Long-term effectiveness of fumigants in controlling decay in Douglas fir waterfront timbers
1986 - IRG/WP 3364
The persistence, movement, and effectiveness of chloropicrin and Vapam (sodium N-methyl dithiocarbamate) in large, horizontal Douglas fir timbers were evaluated 7 years after fumigation. Chloropicrin prevented reestablishment of decay fungi; reinvasion occurred in some Vapam-treated timbers. Residual fungistatic effect was detected up to 1.2 m from the fumigation site in chloropicrintreated timber...
T L Highley
Performance of untreated French Guianan piling in marine exposure
1992 - IRG/WP 92-4173
Round piling of seven French Guianan species, greenheart, and preservativ-treated Southern Pine were installed as fender piling in Key West, FL. After 12½ years, none of the tropical hardwoods performed as well as dual-treated Southern Pine. Of the hardwoods, kouata patou and maho noir were the most resistant to decay and marine borers....
B R Johnson
Marine borers and marine wood protection - Some answers and some outstanding questions - A comment
1990 - IRG/WP 4163
A brief description of the nature of hazards encountered in different parts of the marine environment is given. An attempt is then made to assess what were the essential findings of selected areas of research in the marine wood protection field and what still needs to be done. That is, if we are to more adequately understand what we are attempting to do in this field of study!...
J E Barnacle
Natural durability of some common Indian timbers and marine plywood against biodeterioration in Kochi waters (India)
1992 - IRG/WP 92-4177
Panels of thirty-eight timber species and marine plywood were tested in Kochi harbour (South-west India) for periods ranging from 3 to 21 months, so as to evaluate their natural resistance against marine borers. Results indicate that all the timber species studied are non-durable, 6 of them having undergone more than 50% internal destruction within 3 months; 14 species in 6 months, 13 species and ...
L N Santhakumaran, M V Rao
Plastic-coated marine piling in Los Angeles Harbour
1984 - IRG/WP 4105
G Horeczko
Ultrastructure of degraded, CCA-treated Pinus radiata wood from a marine pile
1990 - IRG/WP 1461
During an inspection of marine piles, 12 years after installation, severe degradation was noted on one of them in the vicinity of a corroded eye-bolt. The wood was dark brown in colour and tended to crumble easily. Wood fragments were examined by light microscopy and scanning and transmission electron microscopy and were also analysed for carbohydrates and lignin. Light microscopy showed numerous ...
A P Singh, M E Hedley
Evaluation of some polyurethanes as protective marine coatings for wood
1985 - IRG/WP 4115
Several polyurethane formulations were evaluated in the marine environment as possible replacements for Irish felt used on U.S. Navy minesweepers as a marine borer barrier between the main wooden hull and an outer, wooden sheathing which covers it. Pine panels coated with the candidate materials were tightly juxtaposed with untreated pine baitwood to simulate the hull/sheathing configuration, the ...
J D Bultman, J E Pinto
The practice of using concrete on wood piling for marine use in Thailand
1982 - IRG/WP 492
The practice of using concrete on wooden poles has been carried on in Thailand for a long time in pile-houses and pier constructions which have been situated in, or partly in the sea. In such instances, the hewed round and/or square-sawn heartwood poles of naturally durable timber species have been coated with concrete of about 5 to 10 cm or more in thickness, and to about 100 cm above the highest...
B Anuwongse
Premature failure of treated timber in wharfs in Papua New Guinea, attributed to defects in design
1991 - IRG/WP 4158
The performance of timber in wharfs in Papua New Guinea has been monitored for a number of years. Premature failure of wharf structures was found in many cases to be due to defects in design rather than ineffective preservative treatment. Above-water timbers were found to be prone to severe checking followed by decay. Protection for the end grain of pile tops and the limiting of radial checking in...
S M Cragg
Ability of chloropicrin, Vorlex, or methylisothiocyante to prevent marine borer attack of Douglas fir piling
1989 - IRG/WP 4153
The preservative-treated shell around Douglas-fir piling is an excellent barrier to attack by marine borers; however, damage to this shell can permit marine borer attack. The feasibility of using fumigants to enhance piling performance was examined by exposing fumigant-treated Douglas-fir sections in marine waters off Newport, OR, or Port Hueneme, CA. The piling were inspected annually and increme...
M A Newbill, J J Morrell
Sediment toxicity study of marine piles treated with CCA-C
1995 - IRG/WP 95-50040-35
A study was undertaken to demonstrate the effects of 10-day exposure to sediments mixed with leachate from chromated copper arsenate Type-C (CCA-C) southern pine marine piles treated to a retention of 40 kg/m³ (2.5 pcf) and untreated southern pine piles on the benthic amphipod, Ampelisca abdita. The biological endpoint used to establish effects was organism survival. Leachate obtained during a 28...
W J Baldwin, E A Pasek, P D Osborne
Protection of pile tops using combinations of internal treatments and water shedding caps
1993 - IRG/WP 93-30020
Preservative treatment produces an excellent barrier against fungal, insect, and marine borer attack; however, fabricators often disrupt this barrier during construction, creating avenues for entry of decay agents. This problem is particularly acute in marinas along the coastal United States. Standards recommend the application of a water-shedding cap at the time of installation to prevent pile to...
P Schnieder, M A Newbill, J J Morrell
The use of fumigants for controlling decay of wood: a review of their efficacy and safety
1989 - IRG/WP 3525
Volatile agricultural chemicals (fumigants) such as chloropicrin (trichloronitromethane) and sodium n-methyldithiocarbamate have been used in the United States for controlling internal decay of large dimension wood products for over 20 years. This usage has been concentrated in the electric utility industry, but fumigants are increasingly applied to protect bridge timbers, marine piling, and even ...
J J Morrell