EPR observation of Mn(II) in decayed wood
2002 - IRG/WP 02-10443
Preliminary Electron Paramagnetic Resonance (EPR) studies of copper/chromium (CC) treated spruce wood, subjected to laboratory soil decay test showed increased intensities of Mn(II) EPR signal in partially decayed specimens. Several reasons might be responsible for this phenomenon: Mn(II) could originate from the wood after being released from the typical ligand binding, from reduction of other Mn...
M Petric, M Humar, P Kalan, F Pohleven, U Schoknecht, M Šentjurc


Photo-degradation of modified and non-modified wood, coated with water borne acrylic coatings during artificial light exposure
2007 - IRG/WP 07-30416
A series of experiments were carried out to investigate photo-degradation of thermally modified (at 210oC and – 0.9 bars for two hours) and non-modified spruce wood (Picea abies L (Karst)), coated with transparent and semitransparent (with 3% pigment content) acrylic coatings during artificial UV light irradiation for 200 hours. Photo-degradation was evaluated in terms of colour changes througho...
M Deka, M Tomažic, M Petric


Effect of acetylation on decay resistance of wood against brown-rot, white-rot and soft-rot fungi
1989 - IRG/WP 3540
Effect of acetylation on decay resistance of wood was investigated using wood blocks of Cryptomeria japonica, Pinus densiflora, Albizia falcata and Fagus crenata. Blocks were treated with uncatalyzed acetic anhydride for different lengths of time and exposed to Tyromyces palustris, Serpula lacrymans, Coriolus versicolor and unsterilized soil. The action of OH-radical on acetylated wood was also ex...
M Takahashi, Y Imamura, M Tanahashi


Fungal degradation of wood treated with metal-based preservatives. Part 2: Redox states of chromium
1996 - IRG/WP 96-10164
Concerns have arisen about the leaching of heavy metals from wood treated with metal-based preservatives, such as chromated copper arsenate (CCA). Of particular concern is the toxic redox state of chromium and arsenic in aging and decayed CCA-treated wood. Generally, hexavalent chromium is more toxic than trivalent chromium and trivalent arsenic is more toxic than pentavalent arsenic. The desired ...
B Illman, S Bajt, T L Highley


EPR investigations of interactions between ammoniacal Cu(II) octanoate and wood
1996 - IRG/WP 96-30110
Ammoniacal solutions of copper(II) octanoate [ C u . h l f . 2 . r h l f.(O2CC7H15)4], interactions of these solutions with wood and wood components, and leaching of copper(II) octanoate from impregnated wood samples, have been studied by electron paramagnetic resonance (EPR) method. It is still not clear if in the Cu(II) octanoate - water - ammonia system, Cu(II) remains in a (copper(II) octanoat...
F Dagarin, M Petric, F Pohleven, M Sentjurc


An insight into brown rot decay of timber as revealed by 13C CP/MAS NMR
1985 - IRG/WP 1259
L E Leightley


The use of ESR spectroscopy to assess the photostabilising effects of wood preservatives
2000 - IRG/WP 00-20186
The degradation of wood surfaces exposed to UV light which leads to poor performance of clear coatings is understood to be due to delignification via a mechanism involving free radicals. Certain wood preservatives most notably CCA are able to photostabilise wood and therefore they may reduce the concentration of free radicals formed when treated wood is exposed to ultraviolet light. As a first ste...
S Schmid, R D Webster, P D Evans


EELS (Electron Energy Loss Spectroscopy) - a technique for quantification of nitrogen and other light elements in the cell wall
1999 - IRG/WP 99-20163
A literature survey was performed to find progress in techniques for monitoring penetration of synthetic resins in wood cell walls. Electron energy loss spectroscopy (EELS) in combination with transmission electron microscopy (TEM) was successfully applied for the high resolution examination of the distribution of a partly methylated hydroxymethyl melamine resin in Norway spruce (Picea abies Karst...
A O Rapp, H Bestgen, W Adam, R-D Peek


An investigation of organotin compounds in treated wood using Mössbauer spectroscopy
1983 - IRG/WP 3249
The influence of sample preparation on the 119mSn Mössbauer spectrum of tributyltin chloride in ponderosa pine was investigated. Initial studies with sawdust and compressed discs concluded that the latter were clearly superior. Further studies showed that compressed discs prepared from 0.4 g of treated wood and 0.1 g of cellulose were robust and gave excellent Mössbauer spectra. The possibility ...
J N R Ruddick, J K Ingram


UV-microspectrophotometry of lignin and accessory compounds in wood cell walls of conifers
1999 - IRG/WP 99-20171
The distribution of lignin in the cell wall of conifer tracheids was determined by UV-VIS microspectro-photometer. Wood sections of one micron thickness were measured between the wavelength 240 and 700 nm. Spectral analyses revealed that the conifer lignin associated with the tracheid secondary wall and middle lamella is composed of guiacylpropane units which exhibit a characteristic UV absorption...
G Kleist, G Koch, J Bauch


Prediction of Weight Percent Gain (WPG) of furfurylated wood by FT-NIR spectroscopy
2004 - IRG/WP 04-20295
Wood modification based on furfuryl alcohol improves several important wood properties, such as the resistance to fungal decay and insect attack, hardness, dimensional stability, bending strength and stiffness. The improvements of wood properties depend on the weight percent gain (WPG) due to furfurylation. Fourier transform near infrared (FT-NIR) spectroscopy was used to calibrate PLS-regression ...
M Eikenes, P O Flæte, E Ystrøm Haartveit, S Lande


A comparison of inductively coupled plasma spectroscopy and neutron activity analysis for the determination of concentrations in wood
1993 - IRG/WP 93-10048
As wood decays the ionic composition changes, with increases often being seen in the concentrations of Ca, Mg, Fe, Mn and sometimes K. The concentration of eight cations in red spruce sapwood and heartwood samples was determined independently by inductively coupled plasma spectroscopy (ICP) and by neutron activation analysis (NAA) as part of an effort to standardize our analytical procedures and c...
J Jellison, J Connolly, K C Smith, W T Shortle


The compatability of tributyltin fungicides and synthetic pyrethroid insecticides as wood preservatives
1987 - IRG/WP 3414
The stability of three synthetic pyrethroids, cypermethrin, deltamethrin and permethrin, to selected tributyltin compounds, Bu3SnX {where X = OSnBu3, Cl, 02CC6H5, O2C (Naphthenyl), OSO2Et}, (Bu3SnO)3PO and {NBu4} {Bu3SnCl2}, in toluene solution was investigated by infra-red spectroscopy over a six month period. It was found that only (Bu3Sn)2O reacted with the pyrethroids and that their order of r...
S J Blunden, R Hill


NIR spectroscopy for rapid estimation of decay resistance
2004 - IRG/WP 04-20294
In Scandinavia Scots pine (Pinus sylvestris L.) is an important commercial tree species. Its heartwood has traditionally been used in constructions exposed to risk of decay. In a laboratory experiment Scots pine wood specimens sampled from inner heartwood, outer heartwood and sapwood were exposed to the brown rot fungus Poria placenta. In general outer heartwood was more resistant than inner heart...
P O Flæte, E Ystrøm Haartveit


Properties of cellulose degraded by the brown rot fungus, Postia placenta
1988 - IRG/WP 1350
To gain further understanding of the nature of the cellulose depolymerizing agent or agents of brown-rot fungi, brown-rotted cellulose was chemically and physically characterized. Various culture conditions, such as low nitrogen and elevated oxygen levels, did not induce degradation of cellulose by Postia placenta in liquid cultures. Therefore, brown-rotted cellulose for analysis was prepared by a...
T L Highley, R E Ibach, T K Kirk


Differentiation of Scots pine heartwood and sapwood by near infrared spectroscopy
2003 - IRG/WP 03-10459
In Scandinavia Scots pine heartwood has, in recent years, gained popularity as material for external structures exposed to moderate risk of decay. As non-durable sapwood surrounds the heartwood in pine trunks it is of crucial importance to separate this wood from the heartwood during log processing into heartwood products. Heartwood and sapwood can be differentiated by visual evaluation of colour ...
P O Flæte, E Ystrøm Haartveit


A laboratory evaluation of tributyltin ethanesulphonate as an aqueous fungicide in wood preservation
1983 - IRG/WP 3229
Toxic limit data, using both leached and unleached wood test blocks, are reported for aqueous solutions of tributyltin ethanesulphonate against four Basidiomycete fungi, Poria placenta, Gloeophyllum trabeum, Coriolus versicolor and Coniophora puteana. An in situ study of the tributyltin compound in Scots pine and ponderosa pine sapwood has been carried out, using the technique of 119mSn Mössbauer...
R Hill, P J Smith, J N R Ruddick, K W Sweatman


Preliminary observations on tributyltin treated Scots pine sapwood using 119Sn (Mössbauer and NMR) spectroscopic techniques
1984 - IRG/WP 3312
119mSn Mössbauer data are presented for bis(tributyltin) oxide, tributyltin ethanesulphonate, bis(tributyltin) carbonate and tris(tributyltin) phosphate, both in the pure form and in Scots pine sapwood. The structures proposed for these compounds, in the solid state, are supported by 119Sn nuclear magnetic resonance spectroscopy.
R Hill


Biological test, AAS and EPR study of copper monoethanolamine complex with quaternary ammonium compounds as a wood preservative
2003 - IRG/WP 03-30321
Experiments were carried out on the wood preservative with a strong fungicidal activity based on Cu(II) carbonate, 2-aminoethanol (monoethanolamine) and quaternary ammonium compound (QAC). The object of the performed investigations was sapwood of Scots pine (Pinus sylvestris L.) treated with Cu-EA-QAC formulation. Mycological investigations were carried out according to EN 113 and EN 84 standards....
B Mazela, I Polus, S K Hoffmann, J Goslar


Uptake of copper by mycelium of wood decay fungi growing on copper S-substituted thioglycolate containing nutrient media
1998 - IRG/WP 98-10291
Mycelia of Trametes versicolor, Coniophora puteana and Poria monticola were grown on potato dextrose agar (PDA) media, containing various concentrations of copper N,N-dimethyldithiocarbamoylacetate (which may be regarded as a copper S-substituted thioglycolate). The tested copper compound revealed relatively low fungicidal activity. After 13-18 day growing period, we determined concentrations of a...
M Humar, M Petric, F Pohleven, P Kalan


Changes of EPR spectra of wood, impregnated with copper based preservatives, during exposure to Antrodia vaillantii
2000 - IRG/WP 00-10355
Spruce wood (Picea abies) samples were impregnated with two different aqueous solutions: copper(II) octanoate with ethanolamine or copper(II) sulfate (cCu = 1,0 x 10-2 mol/l). Impregnated and unimpregnated test pieces were exposed to wood rotting fungus Antrodia vaillantii. Some strains of this fungus are known as copper tolerant. After four weeks of exposure to A. vaillantii, we could not detect ...
M Humar, M Petric, F Pohleven, M Šentjurc


The examination of preservative-treated radiata pine using electron spin resonance spectroscopy
1987 - IRG/WP 3423
Electron spin resonance spectroscopy (ESR) may be used to characterise the molecular environment of chemical species containing unpaired electrons. These species include free radicals, bi-radicals, point defects in solids, localised crystal imperfections and many transition metal ions. ESR has previously been applied to the examination of wood weathering or wood pyrolysis and now FRI and Massey Un...
D V Plackett, E W Ainscough, A M Brodie


A spectroscopic investigation of copper ethylenediamine fixation in wood
1999 - IRG/WP 99-20160
The fixation reaction which take place between copper ethylenediamine (Cu-en) solution and wood were expolored using X-ray photoelectron spectroscopy (XPS) and Fourier Transformed Infrared Spectroscopy (FTIR). The FTIR spectra revealed that copper reacts with the carboxylic acid and phenolic groups in wood to form stable complexes. The copper ethylenediamine complexes formed in wood were identifie...
Xiao Jiang, J N R Ruddick


Examination of preservative-treated Pinus sylvestris using electron paramagnetic resonance
1992 - IRG/WP 92-3710
EPR is currently being used to help elucidate the nature and extent of the chemical reactions occurring between wood and copper based timber preservatives. In the work reported here treated Scots pine samples were examined at room temperature and in the frozen state. Plots of the electronic parameters A|| vs. g|| were found to be a useful index of the electronic properties of the various formulati...
A S Hughes, R J Murphy, J F Gibson, A J Cornfield


Qualitative and quantitative assessment of chemicals used for wood durability improvement by Near Infrared Spectroscopy
2006 - IRG/WP 06-20349
The Near infrared spectroscopy (NIRS) could be a suitable technique to assess chemicals used for wood durability improvement in the forest products industry. NIRS methodology can be used to obtain results more quickly, less costly and without damaging the wood. In this study, wood samples selected from heartwood and sapwood of Maritime Pine (Pinus pinaster) were prepared to assess the artificial d...
S Zahri, F Charrier, H Baillères, B Charrier