Evaluation and approval of wood preservatives in Japan
1988 - IRG/WP 2303
Japanese standardized decay test methods, performance requirements and approving system are briefly described. JIS (Japanese Industrial Standard) A 9302, which is related to a testing method for evaluating effectiveness of wood preservatives when applied to pressure treatment, is fundamentally a sand-block laboratory test method. According to performance requirements in JIS A 9201, mean percentage...
K Tsunoda
Laboratory evaluation of organophosphates as termiticides
1985 - IRG/WP 3330
In accordance with Japan Wood Preserving Association Standard 11(1) laboratory evaluations of five organophosphate insecticides and chlordane were conducted. Superficially treated sapwood of Pinus densiflora Sieb. et Zucc. (10 x 10 x 20 mm³) was compulsorily exposed to the attacks of 150 workers and 15 soldiers of Coptotermes formosanus Shiraki for 21 days at 28±2°C in the dark. Percentage weig...
K Tsunoda, K Nishimoto
Results from soft rot tests in vermiculite jars
1976 - IRG/WP 272
T Vihavainen
Biodegradation of acetylated southern pine and aspen composition boards
1994 - IRG/WP 94-40020
This objective of this study was to investigate the influence of the acetylation treated wood fiber, Phenol-formaldehyde resin content level, two wood fiber species, three fungi species on the dimensional stability and decay resistence of high density composition boards. A standard ASTM method was used to evaluate weight loss and thickness change. The linear shrinkage and expansion of each species...
P Chow, T Harp, R Meimban, J A Youngquist, R M Powell
Effects of a formaldehyde and sulphur dioxide treatment on decay and mechanical properties of aspen waferboard
1983 - IRG/WP 3242
Aspen wafers were sequentially treated under vacuum with formaldehyde and sulfur dioxide gas and pressed into waferboard bonded with powdered phenol formaldehyde resin. Decay resistance and strength properties were determined before and after simulated weathering. The water resistance of the phenol bonding system was lost in board made from the gas-treated wafers. This white rot fungus Coriolus ve...
E L Schmidt
About the relations between the natural durability of some tropical species and their extractives content
1983 - IRG/WP 1208
G R Y Déon
Virulence tests with fungal strains used in EN 113 CEN ring test. Results with Coniophora puteana (Schum.ex Fr.) Karst
1986 - IRG/WP 2249
D Dirol
Collaborative soft rot experiments 1974. Preliminary analysis of results
1975 - IRG/WP 251
J K Carey, J G Savory
Relative performances of DNBP and CCA wood preservatives in accelerated decay tests
1988 - IRG/WP 3496
The effectiveness of 2-sec-butyl-4,6-dinitrophenol (DNBP) was compared with that of CCA. Test blocks of Pinus patula and Eucalyptus grandis were impregnated to precisely known retentions of approximately 3, 6, and 10 kg/m³ CCA and solvent-borne DNBP respectively. They were then challenged in decay tests comprising soil burial and exposure to monocultures of Chaetomium globosum, Coriolus versicolo...
W H Schnippenkoetter, L D Abraham, A A W Baecker
Evaluation of New Zealand staining fungi for degradation of radiata pine
1999 - IRG/WP 99-10310
This investigation sought to determine the potential of selected NZ staining fungi to induce weight loss and changes in toughness (impact bending strength) and composition in unseasoned radiata pine sapwood. Furthermore, assays were performed to eveluate enzyme production by staining fungi. Sets of side-matched specimens were inoculated with Ophiostoma floccosum, Sphaeropsis sapinea and O. plurian...
A Schirp, R L Farrell, B Kreber
Effects of Trichoderma harzianum on enzyme activity and oxalic acid production of Gloeophyllum trabeum in ponderosa pine sapwood blocks
1992 - IRG/WP 92-1550
The effect of a bioprotectant, Trichoderma harzianum, on the activity of Gloeophyllum trabeum was investigated using a wood wafer sandwich method. Wood weight loss was greatest with Gloeophyllum trabeum exposed wafers, intermediate with those exposed to both the bioprotectant and decay fungus, and lowest with the bioprotectant exposed wafers. Extracts of wood wafers after 2, 4, or 6 weeks of funga...
C M Sexton, J J Morrell
The performance of CCA treatment in bamboo against decay fungi
1993 - IRG/WP 93-30027
Samples of culm wall material from young (< 6 month age) and mature (> 3 years age) culms of the bamboo, Phyllostachys virideglaucescens were treated to equivalent% w/w retentions of a CCA preservative. After fixation and leaching the treated samples were exposed to decay by Chaetomium globosum FPRL S70K, Coriolus versicolor FPRL 28A and Coniophora puteana FPRL 11E. Thin section samples of u...
O Sulaiman, R J Murphy
Effectiveness of Busan 30 treated birch blocks in a soil medium
1987 - IRG/WP 3409
TCMTB based formulation has been anticipated for use in dip-diffusion treatment in Papua New Guinea to replace BFCA Wood preservative. One such formulation is the Penacide (TCMTB + MBT Boron) which is currently being tested against fungi and insects. Accelerated laboratory test in soil exposure was employed to test a related formulation (Busan 30) to determine its effectiveness against soil inhabi...
H C Konabe
Kinetic of the wood degradation produced by wood decay fung
1993 - IRG/WP 93-20016
The degradation degree of a wooden structure has a direct influence on its loss of mechanical strength. It's necessary to deepen in non destructive techniques which permit to extrapolate the results obtained in laboratory to structural timber used in the building's construction. This work studies the relationship existing between the pulse velocity of ultrasonic waves and the wei...
M T De Troya, A M Navarrete, A Sanchez, V Bucur
High CCA retentions and the protection of eucalypt power poles
1983 - IRG/WP 3226
Tasmanian power pole material treated to high retentions, was analysed to accurately determine the amount of CCA preservative in the timber. Material from the same disc was subsequently exposed in unsterile soil in order to determine the effectiveness of treatment. Results showed that even at high retention levels, soft-rot attack was not prevented. Fourteen further poles were sampled, but this ti...
L E Leightley, J Norton
The effect of ACC (Celcure) on durability of blue beech
1999 - IRG/WP 99-30209
Durability of the sapwood and heartwood of blue beech (Carpinus betulus) against white rot fungus (Coriolus versicolor) was studied. As treatment three concentrations of preservative (control or 0%, 3%, and 5% of ACC) were applied. The measuring 1.5x2.5x5cm3 as dimension of wood samples (sap and heartwood) was used. During 16 weeks exposure, untreated wood blocks were completely deteriorated by th...
S M Kazemi
Decay Resistance and Bonding Properties of Structural Flakeboard
2002 - IRG/WP 02-40233
Experimental structural flakeboard panels consisting of differing furnishes and resins were produced and tested for internal bond, linear expansion, thickness swell, and decay resistance. One group of panels was produced with recycled CCA-treated wood as the furnish and commercial phenol formaldehyde (PF) resin as the binder. Other groups of panels were produced with either mixed hardwoods or so...
T F Shupe, Chung-Yun Hse
Decrease of the antidecay resistance of beech wood treated with organotin fungicides after its natural ageing
1998 - IRG/WP 98-30185
The antidecay resistance of beech-wood samples (120 x 8.5 x 8.5 (MM)) treated with tributyltin fungicides gradually decreased due to prolongation of their natural ageing:
tributyltin fungicides (TBTO, TBTS, TBTCA, TBT-DEDTK were applied by pressure impregnation technique in ethanole solutions (c = 0. 1%, 0.33% or 1%);
treated beech-wood samples were naturally aged without their contact with grou...
L Reinprecht
EELS (Electron Energy Loss Spectroscopy) - a technique for quantification of nitrogen and other light elements in the cell wall
1999 - IRG/WP 99-20163
A literature survey was performed to find progress in techniques for monitoring penetration of synthetic resins in wood cell walls. Electron energy loss spectroscopy (EELS) in combination with transmission electron microscopy (TEM) was successfully applied for the high resolution examination of the distribution of a partly methylated hydroxymethyl melamine resin in Norway spruce (Picea abies Karst...
A O Rapp, H Bestgen, W Adam, R-D Peek
Wood decay of Pinus sylvestris L. by marine fungi
1990 - IRG/WP 1463
Waterlogged wood decay by marine microorganisms represents a major problem for the conservation of wood structures of historic value. It is important to know which kind of decay affects the wood from a conservation point of view. Enzyme activities of 14 marine fungi belonging to several localities were studied. Also, the weight loss and the rot type suffered by the wood at a microscopic level were...
M C Escorial, M T De Troya, J E Garcia de los Rios
Treatment of wood with formaldehyde. Acid catalysis of the reaction between formaldehyde and wood
1980 - IRG/WP 3146
Formaldehyde reacts with the free OH-groups in wood forming cross-linking bonds. The reaction can be brought about without any catalyst but in that case the activation energy is very high and high temperatures and long reaction times are needed. Normally, the reaction is catalysed by different acids. Acid catalysts, however, tend to degrade the cellulose and the wood matrix causing reduction in th...
T Vihavainen, K Piispanen, P Mansikkamäki
Microscopical analysis of formaldehyde-acid modified wood
1981 - IRG/WP 3182
Cross-linking of wood with gaseous formaldehyde improves its hygroscopic and dimensional behaviour, and its resistance against micro-organisms. However, formaldehyde cross-linking reactions take place only in the presence of an acid catalyst, which results in losses in mechanical By optimization of a formaldehyde-sulfur dioxide vapour phase process the reaction conditions were established to limit...
M Stevens, N Parameswaran
Investigation on different variation factors in the results of mycological test and means to reduce and avoid them
1986 - IRG/WP 2264
In order to clarify the causes of the dispersion observed in the results obtained with mycological tests made in accordance with standard EN-113, different factors assumed to be sources of the variations were studied. These included the moisture content of the test samples during the test, the influence of certain technological properties of the wood, the virulence of the fungus strains, the metho...
D Dirol
Decay and mold resistance of borate modified oriented strandboard
2003 - IRG/WP 03-40260
Decay and mold resistance of zinc borate (ZB) and calcium borate (CB) modified
oriented strandboard (OSB) from southern mixed hardwoods and yellow pine was investigated in this study. Tests were done with brown rot, Gloeophyllum trabeum, and white-rot, Trametes versicolar, fungi for 8 and 12 weeks, respectively. Wood species and fungus type had significant influence on the decay resistance. Decay...
Q Wu, S Lee, J P Jones
The use of modulus of rupture and modulus of elasticity in natural durability testing
1997 - IRG/WP 97-20117
Losses in weight, losses in bending strength and changes in elastic behaviour were assessed in a fungus cellar test with beech wood stakes (Fagus sylvatica). Results were gained after 8, 12, 16 and 20 weeks resp . The outcomes show, that the non-durable species beech is very rapidly attacked by fungi and loses up to 60% of its initial bending strength even within the first 8 weeks. Earlier researc...
L Machek, H Militz, W Gard