Dimensional stabilization of wood with dimethylol compounds
1987 - IRG/WP 3412
This study showed that a substantial degree of dimensional stability can be imparted to wood by crosslinking with low concentrations of dimethyloldihydroxyethyleneurea. It was demonstrated that by selecting the right catalyst system the cure temperature can be reduced to the point that strength loss of the treated wood is minimized....
D D Nicholas, A D Williams
Steam conditioning of partially dried radiata and Corsican pine roundwood
1988 - IRG/WP 3499
The effect of partial air drying prior to steam conditioning and its effect on subsequent preservative treatment by the Bethell treatment process was investigated. A high standard of preservative treatment was obtained in both radiata and Corsican pine, irrespective of whether a period of partial drying was imposed before or after steam conditioning....
P Vinden, D R Page, K Nasheri
Decay patterns observed in butylene oxide modified ponderosa pine attacked by Fomitopsis pinicola
1983 - IRG/WP 1183
Small blocks of ponderosa pine chemically modified by butylene oxide to three different weight percent gains (WPG) were decayed for 2 months with the brown rot fungus Fomitopsis pinicola. Wood substance loss and the type of decay pattern recognised were fairly similar both for control and blocks treated to 8 and 15 WPG. No difference in attack was observed between radial or tangential walls in lat...
T Nilsson, R M Rowell
Effect of Trichoderma harzianum on induction of laccase by Trametes versicolor on ponderosa pine sapwood
1996 - IRG/WP 96-10177
Trichoderma harzianum has long been studied as a possible biocontrol agent against wood degrading fungi, and has provided varying degrees of protection in several European field trials. In laboratory trials, however, this fungus appears to be less active against white rot fungi. This characteristic was studied using a wood wafer sandwich procedure which simultaneously expose ponderosa pine sapwood...
E A Canessa, J J Morrell
Effect of borate on uptake and efficacy of an anti-sapstain treatment
2005 - IRG/WP 05-30380
The potential for using borates to enhance uptake and efficacy of propiconazole-based anti-sapstain chemicals was assessed on ponderosa pine sapwood wafers. Borates had no consistent effect on either net solution absorption or propiconazole distribution in the wood. Even small amounts of borate, however, markedly improved the performance of propiconazole against fungal discoloration. These resul...
Jianju Luo, Hua Chen, J J Morrell
TBTO absorption and penetration in pine joinery treated by various processes
1989 - IRG/WP 3523
Matched sections of several White pine (Pinus strobus) and Ponderosa pine (Pinus ponderosa) mouldings were treated with TBTO by Double vacuum, modified empty-cell, 15 second dip and several preheating treatments followed by a 15 s dip treatments. As expected the double vacuum and empty-cell (batch) treatments resulted in much greater retentions and penetrations than the dip treatments. The absorpt...
P A Cooper, Y T Ung
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell
Effects of Trichoderma harzianum on enzyme activity and oxalic acid production of Gloeophyllum trabeum in ponderosa pine sapwood blocks
1992 - IRG/WP 92-1550
The effect of a bioprotectant, Trichoderma harzianum, on the activity of Gloeophyllum trabeum was investigated using a wood wafer sandwich method. Wood weight loss was greatest with Gloeophyllum trabeum exposed wafers, intermediate with those exposed to both the bioprotectant and decay fungus, and lowest with the bioprotectant exposed wafers. Extracts of wood wafers after 2, 4, or 6 weeks of funga...
C M Sexton, J J Morrell
Leachability of didecyldimethylammonium chloride (a quaternary ammonium compound) from four wood species
1982 - IRG/WP 3204
Sapwood blocks prepared from red pine, ponderosa pine, southern yellow pine and hem-fir (a commercial mixture of western hemlock and amabilis fir) were treated with didecyldimethylammonium chloride, (an alkylammonium compound, AAC). After oven drying the blocks were vacuum impregnated with distilled water and subjected to a static leach cycle for 48 hours. The leachate was analyzed and the amount ...
J N R Ruddick, A R H Sam
Colonization of treated and untreated ponderosa pine exposed in Hilo, Hawaii
1995 - IRG/WP 95-20068
The rate of decay in above ground exposures is largely controlled by rainfall and temperature, factors which can be used to construct a climate index of decay hazard in above ground exposures. Developers of new biocide formulations have utilized this knowledge by establishing test sites in sub-tropical regions such as the Gulf Coast of the United States. More recently, field sites have been locate...
C M Freitag, J J Morrell, K J Archer
Effect of Pseudomonas cepacia on the activity of a mixture of wood staining fungi on ponderosa pine sapwood
1995 - IRG/WP 95-10107
There are major incentives for limiting the degree of fungal discoloration which occurs during wood processing. Most lumber producers apply prophylactic fungicides which limit microbial growth, but increasing restrictions on the use of these chemicals have encouraged the search for alternative stain prevention strategies. Among the possible strategies for stain prevention is biological control. Wh...
J J Morrell, R K Velicheti
Internal pressure development in Douglas fir lumber during pressure treatment
1997 - IRG/WP 97-40091
Preservative treatment of Douglas fir lumber to meet current industry standards poses a major challenge and a variety of methods have been developed to overcome these problems. One aspect for treatment improvement that has received less attention is the relative effect of treatment parameters on changes in pressure within the wood. Previous studies of spruce and radiata pine suggest that internal ...
P F Schneider, J J Morrell
Effects of heat treatments on decay resistance and material properties of ponderosa pine and yellow poplar
2007 - IRG/WP 07-40374
The potential for using heat treatment to improve the properties of North American fenestration species was evaluated on ponderosa pine (Pinus ponderosa L) and yellow poplar (Liriodendron tulipifera L) treated using the ThermoWood process at various treatment temperatures and times. Soil block tests using Gloeophyllum trabeum, Postia placenta, or Trametes versicolor showed that durability was enh...
C Vidrine, C Freitag, J Nicholson, J J Morrell
Using an accelerated laboratory method to evaluate Aureobasidium pullulans colonization on painted surfaces and underlying wood substrate
2012 - IRG/WP 12-20480
Mold growth on painted surfaces can lead to premature paint film failure and is unsightly. Aureobasidium pullulans has been identified as a major cause of black stain on surfaces painted with acrylic or latex paints. In this study, an accelerated laboratory method developed by Zabel and Horner (1981) was used with modifications to the type of agar used and sample evaluation methods. A study was ...
C Schauwecker, L Burns, A Preston
Performance of 3-iodo-2-propynyl butyl carbamate (IPBC) in L-joints under tropical conditions
2016 - IRG/WP 16-30688
The ability of 3-iodo-2-propynyl butyl carbamate (IPBC) to protect wood against fungal decay out of soil contact was evaluated using ponderosa pine L-joints at two exposure sites over a 12 year period. IPBC tended to provide better protection when formulated in an organic solvent and when applied using a double vacuum treatment. Performance also tended to be better when systems contained a water...
J J Morrell
Confocal laser scanning microscopy of a novel decay in preservative treated radiata pine in wet acidic soils
1997 - IRG/WP 97-10215
Light microscopy of radiata pine (Pinus radiata D. Don) field test stakes (20x20x500mm3) exposed in wet acidic (pH 3-4) soil for 12 - 24 months showed predominance of an unusual type of decay characte-rised by tunnelling attack of wood cell walls. After two years decay was moderate to severe in wood treated to ground contact CCA specifications and also equivalent retentions of creosote, and a numb...
R N Wakeling, Ying Xiao, A P Singh
Field trial with poles of Scots pine treated with six different creosotes
1996 - IRG/WP 96-30115
In the middle of the 50's field trials with creosote-treated poles were started in France, Germany and Sweden. The trials were initiated by WEI (Western-European Institute for Wood Preservation). Six different creosotes were used and 40 poles per creosote were installed at each test field. Results after 39 years of exposure in Simlangsdalen, Sweden are reported. Poles treated with a heavy...
Ö Bergman
Screening potential preservatives against stain and mould fungi on pine timber in Zimbabwe
1995 - IRG/WP 95-30063
The search for environmentally and toxicologically safer chemicals for use in the timber preservative industry against stain and mould fungi has been intensified during the past few years. Results of field tests with two chemicals previously evaluated in the laboratory are presented. The conventional sodium pentachlorophenate was the more efficacious chemical against stain and mould fungi, providi...
A J Masuka
Dimensional stability and decay resistance of hot-melt self-bonded particleboard by surface benzylated pine chips
1991 - IRG/WP 3652
Akamatsu (Pinus densiflora Sieb. et Zucc: Japanese red pine) particles were pretreated with 40% NaOH solution and benzylated with benzyl chloride, and the surface of particle was converted into meltable materials. Hot-melt self bonded particleboard having smooth and high glossiness surface was prepared by hot pressing at 150°C and 1.96 MPa without using any conventional adhesives. Dimensional sta...
M Kiguchi, K Yamamoto
Strength loss associated with steam conditioning and boron treatment of radiata pine framing
1987 - IRG/WP 3438
The combined effect of included defects and wood moisture content on the strength loss of second rotation radiata pine framing following conventional steam conditioning is investigated. The green Modulus of Elasticity (MOE) is reduced by approximately 13% after steaming. When dried after steaming, however, neither the MOE nor MOR is significantly different from unsteamed dried controls....
M J Collins, P Vinden
Soil virulence tests using Scots pine sapwood
1973 - IRG/WP 222
Following the tests reported in Document No: IRG/WP/210, in which soils from different laboratories were investigated for virulence, supplementary tests have been carried out using Scots pine sapwood and an extended incubation period....
J K Carey, J G Savory
Types of decay observed in CCA-treated pine posts in horticultural situations in New Zealand
1984 - IRG/WP 1226
The few reported failures of 11-12-year-old horticultural posts in New Zealand in 1982 were caused by brown-rot. A subsequent survey of CCA-treated posts in all the major horticultural areas has revealed decay of many posts. A microscopic examination of these posts has shown decay by brown-rot, white-rot, soft-rot and bacteria. Several types of bacterial decay have been observed....
J A Drysdale, M E Hedley
Light organic solvent preservative treatment schedules for New Zealand-grown radiata pine
1986 - IRG/WP 3379
The influence of pressure differential and treatment time on preservative uptake and distribution in radiata pine heartwood and sapwood is investigated. Treatment schedules are defined which minimise solvent usage but ensure complete sapwood penetration and optimise heartwood penetration....
P Vinden
Termite resistance of pine wood treated with chromated copper arsenates
1997 - IRG/WP 97-30128
Two four-week, no-choice laboratory tests were performed with CCA-treated southern yellow pine and radiata pine against Formosan subterranean termites, Coptotermes formosanus. CCA retentions as low as 0.05 kg/m3 (0.03 pcf) provided protection from all but light termite attack (rating of 9 on a 10-point visual scale). Similar and consistent light attack on wafers containing retentions as high as 6....
J K Grace
Durability of pine modified by 9 different methods
2004 - IRG/WP 04-40288
The decay resistance was studied for pine modified by nine methods of wood modification: 1) Acetylation, 2) Treatment with methylated melamine resin (MMF), 3) Acetylation followed by post-treatment with MMF-resin, 4) Thermal modification, 5) Furfurylation, 6) Maleoylation (using water solution of MG or ethanol solution of maleic anhydride), 7) Succinylation, 8) NMA-modification and 9) modification...
M Westin, A O Rapp, T Nilsson