project is aiming at finding realistic leaching rates from preservative-treated wood in use class 3 (above ground). The project focuses on developing a field trial method for investigating leaching.
Panels are subjected to outdoor exposure under natural weather conditions at a test field at the Danish Technological Institute. The leachate is collected and monitored by chemical analysis of the...
N Morsing, B Lindegaard
Proposed test procedure to determine the effect of timber substrate on the effectiveness of a copper/chrome/arsenic preservative in seawater
1975 - IRG/WP 411
R A Eaton
Absorption of inorganic salts solutions. Retentions of inorganic salts. Fire retardants
1990 - IRG/WP 3625
The study aims evaluated the impregnation capacity using fire retardants on woods with differents densities. At the same time, impregnation with several fire retardant salts were carried out in order to obtain their absortion and retention in wood....
A Garcia, J Navarro
Comparative performance of pentachlorophenol and copper naphthenate in a long term field stake test
2000 - IRG/WP 00-30243
In this study the performance of copper naphthenate (Cu-Nap) and pentachlorophenol (Penta) treated pine stakes against decay and termite attack were compared at two test sites in Mississippi. Four different petroleum oils meeting AWPA Standard P9-A were used as carriers for these wood preservatives. After ten years exposure, the efficacy of Cu-Nap at a retention level of 0.05 pcf Cu was equivalent...
D D Nicholas, M H Freeman
Evaluation of wood treated with copper-based preservatives for Cu loss during exposure to heat and copper-tolerant Bacillus licheniformis
1999 - IRG/WP 99-20155
Copper-based wood preservatives need to be effective against exposure to all types of microorganisms. Wood treated with six copper-based preservatives was exposed to 121°C and 20 psi pressure for 15 minutes under standard autoclave conditions and the copper-tolerant bacterium, Bacillus licheniformis CC01, for 10 d at 28°C and 150 rpm. Sixteen to 37 percent of the copper was released from the woo...
D M Crawford, C A Clausen
An introduction to environmental aspects of groundwater arsenic and CCA treated wood poles in Bangladesh
1997 - IRG/WP 97-50081
The environment comprises biosphere, lithosphere, atmosphere and hydrosphere. Therefore, environmental science is a multi-disciplinary study, includes life sciences, physical sciences, chemical sciences, geology, geography, meteorology, forestry, agriculture, soil science, hydrology, ecology, public health, engineering etc. Tremendous industrial and mining activities, deforestation and population ...
A K Lahiry
Wood preservation in the Australian beekeeping industry
1988 - IRG/WP 3473
This paper reports the results of a survey of Australian commercial beekeepers working 200 or more hives in June/July 1985. Nine hundred and forty seven apiarists were asked to participate and to provide information on their wood preservation methods, painting procedures and maintenance of bee boxes. Three hundred and eighty-four apiarists returned completed questionnaires (41%). The main wood pre...
P J Robinson, J R J French
X-ray analysis of selected anatomical structures in copper/chrome/arsenic treated wood
1973 - IRG/WP 320
Application of analytical electron microscopy to problems in wood preservation has been very limited. Indeed, less than ten workers appear to have published their results using the technique, and of these' only two papers deal with energy dispersion procedures in the scanning electron microscope; the others employ the more familiar wavelength dispersive methods of the electron probe....
H Greaves
A laboratory soil-block decay evaluation of plywoods edge-treated with preservatives
1982 - IRG/WP 2174
Preservative-treated plywood used under conditions or severe decay hazard frequently has its original, or cut edges, protected by the application of a field-cut preservative. This study uses a laboratory test method to compare the efficacy of four commercial preservative treatments against two commonly occurring brown-rot fungi. The results are not meant to indicate the service life of such treate...
R S Smith, A Byrne
Copper naphthenate-treated Southern Pine pole stubs in field exposure. -Part 2: Chemical characterization of full size pole stubs 12 years after treatment
2000 - IRG/WP 00-30246
This study examines the influence of pre-treatment and post-treatment steaming on the character and physio-chemical nature of copper naphthenate in hydrocarbon solvent treated pine in larger, pole diameter, pole stub-length samples. This work is the continuation of two projects that began almost a decade ago. Previous reports indicated that certain morphological changes might occur in small labora...
H M Barnes, D P Kamdem, M H Freeman
Copper based water-borne preservatives: The biological performance of wood treated with various formulations
1987 - IRG/WP 3451
Wood samples treated with the various components of CCA preservative singly and in combination were tested against a soft rot organism, a copper tolerant brown rot organism and in soil burial both unleached and after leaching. The results suggest that, of the elements tested, fixed copper is essential for preventing soft rot attack and fixed arsenic is essential for preventing attack by a copper t...
S M Gray, D J Dickinson
Lignin-copper, a new wood preservative without arsenic and chromium
1992 - IRG/WP 92-3702
A more environmentally sound treatment for wood with preservatives containing no arsenic or chromium, has been developed and studied on a laboratory scale. The method involves a first step impregnation with an aqueous solution containing modified, water-soluble kraft lignin followed by a second step involving impregnation with a copper salt solution to give fixation of the lignin into a water-inso...
B Ohlsson, R Simonson
A field test with anti-sapstain chemicals on sawn pine timber in Finland
1986 - IRG/WP 3368
Fourteen formulations, each in two concentrations, were tested for effectiveness against sapstain, mould and decay on Scots pine (Pinus sylvestris L.) in a field test in South-Finland. The trial was commenced in June 1985 and finished in October 1985. During the test the boards were infected mainly by mould fungi. In kiln dried boards the protective effects of nine and in green boards of four trea...
L Paajanen
A wood preservative for the future: Copper dimethyldithiocarbamate
1994 - IRG/WP 94-30045
The development of a new wood preservative, copper dimethyl-dithiocarbamate (CDDC) is reviewed in this paper. CDDC is formed in situ by dual pressure treatments. Laboratory and field efficacy trials, physical and chemical properties of the preservative solutions and treated wood, and plant handling characteristics of the system are examined....
D K Stokes, M H Freeman, T L Woods, R D Arsenault
Soil-bed studies (Part 3): A cause of failure of multisalt preservatives following soil-bed exposure
1983 - IRG/WP 3261
P Vinden, J F Levy, D J Dickinson
Examen chimique du traitement de poteaux effectué à St-Michel s/Meurthe
1974 - IRG/WP 337
J Guillemain-Thévenot, C Jacquiot