Ancillary properties of vapor boron-treated composites
2001 - IRG/WP 01-40210
This paper discusses the water absorption, thickness swelling, and internal bond strength of North American composites treated using a vapor boron treatment process. For oriented strandboard, high boron loadings led to lower internal bond strength and lower thickness swelling. Water absorption results were variable but no deleterious effect of treatment was noted. For medium density fiberboard, th...
W A Jones, H M Barnes, R J Murphy
Leachability of borate-modified oriented strandboard: A comparison of zinc and calcium borate
2002 - IRG/WP 02-40232
The leachability of boron in zinc and calcium borate-modified oriented strandboard (OSB) was investigated in this study. The leaching experiments were conducted by exposing edge-sealed OSB samples under running water for 8, 24, 72, and 216 hours. The results were compared with those from the unleached controls. Boron leaching of the modified OSB occurred upon the initial water exposure, and the le...
S Lee, Q Wu
A Preliminary Report on the Properties of Engineered Wood Composite Panels Treated with Copper Naphthenate
2005 - IRG/WP 05-40294
This paper reports on our preliminary investigation of the properties of randomly oriented strandboard which had waterborne or powdered copper naphthenate (CuN) incorporated into the board during manufacture. When compared to zinc borate-treated controls (ZnB), the mechanical properties of strandboard (MOR, MOE, work-to-maximum load, internal bond strength) were not adversely affected by treatmen...
J W Kirkpatrick, H M Barnes
Mold susceptibility of oriented strandboard made with extracted flakes
2008 - IRG/WP 08-40402
As part of a larger study on the manufacture of oriented strandboard (OSB) using hot-water-extracted flakes, the mold susceptibility of extracted-flake and un-extracted-flake OSB was assessed using the standard ‘mold box’ test. OSB made with extracted flakes was much less susceptible to mold. This suggests that the extraction of hemicelluloses and other carbohydrates from wood for the producti...
A M Taylor, O Hosseinaei, Siqun Wang
Decay and mold resistance of borate modified oriented strandboard
2003 - IRG/WP 03-40260
Decay and mold resistance of zinc borate (ZB) and calcium borate (CB) modified
oriented strandboard (OSB) from southern mixed hardwoods and yellow pine was investigated in this study. Tests were done with brown rot, Gloeophyllum trabeum, and white-rot, Trametes versicolar, fungi for 8 and 12 weeks, respectively. Wood species and fungus type had significant influence on the decay resistance. Decay...
Q Wu, S Lee, J P Jones
Effect of point of preservative addition on the mechanical and physical properties of strandboard treated with Tanalith 3485
2000 - IRG/WP 00-40152
Preservative has been added to a PF bonded strandboard at various different stages in the manufacturing cycle and the physical and mechanical properties of the boards have been evaluated (modulus of elasticity, modulus of rupture, thickness swelling, water absorption, internal bond strength, and shear strength). Preservative addition has been examined at five different stages namely green strand d...
G J Goroyias, M D C Hale
Performance of Oriented Strandboard, Medium Density Fiberboard, Plywood, and Particleboard Treated with Tebuconazole in Supercritical Carbon Dioxide
2005 - IRG/WP 05-30364
The performance of oriented strandboard (OSB), medium density fiberboard (MDF), particleboard and plywood treated with tebuconazole using supercritical carbon dioxide was investigated over a 48 month exposure under harsh above ground conditions in Hilo, Hawaii. Samples treated to low retentions (<0.20 kg/m3) tended to experience decay at rates that were only slightly lower than those found wit...
J J Morrell, M N Acda, A R Zahora
Tool wear for vapor boron-treated composites
2001 - IRG/WP 01-40209
A series of composites, including oriented strandboard and medium density fiberboard, were treated via vapor boron technology. Treated samples were compared to untreated composites using a tool force measuring technique. Tool forces measured with a dynamometer indicated a positive effect of boron addition. Visual and SEM examination indicated a wider wear zone on the rake face of the tool for the ...
W A Jones, H M Barnes, H A Stewart, R J Murphy
Effect of fungal attack on maximum load capacity of simulated wall assemblies
2007 - IRG/WP 07-20363
The effects of moisture intrusion and fungal attack on the maximum load capacity of nailed assemblies was investigated using one white and one brown rot fungus against 4 material combinations over a 20 week period. Wetting significantly reduced the maximum load capacity of all four material combinations, while wetting and autoclaving only affected the OSB sheathing/spruce stud. The white rot fung...
N Melencion, J J Morrell
The effects of zinc borate treatment of wood strands on some technological properties of oriented strandboard (OSB)
2008 - IRG/WP 08-40419
In this study, influences of zinc borate treatment on some technological properties of oriented strandboard (OSB), from aspen wood (Populus euroamericana cv.) were evaluated. Therefore, a total of nine panels with dimensions of 40 cm by 40 cm by 1.8 cm and with an average target density of 0.65 g/cm3 were manufactured under the laboratory conditions. Experimental panels were manufactured at two di...
A D Çavdar, H Kalaycioglu, G Nemli