Application of radio frequency heating to accelerate fixation of CCA in treated round-wood
1999 - IRG/WP 99-40133
The potential of radio frequency heating to accelerate the fixation of chromated copper arsenate (CCA) in treated round-wood was assessed. Pre-dried Douglas-fir and western red cedar round-wood sections were pressure treated with CCA in a pilot plant retort, after which they were placed individually in a pilot radio frequency (RF) chamber. Based upon the color reaction of chromotropic acid with he...
Fang Fang, J N R Ruddick


Problems of fixation of CCA-preservatives in palm-wood
1985 - IRG/WP 3338
Palm-wood may be used for posts and poles where it needs proper treatment for long time use. Based on observations by W. Killmann on low CCA-fixation in palm-wood, samples of Jubaea-palm grown in a Greenhouse at Hamburg, have been treated in two different series with a 4% solution of CCA-type B. After 1-16 weeks of storage the blocks were split into sticks of 1-2 mm² and leached. In all series 50...
H Willeitner, K Brandt


Radical changes in the requirements for more safe pressure impregnation in the Nordic countries in 1988
1990 - IRG/WP 3581
After introduction of quality control schemes and standards in the Nordic countries during the seventies, the first radical change of the standards and practice of work took place after pressure from the labor unions and authorities in 1988 and 1989 in Denmark and in Sweden. A new class of preservation with less retention for out of ground contact use was introduced, fixation times were prolonged ...
B Moldrup


Accelerated fixation of CCA in borak bamboo (Bambusa balcooa Roxb.) of Bangladesh
2001 - IRG/WP 01-40193
CCA-C fixation study on impregnated (6% CCA solution), then boiled, oven-dried, normal, air-dried and steamed bamboo slices of air-dried borak bamboo (Bambusa balocca Roxb) of Bangladesh, revealed almost complete fixation in steamed (accelerated fixation) and air-dried (3 weeks, slow fixation) bamboo slices compared to moderate to slow fixation in boiled, oven-dried, normal and 24h air-dried slice...
A K Lahiry


A discussion of current theories concerning CCA fixation
1983 - IRG/WP 3238
The understanding of the fixation mechanism of CCA and related preservatives in wood has been greatly improved by a significant series of recent scientific papers. In view of recent concerns in New Zealand regarding the long-term efficacy of CCA in high decay-hazard situations, it was considered appropriate to review this recent work and to contrast it with theories presented by previous workers....
D V Plackett


nvestigation of anomalous fixation and leaching of CCA-treated red maple
2004 - IRG/WP 04-30341
The fixation of CCA-C preservative was investigated in red maple sawdust (Acer rubrum L.) at target retentions of 4.0, 6.4, 9.6 and 30.0 kg/m3. The effect of water-soluble extractives on the course of fixation was evaluated comparing the non-extracted with pre-extracted samples treated to 6.4 and 30 kg/m3. Leaching of the CCA components was monitored after complete fixation for all retentions. Fix...
S Radivojevic, P A Cooper


A simple leaching procedure for in-plant monitoring of CCA fixation
1993 - IRG/WP 93-30023
A simple leaching test is described to quantitatively estimate the extent of fixation of chromated copper arsenate (CCA) preservative treated wood products. It is based on the reaction between diphenylcarbazide and unreacted hexavalent chromium leached from borings taken from treated wood during the fixation process. The test requires about 20 minutes to complete and can be set up in a treating pl...
P A Cooper, Y T Ung


Multiple-Phase Pressure (MPP) Process: One-stage CCA treatment and accelerated fixation process. 5. Treatment of Sitka spruce and Scots pine
1999 - IRG/WP 99-40136
The suitability of the MPP Process for CCA treatment and accelerated fixation of species other than Radiata pine was assessed by pilot plant trials on UK-grown Sitka spruce (Picea sitchensis) and Scots pine (Pinus sylvestris). Pressure and vacuum kickbacks of spruce (14 l/m3) and Scots' pine (122 l/m3) were both substantially lower than that generated during treatment of radiata pine (369...
M E Hedley, K Nasheri, G Durbin


A short note on fungal decay in K33-treated poles
1982 - IRG/WP 1169
Soft rot cavities and erosion of the lumen have been found in K33-treated Pinus sylvestris poles from the years 1956-66 by microscopic studies. Poor treatment quality has been proved for some of these poles. The microscopy showed an unusual pattern of attack, and pre-treatment decay is suspected but not yet proved. Sounding the poles and using the Pilodyn indicated decay, but poking did not. Quant...
H Friis-Hansen


A fixation model, based on the temperature dependence of CCA-C fixation
2000 - IRG/WP 00-40163
A model was prepared for the fixation of 1% CCA-C in red pine that allows the prediction of extent of fixation based on the temperature history of the treated wood following pressure treatment. The reaction kinetics of the rapid initial reaction and the slower main reaction were characterized using the Van t'Hoff equation. The initial reaction could be represented by a 10th order chemical...
P A Cooper, K M F Kazi, Jianbin Chen, Y T Ung


The variation in electrical resistance in the CCA-treated wood during the fixation
1989 - IRG/WP 3554
The curve commonly used in Scandinavia for describing the fixation period at different temperatures for CCA-impregnated wood is based on investigation by Dahlgren on the pH-variations in a mixture of sawdust and preservative solution. As far as we know there is no such investigation on solid wood. We have therefore measured the electrical resistance in CCA-treated solid wood to see if this will di...
F G Evans, B Nossen


Field Test Results after Nine Years for CCA and ACQ Preservative-treated Wood Fixed in Different Climates
2003 - IRG/WP 03-30303
During assessment of the ground contact stakes in the Norwegian test field, we have frequently found that the first visual rot attack is in the zone of the stakes, where the stakes have been in contact with each other during the fixation. These parts are usually light green, caused by the lack of light during fixation, compared to the rest of the stake surface, which has a darker colour. To inves...
F G Evans


CCA fixation experiments. Part 1
1989 - IRG/WP 3504
A method of squeezing solution from CCA treated wood that has not been dried at various times after treatment appears to be useful in following the fixation of CCA in wood. Experiments confirm that temperature governs the rate of fixation....
W S McNamara


Rapid leaching test
1991 - IRG/WP 2367
An accelerated test which is suitable for measuring the extent of metal fixation in both chromium and non chromium containing preservatives is described....
J A Cornfield, M Bacon, A Lyman, C Waldie, M R Gayles


CCA Chemistry
1983 - IRG/WP 3268
A Pizzi


Effect of leaching temperature and water acidity on the loss of metal elements from CCA treated timber in aquatic conditions. Part 2: Semi-industrial investigation
1995 - IRG/WP 95-50040-13
In continuation of previous leaching research on the quantification and modelling of metal elements released from CCA treated timber, a series of experiments has been carried out dealing with the influence of temperature and pH of the relative aquatic environment. The leaching method used is the Dutch prestandard for building materials, a long term static leaching test simulating practical bank-sh...
G M F Van Eetvelde, W J Homan, H Militz, M Stevens


Study on the treatment of construction timbers by diffusion methods
1983 - IRG/WP 3252
Several species of timber that could be used for constructional purposes have to be pressure impregnated before such use. Pressure impregnation requires expensive equipment, and needs specialized trained operators, etc, which is not possible in most parts of India. Some timbers cannot be pressure impregnated, but can be treated by diffusion. Diffusion treatments could protect these timbers with si...
V R Sonti, B Chatterjee


CCA fixation experiments. Part 2
1989 - IRG/WP 3505
CCA fixation in wood was measured by both squeezing solution from treated wood that had not been dried and analyzing the solution for copper, chromium and arsenic, as well as using a chromotropic acid test to detect the presence of chromium VI. Both methods provide useful information on the CCA fixation process and illustrate that chromium VI disappears as CCA becomes fixed within wood....
W S McNamara


The influence of age on retention and fixation of CCA in pressure-treated Kenyan-grown Eycalyptus saligna: Summary of findings
2002 - IRG/WP 02-30296
The present study investigates the influence of age on retention and fixation of copper-chrome-arsenate (CCA) in Kenyan-grown Eucalyptus saligna. Samples for the study were obtained from sound trees aged 4, 8, 12, 16, 20 and 24 years. Test samples were radially cut from round material to represent total sapwood and heartwood for each age class, and measured 50mm in thickness, 100mm long, with wi...
R Venkatasamy


Copper binding capacity of modified wood flour
1992 - IRG/WP 92-3709
Wood flour was modified by reaction with oxidising agents and CCA preservative. The copper chromium and arsenic were removed from the CCA treated wood flour by an acid leaching procedure. The modified wood flours were allowed to react with copper acetate solution and the level of copper fixation achieved was determined. The modified wood flours had greater affinity for copper ions present in solut...
N C Milowych, W B Banks, J A Cornfield


Fixation of CCA in Pinus sylvestris after kiln-drying
1990 - IRG/WP 3594
Tanalith C Paste is 98% fixed and Tanalith Oxide C is 99% fixed irrespective of whether treated Pinus sylvestris is kiln or air dried. A schedule suitable for kiln drying of CCA treated Pinus sylvestris is described....
P Warburton, J A Cornfield, D A Lewis, D G Anderson


The effect of treatment temperature on the biological performance of CCA treated wood
1990 - IRG/WP 3624
Birch and Scots pine sapwood blocks were treated with several concentrations of CCA at three different temperatures: 5, 20 and 35°C. The treated wood was maintained at the appropriate temperature for the fixation period. Leached and unleached samples were then exposed in a soft rot monoculture test using Chaetomium globosum and a brown rot monoculture test using Coniophora puteana. The treatment ...
S M Gray


Ground contact performance of wood treated by the MSU process
1990 - IRG/WP 3609
Environmental concerns have prompted a renewed interest in accelerated fixation schemes for CCA-treated wood. Results from stake tests of southern pine (Pinus sp.) treated using a conventional Bethell cycle are compared with matched stakes treated using the MSU Process. The effects of adding boric acid to the preservative formulation are also discussed. Differences among test plots are discussed....
H M Barnes, T L Amburgey, R W Landers


Leaching of copper, chromium and arsenic from CCA-treated slash pine heartwood
1994 - IRG/WP 94-50020
Drying green slash pine with any of three high temperature drying schedules produced a product in which both the sapwood and the heartwood could be penetrated with CCA using a modified Bethell treatment schedule. Required H3 retentions were achieved in both sapwood and heartwood, from 200 litres per m³ charge uptake. Post-treatment fixation/drying was accomplished by three different regimes, incl...
M J Kennedy, G Palmer


The course of fixation of Cu-Cr-As wood preservatives
1972 - IRG/WP 307
Copper-chrome-arsenic (CCA) preservatives in contact with wood result in an instant extensive increase of pH, because of ion-exchange and adsorption reactions with the wood. During precipitation of the active elements the pH continuously increases but reaches a maximum, when all chrome is consumed. Some of the early reaction products are unstable and slowly convert via dissolution into stable comp...
S-E Dahlgren