Your search resulted in 66 documents. Displaying 25 entries per page.
Preliminary Observations of the Photostabilization of Wood Surfaces with Cerium Oxide Nanoparticles
2010 - IRG/WP 10-40504
Reactive transition metal compounds, wood modification and grafting of UV absorbers have all been used to photostabilize wood. Some of these approaches are promising, but the toxicity of certain reactive transition metal compounds and the cost of wood modification and grafting have restricted their commercial applications. Hence, more cost-effective and environmentally friendly methods of protecti...
Chunling Liu, A Ahniyaz, P Evans
NewSiest-Enhancement of UV stability of thermally modified wood through envelope impregnation with nanobased stabilisers
2020 - IRG/WP 20-40909
Thermal modification is a process which improves the properties of wood, resulting in a material that can be disposed at the end of the product life cycle without presenting an environmental hazard. Thermally modified wood retains as a natural product and the grain, original colour variances and characteristics of wood are still present. However, exposure to daylight causes brightening or greying ...
K Srinivasa, M Petrič
The potential for using CuO nanoparticles as a wood preservative
2011 - IRG/WP 11-30569
The potential for using nano-copper particles for wood protection was investigated using mini-agar slant and wood block tests with Gloeophyllum trabeum or Trametes versicolor. Nano-copper was more effective against G. trabeum than T. versicolor, although neither of these fungi would be considered copper tolerant. Nano-copper solutions were stable over a 17 week storage period, but precipitated w...
I S Weitz, K Knani, M Maoz, C Freitag, J J Morrell
Optimized composition of alkyd emulsion with nanoparticles of iron oxide for enhancing protection of thermally modified wood
2022 - IRG/WP 22-40940
Thermal treatment is acknowledged as an environmentally friendly method to improve durability of wood and some of its properties, such as biological resistance, dimensional stability, reduced hygroscopy. Despite these improvements, when used outdoors, also thermally treated wood is subjected to the action of environmental factors, like solar radiation, moisture, precipitations, temperature, etc., ...
E Sansonetti, D Cīrule, I Andersone, B Andersons, E Kuka
Modélisation sur maquette du rejet accidentel d'un gaz toxique et inflammable dans l'atmosphere - Emission de type "bouffée d'oxyde d'éthyléne [Water model simulation of toxic and flammable gases in the environment on industrial sites - Puff of ethylen oxide]
1990 - IRG/WP 3576
Cytochemical localization of hydrogen peroxide in brown rot fungus Tyromyces palustris by cerium chloride technique
1999 - IRG/WP 99-10299
Cerium chloride (CeCl3) was used to localize H2O2 cytochemically for studying relationship between ultrastructural and functional characteristics of cellulose degradation by brown rot fungi. This technique proved very useful in localizing discrete electron-densereactionproducts at high resolution with minimal nonspecific deposition. The cytochemical localization of extracellular H2O2 by CeCl3 usin...
Yoon Soo Kim, Seung-Gon Wi
Movement of boron from fused boron rods implanted in Southern pine, Douglas fir, red oak, and white oak timbers
1995 - IRG/WP 95-30061
This paper reports the distribution of boron from fused boron rods installed into six-inch (15.2 cm) square timbers of Douglas-fir, Southern Pine, red oak and white oak exposed aboveground. The composition and size of rods was: sodium borate and sodium borate-copper oxide (8.5 x 100 mm²); sodium borate-copper, sodium borate and boric oxide-copper oxide (12 x 76 mm²). The boric acid equivalent wa...
T L Highley, L Ferge
Decay patterns observed in butylene oxide modified ponderosa pine attacked by Fomitopsis pinicola
1983 - IRG/WP 1183
Small blocks of ponderosa pine chemically modified by butylene oxide to three different weight percent gains (WPG) were decayed for 2 months with the brown rot fungus Fomitopsis pinicola. Wood substance loss and the type of decay pattern recognised were fairly similar both for control and blocks treated to 8 and 15 WPG. No difference in attack was observed between radial or tangential walls in lat...
T Nilsson, R M Rowell
Effect of fatty acid removal on treatability of Douglas-fir
1993 - IRG/WP 93-40008
Treatment of Douglas-fir with chromated-copper-arsenate (CCA) poses a major challenge. Several hypotheses based on the anatomical aspects as well as chemical reactivity of the preservative formulations with cell wall constituents and deposits have been proposed. Techniques to prevent pit aspiration or slow fixation reactions have, however, not significantly improved treatment. The presence of high...
S Kumar, J J Morrell
Detoxification of preservatives: Tri-n-butyltin oxide as a biocide
1982 - IRG/WP 1156
T E Dudley-Brendell, D J Dickinson
Rapid leaching test
1991 - IRG/WP 2367
An accelerated test which is suitable for measuring the extent of metal fixation in both chromium and non chromium containing preservatives is described....
J A Cornfield, M Bacon, A Lyman, C Waldie, M R Gayles
Testing wood in ground contact: An artificial soil
1977 - IRG/WP 280
This document is an interim report on the development of the artificial soil medium. It includes some information on the relationship between soil, wood and water which is of relevance in testing....
E F Baines, D J Dickinson, J F Levy
Effect of sterilization method on germination of spores of wood decay fungi observed by contact agar block method
1978 - IRG/WP 2117
Previous studies of germination of spores of wood decay fungi on wood have generally concluded that method of wood sterilization has little significant effect on germination response. This study expands the numbers of test fungi as well as number of sterilization methods employed to determine the influence of sterilization method on spore germination response of decay fungi. Germination was assess...
E L Schmidt, D W French
The formation of organotin carboxylates in bis(tributyltin) oxide - treated Pinus sylvestris sapwood
1990 - IRG/WP 3618
Tributyltin compounds have been successfully used for many years as wood preservatives, although their chemical nature in timber have not been fully elucidated. This study by 119Sn and 13C NMR spectroscopy has shown that, on impregnation into Pinus sylvestris sapwood, bis(tributyltin) oxide, (Bu3Sn)2O, is rapidly converted to tributyltin carboxylates, Bu3SnOCO·R, via reaction with components of t...
S J Blunden, R Hill
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell
Leaching of CCA components from treated wood under acidic conditions
1993 - IRG/WP 93-50004
The leaching of CCA components from treated wood under acidic conditions were investigated. Western hemlock treated with three types of CCA and two levels of target retention was subjected to leaching at four different levels of pH. After leaching tests, leached samples were subjected to laboratory decay and soft rot tests. The amount of CCA components leached was dependent on acidity of leaching ...
Jae-Jin Kim, Gyu-Hyeok Kim
Comparisons of differences in electrical conductivity and corrosivity between CCA-oxide and CCA-salt treated wood
1981 - IRG/WP 3178
CCA preservatives have served well in many applications throughout the world. In developed areas it is the preservative in demand for clean dry paintable surfaces with long durability. In developing areas it is widely used for economic and logistical reasons. With the current emphasis on energy resources, the CCA preservatives are gaining greater acceptance as a substitute for hydrocarbon-related ...
J A Taylor
Fixation of CCA in Pinus sylvestris after kiln-drying
1990 - IRG/WP 3594
Tanalith C Paste is 98% fixed and Tanalith Oxide C is 99% fixed irrespective of whether treated Pinus sylvestris is kiln or air dried. A schedule suitable for kiln drying of CCA treated Pinus sylvestris is described....
P Warburton, J A Cornfield, D A Lewis, D G Anderson
The chemical nature of bis(tributyltin) oxide in Pinus sylvestris sapwood
1989 - IRG/WP 3508
Tributyltin compounds have been used for many years as wood preservatives. This study has provided, for the first time, an explanation for the previously reported dealkylation and/or volatilisation of the tributyltin species in, and from, Scots pine (Pinus sylvestris) sapwood. Thus, 119 Sn nuclear magnetic resonance studies have shown that, on impregnation into this timber, bis(tributyltin) oxide ...
S J Blunden, R Hill
Leaching of Arsenic from Mulch Made from Recycled Construction and Demolition Wood
2005 - IRG/WP 05-50232
Mulch made from recycled construction and demolition (C&D) wood has been reported to contain chromated copper arsenate (CCA)-treated wood and potentially release arsenic in the leachate by rainfall. Such recycled wood mulch is commonly masked with iron-oxide colorant, which is known to combine with arsenic. The objective of this study was to evaluate the levels of arsenic leaching from C&...
T Shibata, H M Solo-Gabriele, T G Townsend, B Dubey
Low polymer levels containing bioactive monomer polymerized in situ provide resistance to Gloeophyllum trabeum
1995 - IRG/WP 95-30066
Wood preservation based on in situ polymerization of potentially bioactive monomers has been studied. Tributyltin oxide acrylate (TBTOA) and pentachlorophenol acrylate (PCPA) were synthesized. Wood samples were treated at 2, 5, 10, 15 and 20% by weight solutions with varying amounts of crosslinker (trimethylolpropane trimethacrylate, TMPTM) and polymerized in situ in wood samples (2.54 x 2.54 x 0....
R E Ibach, R M Rowell
Influence of CCA and TnBTO on wood decay, under different oxygen levels and various initial moisture content
2001 - IRG/WP 01-10415
Fagus sylvatica (beech) and Pinus sylvestris (Scots pine) were impregnated by TnBTO (tributyl-tin oxide) and CCA (chromated copper arsenate). In wood blocks two levels of moisture content (50% and 100% of saturation point) were used. Three levels of oxygen concentrations (10, 21, and 50%) were chosen. Treated and untreated wood were exposed to three fungi (C. versicolor a white rot, C. puteana, a ...
S M Kazemi, R J Murphy, D J Dickinson
The effect of preservative distribution in small blocks of Pinus sylvestris on the toxicity of tributyltin oxide to Reticulitermes santonensis Feytaud
1971 - IRG/WP 206
Small blocks of Pinus sylvestris (50x25x15 mm³) were treated by a full-cell method with various concentrations of tributyltin oxide in benzene. Replicate blocks were then freeze dried, rapidly air dried or slowly air dried and exposed to surface attack by the subterranean moistwood termite Reticulitermes santonensis Feytaud. At all concentrations it was found that the freeze-dried blocks were mor...
M P Levi, D N R Smith
Pentachlorophenol and tributyltin oxide - the performance of treated Pinus radiata after 12 years' exposure
1986 - IRG/WP 3361
Pinus radiata samples were impregnated with a range of light organic solvent preservatives and copper/chrome/arsenic salt and exposed with no surface coating both in and above ground for 12 years. Inspection of the test samples revealed that some formulations of light organic solvent preservatives will give good fungal protection and reduce splitting in Pinus radiata exposed externally without a s...
R S Johnstone
Experiments on the degradation of tributyltin oxide: A progress report
1984 - IRG/WP 3287
A variety of experiments designed to assess the chemical and physical factors affecting the degradation of tributyltin oxide in treated timber are described. Simple procedures in which temperature and oxygen availability were increased in the presence of wood and water suggest that the wood itself was of prime importance. Attempts to decrease degradation with antioxidants were unsuccessful but led...
R J Orsler, G E Holland