Heat treatment of less-valuable Nigerian-grown Ceiba pentandra wood for improved properties
2006 - IRG/WP 06-40332
The hardwood Ceiba pentandra locally known as “ araba “ in Nigeria is rarely used for structural and construction works due to its high dimensional instability, low strength and durability values. Samples (10 x 10 x 150mm) were removed from four green boards (25 x 200 x 3000mm) of this species originating from a natural forest stand in Nigeria and subjected to 2-hour heat treatment at 160°C a...
Assessment of the ease of preservative treatment in the less-valuable Nigerian-grown Ceiba pentandra wood
2006 - IRG/WP 06-40330
The hardwood Ceiba pentandra locally known as “araba“ in Nigeria is rarely used for structural and construction works due to its high dimensional instability, low strength and durability values. Samples (25 x 50 x 600mm) were removed from four green boards (25 x 200 x 3000mm) of this species originating from a natural forest stand in Nigeria. The sapwood and heartwood were differentiated by me...
L Awoyemi, A J Pitman
Leaching of CCA from Bombax ceiba catamarans in operation for 15 years
2002 - IRG/WP 02-50191
Core samples of wood at random were collected from all the timber pieces of each of the three catamarans made of CCA treated logs of Bombax ceiba put to continuous service for the last 15 years at the Lawson's Bay fishing village, Visakhapatnam. The samples were dried to constant weight, powdered, digested and analyzed for the residual salts of the preservative. The residual content of ...
V Kuppusamy, M Balaji, M V Rao, K S Rao
Performance of Copper-Chrome-Arsenic (CCA) and Copper-Chrome-Boric (CCB) treated panels of Bombax ceiba and Paraserianthus falcataria against bio-deterioration at Krishnapatnam harbour, east coast of India
2003 - IRG/WP 03-30310
Results of investigations on the durability of light weight timber species (Specific gravity below 0.4) i.e., Bombax ceiba and Paraserianthus falcataria in treated and untreated condition conducted at Krishnapatnam harbour (Lat 13o28’ to 13o59’ N; Long: 80o10’ to 80o16’E) along the east coast of India are reported in the paper. Exposure trails were conducted with panels (Size: 30 x 3.8 x...
B Tarakanadha, N R Raveendra Prasad, K S Rao
The present status of wooden catamarans of the Indian Coast
1997 - IRG/WP 97-10231
Catamarans (a.k.a. kattumarams) are the most widely used fishing craft in India, and hundreds of thousands of poor, traditional fishermen depend on these vessels for their livelihood that are almost made entirely of wood. In recent years, acute shortages and phenomenal increases in prices of timber species used in catamaran fabrication have been reported, causing great hardship to the user communi...
K S Rao
Non-pressure preservation technique of five less durable timber species – Kadam (Anthocephalus cadamba), Shimul (Bombax ceiba), Pithalu (Trewia nudiflora), Am (Mangifera indica) and Boroi (Ziziphus jujube) of Bangladesh
2006 - IRG/WP 06-40322
Wood is a versatile renewable resource, which has been extensively used as a reliable construction material as well in furniture ever since the beginning of civilization. The Major disadvantage of wood is its susceptibility to biodeterioration by fungi, insects and bacteria. In tropical countries like Bangladesh, fungi is the most significant of these biodeterioration agents. Kadam (Anthocephalus...
G N M Ilias, A H Kabir, F Begum, M F Alam
Effect of borax-boric acid Treatment of simul (Bombax ceiba) Veneers on Glue-Bond Quality of Plywood
2010 - IRG/WP 10-40525
The glue-bond quality of plywood made of treated simul (Bombax ceiba) veneers was investigated. The veneers were treated with cold and hot water solution of borax-boric acid (BB) of different concentrations and treatment durations. The plywoods were made at three different pressures in hot press using urea formaldehyde glue. The glue-bond strength of untreated plywood in dry shear-test was found t...
K Akhter, Md Abul Hashem, S Akhter
Preservative Treatment of simul (Bombax ceiba) Veneers with Hot and Cold Water Solution of borax-boric acid by Soaking Process
2010 - IRG/WP 10-40528
Veneers of simul (Bombax ceiba) were treated with different concentrations of water- borne preservatives borax-boric acid (BB) by soaking process for different time periods. In the case of hot water treatment, it was found that the average retention of preservative chemicals increased gradually with the increasing treatment period from 20 minutes to 60 minutes. Similar trend was observed in the ca...
K Akhter, Md Abul Hashem, S Akhter
Effect of preservative treatment on dimensional stability of plywood made of treated simul (Bombax ceiba) veneer
2012 - IRG/WP 12-40575
The dimensional stability such as thickness swelling and water absorption of plywood made of treated simul (Bombax ceiba) veneers were investigated after 2 hours and 24 hours soaking under water. The veneers were treated with hot water and cold water solution of borax-boric acid (1:1), neem leaves and mahogany seeds of different concentration (1:10, 1:20, and 1:40) at different treatment duration....
K Akhter, M Mahabubur Rahaman, A Ara
Glue-bond strength of simul (Bombax ceiba) plywood made of Neem (Azadiracta indica) leaves treated veneers
2013 - IRG/WP 13-40647
The glue-bond qualities of plywood made of treated simul (Bombax ceiba) veneers were investigated. The veneers were treated with cold and hot water solution of neem (Azadiracta indica, A. Juss.) leaves of different concentrations and treatment durations. The plywoods were made at three different pressures in hot press using urea formaldehyde glue. The glue-bond strength of untreated simul plywood ...
K Akhter, M A Hashem, S Akhter