Failure characteristics of thermally modified poplar wood subjected to mechanical tests
2023 - IRG/WP 23-40983
Poplar (Populus spp.) are among the fastest growing timber species and have been widely planted for use in plywood, composites, pallets, furniture components and paper production. However, the low density of the wood limits many structural applications and the wood has little resistance to biodegradation. Thermal modification represents one approach to improving durability by changing the moistur...
E Bari, M Ghorbanian Far, N Moradi, J J Morrell, G Daniel, B Mohebby, R Hosseinpourpia, M Humar


Microbiological degradation of wooden piles in building foundations
1988 - IRG/WP 1370
White rot, soft rot and bacterial attack have been detected in softwood piles under buildings. In some cases bacteria were found to be the main degradation organisms in the studied piles. The water content of degraded piles was very high. The compression strength was quite low also in the piles deteriorated by bacteria. The density of wood was very variable, and the degree of degradation could not...
L Paajanen, H Viitanen


Changes in the degree of decay of lignocellulosic substrate used in a screening test of fungicidal wood preservatives
1977 - IRG/WP 287
This report contains results of investigations aimed at: a) determination of the effect of the kind of substrate and species of test fungus on quantitative changes in used samples prepared from spruce cardboard, and b) comparison of the threshold fungicidal values of come fungicides determined with accelerated method, with values obtained by block method. During performed investigations, the metho...
K Lutomski


Low polymer levels containing bioactive monomer polymerized in situ provide resistance to Gloeophyllum trabeum
1995 - IRG/WP 95-30066
Wood preservation based on in situ polymerization of potentially bioactive monomers has been studied. Tributyltin oxide acrylate (TBTOA) and pentachlorophenol acrylate (PCPA) were synthesized. Wood samples were treated at 2, 5, 10, 15 and 20% by weight solutions with varying amounts of crosslinker (trimethylolpropane trimethacrylate, TMPTM) and polymerized in situ in wood samples (2.54 x 2.54 x 0....
R E Ibach, R M Rowell


Termite and fungal resistance of in situ polymerized tributyltin acrylate and acetylated Indonesian and USA wood
2000 - IRG/WP 00-30219
Wood [Indonesian pine (IP), Indonesian Jabon (IJ) and USA southern yellow pine (USP)] was either in situ polymerized with tributyltin acrylate (TBTA) or acetylated and then exposed to termite and fungal degradation both in laboratory tests and field exposure. The TBTA woods had an average weight percent gain (WPG) of 11% for IP, 12% for IJ, and 10% for USP. The acetylated woods had a WPG of 15-27%...
R E Ibach, Y S Hadi, D Nandika, S Yusuf, Y Indrayani


Chitosan for wood protection - state of the art
2005 - IRG/WP 05-30378
The aim of this paper was to give a state of the art description of chitosan as a wood protecting agent. Chitosan is a metal free natural compound derived from crustacean shells and is under evaluation as an environmentally benign wood protecting agent. Information from journals states that chitosan may act both fungistatically and at higher concentrations, as fungitoxic, but the mode of action is...
M Eikenes, G Alfredsen, E Larnøy, H Militz, B Kreber, C Chittenden


Residual resistance in eucalypt poles according to the degree of sanity
1984 - IRG/WP 2225
A lot of 50 eucalypt poles presenting external deterioration by fungus was taken from service and tested. These poles were classified into five degrees of sanity according to evaluation criteria adopted by the IPT Wood Division. After being classified, they were tested with respect to their bending resistance, in order to gather information about their critical degree of sanity which may define th...
F C Geraldo, S Milano, S G De Sequeira


Estimation of the impregnation degree of pine wood by the distribution analysis of active ions concentration in the cross-section
1999 - IRG/WP 99-20174
Samples in the form of pine wood rollers of diversified moisture content of ca. 50, 28 and 12% were impregnated with a water solution of the mixture type CCB with the use of the full-cell process. Moisture content was determined in individual layers from the girth to the pith. In the same way the concentrations of copper and chromium ions with the use of the spectrophotometric method and recalcula...
K Lutomski, B Mazela


Relationship between the bending strength and the degree of termite attacks on western hemlock by Coptotermes formosanus Shiraki
1990 - IRG/WP 1434
For the examination of the relationship between the bending strength and the degree of termite attacks, Western Hemlock (Tsuga heterophylla Sarg.) was used. Sixty specimens (4.5 x 4.5 x 82 cm³) were attacked by termites at the culture room of Coptotermes formosanus Shiraki. The termites were introduced on the central parts (10 cm) of specimens. In the case of the 2 points loading, the bending mom...
K Suzuki, T Tanaka


A new process for in situ polymerization of vinyl monomers in wood to delay boron leaching
1998 - IRG/WP 98-40110
Efforts were accelerated on effective use of boron compounds in wood preservation owing to their environmentally safe characteristics and relatively low costs in addition to their well-known high bioactivity and fire resistant properties. Although having these unique favorable properties, they are readily leachable from treated wood at humid conditions. Therefore, they had limited market for exter...
M K Yalinkilic, W Dwianto, Y Imamura, M Takahashi


Characterization of wood modification prepared by in situ polymerization with pre-polymer and the mechanism of modification
2013 - IRG/WP 13-40633
Chemical modification of wood is a potential way to obtain high quality wood. In this study, the fast-growing poplar was impregnated with modifier using a pulse-dipping machine by in situ polymerization. Fungal decay analysis, mechanical properties and dimension stability of the natural and modified woods were investigated. The wood samples were also characterized by X-ray diffraction (XRD) Therma...
Qian Lang, Zeng Bi, Junwen Pu


Study of in-situ gel polymerization established by Si-O-Si framework within wood micropores
2014 - IRG/WP 14-40672
Sodium silicate was used to form Si–O–Si framework by gel process and optimize the effect of the methylolurea impregnation on poplar wood. The modifier cured within the wood micropores by in-situ gel polymerization during the kiln drying. The results showed that treated wood acquired higher mechanical strength, but lower hygroscopicity. New positions of the XRD peaks appeared which caused by s...
Zeng Bi, Qian Lang, Heyu Chen, Junwen Pu


The impact of catalyst on the properties of furfurylated beech wood
2016 - IRG/WP 16-40748
European beech (Fagus sylvatica L.) is a major tree species of European forest that is underexploited because of its low dimensional stability and durability. Similarly to what has been developed with radiata pine, furfurylation might be the answer to optimize the utilization of local beech wood. Beech wood furfurylation process was studied using five different catalysts: maleic anhydride, maleic ...
P S Sejati, A Imbert, C Gérardin, S Dumarçay, E Fredon, E Masson, D Nandika, T Priadi, P Gérardin


Effect of insitu polymerization on practical properties of heat treated wood
2016 - IRG/WP 16-40763
This research was conducted to investigate the effect of combined modification; heat treatment and impregnation with styrene monomer on physical and mechanical properties of poplar wood (Populus deltoides). Test samples were grouped in six levels of control, wood polymer made from styrene, heat treatment at 170 ºC and 200ºC and combined modification; first hat treated at 170 ºC and 200ºC and t...
M Ghorbani, M Mohseni Shaktaei


Black-stain Resistant Acrylic Latexes for Wood Coatings Applications
2017 - IRG/WP 17-40786
Translucent coatings on wood in exterior applications often fail due to photodegradation and colonization by black-stain fungi and require frequent refinishing. This limits competitiveness with alternative materials. In this project, it was hypothesized that an effective dispersion of inorganic nanoparticles will provide a translucent coating with long-term resistance to black-stain fungi. Functio...
G Boivin, A M Ritcey, P I Morris, V Landry


Evaluation of chemical densification of three hardwood species through in-situ electron beam polymerization
2020 - IRG/WP 20-40893
Hardwoods are the most suitable species for wood flooring for their appearance as well as their hardness. Yet, improving hardness can provide substantial benefit for the wood flooring market. Chemical densification of wood and in-situ polymerization through electron beam technology was chosen to increase hardness of three hardwoods (Yellow birch (YB) (Betula alleghaniensis Britt.), Sugar maple (SM...
J Triquet, P Blanchet, V Landry


Surface chemical wood densification through in situ electron beam polymerization: description and dose study
2022 - IRG/WP 22-40933
Traditional wood chemical densification processes can be used to improve wood mechanical properties by increasing density of the material throughout its thickness. While mechanical surface densification has heavily been investigated, surface treatments involving impregnation of monomers remain unexplored. This study describes a new material, surface densified through lateral impregnation of acryla...
J Triquet, P Blanchet, V Landry