An investigation of the factors influencing the rate of deterioration of timber samples due to microfungi in laboratory tests
1997 - IRG/WP 97-20116
An investigation was performed into the comparative performances of test 1 (vermiculite burial) and test 2 (soil burial) as described in ENV 807. Two test preservatives were used - copper naphthenate and propiconazole. Copper chromate was included as a reference preservative. The wood species used was beech (Fagus sylvatica). Test 1 was performed using both a mixed inoculation of the five stipulat...
I J Herring, D J Dickinson, S M Gray, J K Carey
Resistance of acetylated wood to biological degradation. Evaluation of field test
1997 - IRG/WP 97-30139
Acetylated wood samples were tested in ground contact (stake test) at two test fields, one in Simlångsdalen, Sweden, and one in Viikki, Finland, according to European standard EN 252. The test samples were inspected annually and their condition was compared with that of untreated controls and of samples treated with two reference CCA preservatives. The use of untreated controls and preservative t...
P Larsson Brelid, R Simonson, Ö Bergman
Stake test with ammoniacal copper in combination with different agents started in 1962
1997 - IRG/WP 97-30130
In 1962 a stake test was started with ammoniacal copper in combination with chromium, arsenic, pentachlorophenol, boron, salicylic acid, benzoic acid, sorbic acid, pyridine and tannin. Different concentrations of the copper component were used as well as the added agents. For each concentration and test site, ten stakes of Pinus sylvestris L. sapwood were treated. The stakes were set out at two te...
B Häger, Ö Bergman
A new concept for the evaluation of wood durability for out of ground contact using accelerated L-joint testing
1997 - IRG/WP 97-20123
Since the wood preservation sector is developing in favour of defining exactly the utilization of wood products and preservation techniques as a function of the envisaged hazard class, more in particular the hazard classes 3 and 4 (EN 350) there is obviously a need for a test method evaluating natural durability for out of ground contact applications. Based on the L-joint test as described in the ...
J Van Acker, M Stevens
Accelerated testing for out of ground contact using natural biological preconditioning: Part 2
1997 - IRG/WP 97-20108
Small blocks of scots pine sapwood were treated, buried in vermiculite and exposed to natural microbial colonisation during outdoor exposure prior to laboratory decay testing. An EN 84-type leach trial was carried out on unexposed samples. Periodic microbial isolations, moisture content, permeability and weight loss tests were also conducted. The experiment ran for 12 months. The colonisation of t...
S Molnar, D J Dickinson, R J Murphy
Improvements of monitoring the effects of soil organisms on wood in fungal cellar tests
1996 - IRG/WP 96-20093
Accelerated testing the durability of preservative treated timber in a so called "fungal cellar" or "soil-bed" to evaluate its performance in ground contact is widespread practice. In order to obtain a more accurate and reproducible estimate of preservative performance, several institutes, among them the BAM in Berlin, have routinely carried out static bending tests in addition to visual examinati...
I Stephan, S Göller, D Rudolph
In-ground performance of two formulations of chlorothalonil after five years of exposure at three test sites in Australia
1996 - IRG/WP 96-30101
Sapwood specimens of Pinus radiata D. Don and Eucalyptus regnans F. Muell. were each treated to three retentions of each of two preservative formulations (chlorothalonil in oil; chlorothalonil plus chlorpyrifos in oil) and installed in-ground at three field test sites in Australia. Specimens were treated with each formulation to achieve 3.2, 6.4 and 12.8 kg/m³ of chlorothalonil a.i. and 3.2 + 0.2...
J W Creffield, T L Woods, N Chew
Climate indices at work: Above ground decay L-joint tests (EN 330 and AWPA E9) at two sites 12000 km apart and with Scheffer climate indices of 60-65 and 300-330
1996 - IRG/WP 96-20095
Matched sets of Scots pine sapwood (Pinus sylvestris) L-joints were exposed above ground at two field sites for approximately five years. One site, at Garston, Watford, UK has a climate index between 60 and 65 while the other, close to Hilo, HI, USA has an index between 300 and 330. The joints were treated with a range of organic solvent treatments applied either by three minute dip immersion or b...
A F Preston, K J Archer, D M Roberts, J K Carey, A F Bravery
Occurrence of manganese deposits in test stakes exposed in groung contact situations
1996 - IRG/WP 96-10182
Dark spots and flecks were frequently recognized on the surface and within non-preservative treated hard- and softwood test stakes placed in soil contact. Energy dispersive X-ray microanalysis in conjunction with electron microscopy showed the flecks to be composed primarily of manganese dioxide. Detailed transmission electron microscopy observations indicated intrusion of manganese into the wood ...
G F Daniel, T Nilsson, J Volc
In-ground evaluation of a copper azole wood preservative (Tanalithâ E) at a tropical Australian test site
1996 - IRG/WP 96-30100
A field trial to determine the in-ground termite and decay resistance of Pinus radiata D. Don impregnated with a copper azole formulation, TANALITHâ E, has been established at a tropical site in the Northern Territory of Australia. Four retentions of TANALITHâ E, containing 1.54, 2.08, 2.92 and 4.30 kg/m³ of Cu, are being evaluated. For comparison, Pinus radiata specimens treated to two retenti...
J W Creffield, J A Drysdale, N Chew
A comparison between different accelerated test methods for the determination of the natural durability of wood
1996 - IRG/WP 96-20099
According to the European standard EN 350-1 the natural durability of wood is defined as: "the inherent resistance of wood to attack by wood destroying organisms". This standard also describes how, for certain hazard classes, the durability is determined. The two methods described in this standard are the kolleflask method (EN 113) and the field-stake-test method (EN 252). The EN 113 test gives re...
H Militz, S G L Michon, J E Polman, M Stevens
Is laboratory testing of decay resistance questionable as a single criterion for natural durability?
1996 - IRG/WP 96-20096
In a laboratory test set up over 20 hardwood species were evaluated according to the European Standard EN 350-1 including Basidiomycete and soft rot testing. Half of the species used were of a known natural durability. The Basidiomycete testing was carried out using Coriolus versicolor, Gloeophyllum trabeum and Coniophora puteana in a malt agar test similar to EN 113. From this test it was not pos...
J Van Acker, M Stevens, T Van Cauwenberghe, T Seynaeve
Use of compression strength loss for measuring decay in the soil block test
1996 - IRG/WP 96-20083
The possibility of using radial direction compression strength of wood, rather than mass loss, was evaluated for both a brown-rot fungus (Gloeophyllum trabeum) and white-rot fungus (Trametes versicolor). With untreated pine wafers (5 x 19 x 19 mm³ - l x r x t) exposed to Gloeophyllum trabeum in a soil block test for five days, the compression strength loss was nearly 50% compared to a 5% mass los...
D D Nicholas, Zhongwei Jin
Performance of copper-chrome formulations in ground contact in five test sites in New Zealand
1996 - IRG/WP 96-30113
Copper-chrome-arsenate (CCA), copper-chrome-boron (CCB), copper-chrome-fluoride (CCF) and copper-chrome-phosphate (CCP) have been tested at four retentions each in ground contact (25 x 50 x 500 mm³ radiata pine sapwood stakes) for 16 years in five test sites in New Zealand. Results to date show that test site characteristics have a marked effect on relative performance. In a warm and wet site (an...
M E Hedley, R N Wakeling, J Foster, B E Patterson
An aquaria test of the natural resistance against marine borers of some commercial timbers available in Australia
1996 - IRG/WP 96-10145
The natural resistance of the heartwood of 22 different timbers grown or commercially available in Australia was examined. Radiata pine sapwood both untreated, and treated with 5.4 kg/m³ CCA salt, was included for comparison. Small timber blocks were exposed for one year in tanks containing either Limnoria tripunctata or Lyrodus pedicellatus. Four softwood species tested were heavily attacked and...
L J Cookson
Leaching of copper-chrome-arsenic treated timber: Simulated rainfall testing
1996 - IRG/WP 96-50074
Six kiln dried radiata pine sapwood packs of timber were preservative treated with copper-chrome-arsenic preservative using a modified Bethell treatment schedule. The packs were then subjected to simulated rain leaching at specified periods after treatment. Higher chromium leachate was obtained when higher volumes of simulated rainfall were applied. Lower chromium leachate was obtained for timber ...
S Walley, P R S Cobham, P Vinden
Field test of wood preservatives with Nasutitermes rippertii RAMBUR in Cuba
1996 - IRG/WP 96-10181
A field test of wood preservatives was carried out with Nasutitermes rippertii RAMBUR in the vicinity of the Material Testing Centre „Alexander von Humboldt" in Santiago de las Vegas/ Havana (Cuba) for 12 and 24 months. Test specimens of Pinus sylvestris L., Picea abies (L.) Karst. and Fagus sylvatica L. with dimensions of 25 x 25 x 490 mm³ were arranged vertically or horizontally in a circle o...
W Unger
What information can we glean from field testing
1995 - IRG/WP 95-20057
To mathematically compare the performance of preservatives in a field test, equations were formulated to describe the relation between log score and time and between rate of decay and retention. By combining these equations, a model was derived for the performance of a number of waterborne preservatives. Some relations between the estimated parameters for different preservatives were noted and the...
P I Morris, S Rae
A note on testing the efficacy of wood preservatives above ground
1995 - IRG/WP 95-20078
A number of test methods have been used to evaluate the performance of wood preservatives in above ground situations. These have included EN 113 tests following natural exposure weathering (NEWT), L-joint or T-joint tests, lap-joint tests, and decking tests. A new test referred to as the A-frame test has been developed and is under evaluation. This is based on a sandwich-type test in which a thin ...
G R Williams, J A Drysdale, R F Fox
Leaching results of shower test on L-joints with boric acid, bifluoride and TBTO rods
1995 - IRG/WP 95-50051
As part of the EC-project "Improvement of a local preservation process for wood products with reduced environmental impact", TNO has performed a leaching test on L-joints treated with pills with boric acid (Defence corner), bifluorides (Woodpil 55) and TBTO (Woodcap). The L-joints were exposed in an adapted shower test during 10 days, using 70 liters of water per day. The experiment is designed to...
P Esser, M J Boonstra, W L D Suitela, A J Pendlebury
Above-ground field tests undertaken in New Zealand
1995 - IRG/WP 95-20063
In addition to "standard" L-joints, above-ground test material exposed at the NZ FRI test site includes treated and untreated decking units, Y-joints, fence battens and weatherboards either with or without additional protection from surface coatings. The latter tests bridge the gap between "model" test assemblies, such as L-joints, and services tests. Most tests are of preservative-treated radiata...
M E Hedley, D R Page, J B Foster, B E Patterson
Field tests of preservative-treated radiata pine in Japan
1995 - IRG/WP 95-30083
Test stakes of radiata pine treated with various alkyl ammonium compound (AAC) formulations and with copper-chrome-arsenate (CCA) as reference preservative were installed in 3 test sites in Japan in 1981-82. When inspected in 1995, CCA-treated stakes showed less decay at all three sites than stakes treated with other formulations. Ammoniacal copper quaternary (ACQ)- treatment was only slightly les...
M E Hedley, K Tsunoda, K Suzuki
Acetylated solid wood. Laboratory durability test (part 2) and field trials
1995 - IRG/WP 95-40048
Degradation of acetylated beech, pine and poplar by soft rot fungi was related to strength loss in a laboratory test. No strength loss was noticed for poplar acetylated to a weight percent gain (WPG) of more than 11.2% and beech with a WPG of 12.8%. Several field trials were set up to determine the durability of acetylated products in practice. They included a field test to determine the durabilit...
E P J Beckers, H Militz, M Stevens
Distribution of copper/chrome/boron preservative in light red meranti (Shorea leprosula) before and after exposure test for 72 months
1995 - IRG/WP 95-20073
Copper/chrome/boron (CCB) preservative at 6% w/w was impregnated into light red meranti (Shorea leprosula) by full cell process. The quantitative analysis for copper, chrome and boron contents in treated wood samples was carried out by Inductive Couple Plasma (ICP). Electron Probe Microanalyser (EPMA) was used to monitor the distribution of copper, chrome and boron in the various treated wood tiss...
S Salamah, S Ani
Alternatives to preliminary oven-drying prior to spot-testing treated timber for borate or TBTN preservative penetration
1995 - IRG/WP 95-20067
Commonly-used penetration test procedures for timber treated with borate or organotin wood preservatives demand preliminary oven-drying before application of the spot-testing reagent(s), in order to achieve reliable results. The delay of 12 hours or more during oven drying is often a nuisance. Modifications to the spot-testing procedures, involving alternative solvents and acidification conditions...
M J Kennedy, A Zosars, J Norton