Your search resulted in 67 documents. Displaying 25 entries per page.
Chemical analyses of IRG/COIPM INTERNATIONAL MARINE TEST (to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water) samples
1987 - IRG/WP 4114
Chemical analysis of CCA and CCB treated timber was carried out after exposure at tropical and temperate marine sites. Results indicated that losses of all elements had occurred. In particular, losses of boron were severe. Arsenic and copper were also lost. The chromium components in both formulations was the most dominant metal remaining. The results suggest that chromium modification was importa...
L E Leightley
CCA fixation experiments. Part 2
1989 - IRG/WP 3505
CCA fixation in wood was measured by both squeezing solution from treated wood that had not been dried and analyzing the solution for copper, chromium and arsenic, as well as using a chromotropic acid test to detect the presence of chromium VI. Both methods provide useful information on the CCA fixation process and illustrate that chromium VI disappears as CCA becomes fixed within wood....
W S McNamara
Ultrastructure of degraded, CCA-treated Pinus radiata wood from a marine pile
1990 - IRG/WP 1461
During an inspection of marine piles, 12 years after installation, severe degradation was noted on one of them in the vicinity of a corroded eye-bolt. The wood was dark brown in colour and tended to crumble easily. Wood fragments were examined by light microscopy and scanning and transmission electron microscopy and were also analysed for carbohydrates and lignin. Light microscopy showed numerous ...
A P Singh, M E Hedley
Sampling variation in a copper chrome arsenic treated power transmission pole
1990 - IRG/WP 2351
The Queensland Forest Service routinely samples poles treated at all treatment plants throughout the State. Each treatment plant is issued with a Certificate of Registration and the accompanying documents list the different levels of preservative retention required for performance in various service conditions. The posted levels represent the.minimum permissible, and it is to these concentrations ...
J Norton
Monographic information on Serpula incrassata (Berk. and Curt.) Donk
1980 - IRG/WP 1128
J G Palmer, W E Eslyn
First draft of a monographic card for Gloeophyllum abietinum (Bull. ex Fr.) Karst
1973 - IRG/WP 116
T Hof
An investigation of organotin compounds in treated wood using Mössbauer spectroscopy
1983 - IRG/WP 3249
The influence of sample preparation on the 119mSn Mössbauer spectrum of tributyltin chloride in ponderosa pine was investigated. Initial studies with sawdust and compressed discs concluded that the latter were clearly superior. Further studies showed that compressed discs prepared from 0.4 g of treated wood and 0.1 g of cellulose were robust and gave excellent Mössbauer spectra. The possibility ...
J N R Ruddick, J K Ingram
The chemical nature of bis(tributyltin) oxide in Pinus sylvestris sapwood
1989 - IRG/WP 3508
Tributyltin compounds have been used for many years as wood preservatives. This study has provided, for the first time, an explanation for the previously reported dealkylation and/or volatilisation of the tributyltin species in, and from, Scots pine (Pinus sylvestris) sapwood. Thus, 119 Sn nuclear magnetic resonance studies have shown that, on impregnation into this timber, bis(tributyltin) oxide ...
S J Blunden, R Hill
Chemical and biological studies of organotin treated and painted wood stakes after outdoor exposure
1987 - IRG/WP 3419
Organotin based wood preservatives containing tributyltin oxide (TBTO) or tributyltin naphthenate (TBTN) are used in Sweden mainly for double-vacuum treatments of window joinery of Pinus sylvestris. After impregnation the joinery is painted or stained in different colours. To evaluate this effect (different colours on the degree of degradation of TBTO and TBTN, effected by different temperatures i...
M-L Edlund, B Henningsson
A light and electron microscopic study of decayed CCA-treated radiata pine (Pinus radiata) wood from a cooling tower
1994 - IRG/WP 94-10056
An inspection of an industrial cooling tower in New Zealand showed surface decay of 12 year old Pinus radiata wood panels treated with CCA preservative to a retention of around 15 kg/m³ of salt. Wood decay micromorphology typical of that caused by soft rot fungi, white rot fungi, 'stripy' and 'v-shaped' erosion bacteria and cavitation bacteria were all commonly...
A P Singh, R N Wakeling, D R Page
Microscopic characteristics of microbial attacks of CCA-treated radiata pine wood
1993 - IRG/WP 93-10011
Light and electron microscopic observations were made of CCA-treated radiata timbers, which had been placed in service in a vineyard soil as supporting poles and as part of a house pile, to determine the cause of their deterioration. The house pile had failed in service after between 9 and 13 years and was of particular interest because decay was more severe in deeper regions than at the surface a...
A P Singh, R N Wakeling
Zur Analytik von Pentachlorphenol und Tetrachlorphenol in der Luft und im Urin. [On the analytics of pentachlorophenol and tetrachlorophenolin the air and in urine]
1979 - IRG/WP 3139
Because of its excellent fungicide and insecticide properties PCP has been used for more than three decades in the field of wood preservation. Recently, however, its application has been criticized repeatedly. The motives for criticism were diseases, the origin of which was supposed to be closely connected with the use of pentachlorphenolic wood preservatives. The quantitative evidence of this sub...
A Dahms, W Metzner
Remedial ground-line treatment of CCA poles in service. Results of chemical and microbiological analyses 6 months after treatment
1986 - IRG/WP 3388
CCA-treated poles in service with incipient internal soft rot were remedially treated by inserting borate rods, brushing with a boron/glycol solution and injecting boric acid paste, copper/creosote paste or a commercial product (DFCK paste). The spread of active chemicals in the treated zone as well as the change in microflora have been studied with time. After six months chemicals had spread to m...
B Henningsson, H Friis-Hansen, A Käärik, M-L Edlund
Utilization of nitrogenous substance by Serpula lacrymans
1989 - IRG/WP 1397
When Serpula lacrymans degrades wood, the fungus is considered to have to assimilate nitrogen, which is not abundant in the wood, from the third material. The strands/mycelium has grown into the soil under the floor of the wooden house damaged by the dry rot fungus. The authors analyzed the soil samples collected from the ground under the floors of the dryrotted houses. The samples which were coll...
S Doi, I Togashi
Distribution of copper/chrome/boron preservative in light red meranti (Shorea leprosula) before and after exposure test for 72 months
1995 - IRG/WP 95-20073
Copper/chrome/boron (CCB) preservative at 6% w/w was impregnated into light red meranti (Shorea leprosula) by full cell process. The quantitative analysis for copper, chrome and boron contents in treated wood samples was carried out by Inductive Couple Plasma (ICP). Electron Probe Microanalyser (EPMA) was used to monitor the distribution of copper, chrome and boron in the various treated wood tiss...
S Salamah, S Ani
Emissions from the combusting of boron and fluoride containing wood
1995 - IRG/WP 95-50040-18
The combustion properties of waste wood and wood residues containing wood preservatives were investigated in several test series after having been blended with untreated wood at a ratio of 1:4. The results for CFB, SF and boric salt show that, provided an optimized combustion, the concentrations of the stack pollutants correspond approximately with those found for untreated wood. Only during the c...
T Salthammer, H Klipp, R-D Peek
Immuno-electron microscopic localization of extracellular metabolites in spruce wood decayed by brown-rot fungus Postia placenta
1990 - IRG/WP 1441
Degradation by Postia placenta in spruce and birch wood was shown to occur not only in the wood cell wall but also in the middle lamellae region. Middle lamellae was often found to be degraded along the centerline so that cells could separate along this line. Extracellular membrane structures were found surrounding the hyphae and this matrix labelled positively with antisera produced to Postia pla...
Y S Kim, B Goodell, J Jellison
A bioassay for appraising preservative protection of wood above ground
1978 - IRG/WP 2124
A bioassay, using the mold fungus Aspergillus niger, gave results that were correlated with amounts of pentachlorophenol and tributyltin oxide in pine sapwood treated with solutions ranging in strength from 0.016 or below to 5%. Limited bioassay estimates of penta in commercially treated millwork corresponded to estimates by lime ignition. The assay fungus exhibited somewhat greater tolerance of t...
T C Scheffer, L Gollob
The need for realism in wood preservation research. A key address
1983 - IRG/WP 3254
The approval of a chemical for use as a timber preservative and the design of in service retention requirements represents an act linking fundamental research and commercial timber preservation. How difficult is it to translate figures generated through controlled experimentation into working specifications and how confident can we be in the methods used to provide such figures? The chairman of Wo...
L E Leightley
Microscopic analysis of southern pine utility pole core segments
1992 - IRG/WP 92-1542
Fifteen macroscopic core descriptive categories were evaluated by microscopic analysis for accuracy in detecting decay and judging decay severity. Five categories were good indicators of decay as decay was detected in 28 of 48 samples. Five categories were possible indicators of early decay as decay was detected in 6 of 40 core segments and an additional 18 contained hyphae. The remaining five cat...
S E Anagnost, C J K Wang, M Wright
Formation of polychlorinated dibenzo-p-dioxins (PCDD) and polychlorinated dibenzofurans (PCDF) during the combustion of impregnated wood
1995 - IRG/WP 95-50040-19
Wood waste and industrial wood residues often contain various preservatives. The waste management for these residuals can be recycling, deposition or combustion. Among the three possibilities, combustion seems to be the most efficient way of disposal. To obtain detailed information about emissions of organic compounds with environmental impact, especially polychlorinated dibenzo-p-dioxins (PCDD) a...
T Salthammer, H Klipp, R-D Peek
Collaborative soft rot tests: Tests conducted at Princes Risborough and Delft on soil samples from collaborating laboratories
1972 - IRG/WP 210
The laboratories which took part in the original collaborative soft rot test (Savory and Bravery, Holz u Org 5 (1) 58-90, 1970) sent samples of the soil used in the original test to Princes Risborough. Portions of this material were sent to Dr Hof for soil analyses at TNO and the remainder was employed at Princes Risborough for the conduct of comparative tests of soil virulence when used as a comb...
J G Savory
Collaborative soft rot tests: Statistical treatment of results of soil analyses
1971 - IRG/WP 29
Institutes taking part in the collaborative experiments already reported forwarded samples of the soils employed in the tests to the Forest Products Research Laboratory, England. The soils were then autoclaved sterilised under uniform conditions and sent to the Department of Forest Soils, the Royal College of Forestry, Stockholm, Sweden. The results of the soil analyses are given in Table 1, toget...
A F Bravery
Soft rot decay in CCA treated eucalypts in Queensland - A comment
1986 - IRG/WP 1301
A survey has been completed concerned with the distribution and severity of groundline soft rot decay in the CCA treated sapwood of eucalypt poles in Queensland. The survey encountered some 1000 poles of which 55% were slightly, 28% moderately and 17% severely decayed. Soft rot decay was more severe in urban than rural locations. Embedment of poles in concrete resulted in severe soft rot. No signi...
L E Leightley
Protection of rubberwood timber. Part 1: Impregnation with boron preservatives
1989 - IRG/WP 3551
Rubberwood (Hevea brasiliensis) were treated with a 3% proprietary mixture of borax/boric acid using three different treatment schedules i.e. full-cell, full-cell to refusal and full-cell with 12 cycles of vacuum/pressure. Freshly cut samples had mean preservative retentions of 187 kg/m³, 214 kg/m³ and 178 kg/m³ respectively. Pre-air dried samples for one week had retentions of 252 kg/m³, 308 ...
L T Hong, C C K Liew