Evaluation of ACQ-D treated Chinese fir and Mongolian Scots pine with different post-treatments after 20 months of exposure
2010 - IRG/WP 10-30530
The performance of alkaline copper quat-type D (ACQ-D) treated Chinese fir (Cunninghamia lanceolata Hook.) and Mongolian Scots pine (Pinus sylvestris Linn. var. mongolica Litv.) stakes after 20 months exposure in Chengdu and Guangzhou of southern China were evaluated according to AWPA standard E07-07. The ACQ-D treatments used two concentration levels (0.5 and 1.0%) and four different post-treatme...
Lili Yu, Jinzhen Cao, Wei Gao, Haitao Su
Testing of decay resistance of sapwood and heartwood of thermally modified Scots pine and Norway spruce
2010 - IRG/WP 10-40523
Thermal modification at elevated temperatures changes the chemical, biological and physical properties of wood. One of the main targets of thermal modification is to increase the biological durability and decay resistance of wood. Although the effects of thermal modification on wood have been widely studied, the significance of sapwood and heartwood on the resistance of thermally modified wood has...
H Viitanen, S Metsä-Kortelainen
The Effectiveness of Machined Profiles at Reducing the Checking of Wooden Decking
2011 - IRG/WP 11-40541
This study tests the hypothesis that ‘the ability of surface profiling to reduce checking of deck boards exposed to weathering will vary with wood species and profile type’. Southern pine (Pinus sp.) and Pacific silver fir (Abies amabilis) deck boards were machined to produce three different types of surface profiles: flat (control), ribbed (V-shaped grooves), and rippled (U-shaped grooves). B...
P Evans, I Cullis, P Morris
Water absorption and desorption of non treated, pressure impregnated, and pine oil treated glulam made of small diameter Scots pine and Norway spruce
2012 - IRG/WP 12-40616
A growing proportion of harvested timber originates from the first or second commercial thinning stands in Finland, which means smaller average log volumes in comparison to final felling stands. Smaller log volume means challenging wood properties such as higher proportion of juvenile wood and sapwood. Due to these facts, products made of small diameter logs are prone to twist and check, and have ...
H Heräjärvi, V Möttönen, R Stöd
Extraction and analysis of DNA from green and seasoned timber as basic methods for determination of wood species and origin
2013 - IRG/WP 13-20523
Against the background of the European timber trade regulation EUTR, commenced to law by March 2013, the determination of wood species and tracing of its origin is getting a great importance. A promising approach for establishing fast and reliable tracking systems for wood products is DNA analysis. A critical point is the extraction of analysable DNA from the wood and its lignified cell walls. Thu...
K Jacobs, H Mende, W Scheiding
Copper and chromium leaching from wood impregnated with chromium-copper containing preservatives: Results of different studies
2014 - IRG/WP 14-50300
Copper and chromium based wood preservatives remained one of the most important ingredients for wood protection solutions for protection of wood in demanding applications all-over the world. Leaching of heavy metals from treated wood is important from two different aspects; firstly from performance point of view, and secondly from environmental issues. However, the importance of these studies is i...
M Humar, N Thaler, E Melcher
Influence of artificial and natural weathering on water exclusion efficacy of wood
2015 - IRG/WP 15-20559
Water exclusion efficacy (WEE) is one of the most important properties of wood that contributes to the overall performance of naturally durable wood species in outdoor above ground applications. WEE is in strong correlation with moisture dynamics of wood, its hydrophobicity and can indicates susceptibility against wood decay fungi. Despite of the importance of this parameter, WEE is not completely...
M Žlahtič, M Humar
Dynamics of biofilm formation on wood impregnated with vegetable oils
2016 - IRG/WP 16-40769
Biofilms can be used as a living protective coating for wood, showing advantages compared to traditional wood-coatings regarding sustainability and self-repair. Biofilms can be formed on oil impregnated wood. Such an oil-biofilm system has the potential of protecting the wood against UV and bio degradation, creating a homogeneously black surface with self-healing properties. Results of biofilm for...
K Filippovych, H Huinink, L van der Ven, O C G Adan
Decay resistance of beams made from thermally modified Scots pine and Norway spruce after 6 years’ exposure in ground contact
2017 - IRG/WP 17-40806
In the present study the resistance of beams treated by ThermoWood® process was studied in ground contact and the results given are based on a “modified” EN 252 test. After six years’ exposure clear differences were found between untreated Scots pine and Norway spruce beams and treated ones. In all cases thermal modification improved the performance. Thermally modified pine heartwood showed...
S Metsä-Kortelainen, H Viitanen
Impact of sapwood portions on the durability of adjacent heartwood of Pinus sylvestris, Pseudotsuga menziesii and Quercus robur. Part 1: Laboratory studies
2018 - IRG/WP 18-10922
Sapwood is generally considered as non-durable and assigned to durability class DC 5 according to European standards independent from the wood species. It is commonly agreed that sapwood decays faster than adjacent heartwood, but it is controversially discussed whether sapwood serves as feeder material and thus accelerates onset and progress of decay in more durable heartwood or decays independent...
C Brischke, P Homann, A Gellerich
Monitoring uptake and penetration of pesticides during impregnation of pine (Pinus sylvestris) and spruce (Picea abies) wood with bio-based microemulsion gel formulations
2020 - IRG/WP 20-30756
Even in dry state wood is susceptible to biological degradation. Preservation against biological decay in exposed conditions is conventionally achieved by impregnating the wood with pesticides applied at professional and industrial levels. Impregnation of wood with preservatives is a complex process that involves wood macro- and microstructure, and the physical characteristics of woods. Here we fo...
D Messaoudi, K Ruel, J-P Joseleau
Sterilization of Large Timbers during Preservative Treatment: How Quickly We Forget
2020 - IRG/WP 20-40902
Air seasoning is a common method of moisture management in utility poles and is done de facto during pole storage prior to treatment. However, extended air drying prior to treatment encourages fungal attack and can facilitate establishment of decay fungi in poles before a protective preservative barrier is applied. This problem can be mitigated by proper air-seasoning methods coupled with heat ste...
G Presley, J Cappellazzi, M Konkler, K Maguire, R Nelson, J J Morrell
Studies on the material resistance and moisture dynamics of Douglas fir and Sitka spruce from Slovenia
2021 - IRG/WP 21-20677
Wood in outdoor applications is subject to various decomposition factors. Wood degradation can be prevented by construction details, biocide protection of wood, wood modification, or selection of naturally durable wood species. Unfortunately, the majority of timber species in Europe do not have naturally durable wood. Imported tree species represent a new pool from which we can draw wood species w...
M Humar, B Lesar, D Krzisnik, E Kerzic, R Brus
Evaluation of vacuum borate treated spruce or pine CLT in an above ground protected test in southern Mississippi
2024 - IRG/WP 24-41001
Cross laminated timber (CLT) has become a popular wood composite in large building applications that were previously limited to concrete and steel. To extend service and prevent biological attack, chemical protectants are often applied to wood. Cross laminated timber panels are not typically treated, in part due to a lack of data on efficient and effective methods for treating large panels. Ther...
M E Mankowski, A Taylor, G T Kirker
Analysis and performance of spruce alternative species and discarded wood for windows production
2024 - IRG/WP 24-50386
Climate change is having a significant impact on European forestry, particularly on the softwood species used for window frames. This study investigates potential replacement tree species for spruce (Picea abies), the predominant material for window frames. We evaluate Douglas fir (Pseudotsuga menziesii), Scots pine (Pinus sylvestris), thermally modified poplar (Populus nigra) and discarded silver...
B Lesar, J Levanič, M Humar, A Treu
Confocal laser scanning microscopy of a novel decay in preservative treated radiata pine in wet acidic soils
1997 - IRG/WP 97-10215
Light microscopy of radiata pine (Pinus radiata D. Don) field test stakes (20x20x500mm3) exposed in wet acidic (pH 3-4) soil for 12 - 24 months showed predominance of an unusual type of decay characte-rised by tunnelling attack of wood cell walls. After two years decay was moderate to severe in wood treated to ground contact CCA specifications and also equivalent retentions of creosote, and a numb...
R N Wakeling, Ying Xiao, A P Singh
Field trial with poles of Scots pine treated with six different creosotes
1996 - IRG/WP 96-30115
In the middle of the 50's field trials with creosote-treated poles were started in France, Germany and Sweden. The trials were initiated by WEI (Western-European Institute for Wood Preservation). Six different creosotes were used and 40 poles per creosote were installed at each test field. Results after 39 years of exposure in Simlangsdalen, Sweden are reported. Poles treated with a heavy...
Ö Bergman
Status of the research and development of a new preservative system (EFPL) for pressure treatment of spruce in Canada
1975 - IRG/WP 348
Our work has been to develop a system which would have the stability of the ACA system and the formulation flexibility of the CCA system enabling properties such as fixation of arsenic, water repellency, appearance and cost to be controlled. Our permeability studies of spruce using a method previously developed indicated that an ammoniacal solution of copper arsenate is an excellent candidate for ...
J Rak, M R Clarke
Screening potential preservatives against stain and mould fungi on pine timber in Zimbabwe
1995 - IRG/WP 95-30063
The search for environmentally and toxicologically safer chemicals for use in the timber preservative industry against stain and mould fungi has been intensified during the past few years. Results of field tests with two chemicals previously evaluated in the laboratory are presented. The conventional sodium pentachlorophenate was the more efficacious chemical against stain and mould fungi, providi...
A J Masuka
Strength loss associated with steam conditioning and boron treatment of radiata pine framing
1987 - IRG/WP 3438
The combined effect of included defects and wood moisture content on the strength loss of second rotation radiata pine framing following conventional steam conditioning is investigated. The green Modulus of Elasticity (MOE) is reduced by approximately 13% after steaming. When dried after steaming, however, neither the MOE nor MOR is significantly different from unsteamed dried controls....
M J Collins, P Vinden
Soil virulence tests using Scots pine sapwood
1973 - IRG/WP 222
Following the tests reported in Document No: IRG/WP/210, in which soils from different laboratories were investigated for virulence, supplementary tests have been carried out using Scots pine sapwood and an extended incubation period....
J K Carey, J G Savory
Types of decay observed in CCA-treated pine posts in horticultural situations in New Zealand
1984 - IRG/WP 1226
The few reported failures of 11-12-year-old horticultural posts in New Zealand in 1982 were caused by brown-rot. A subsequent survey of CCA-treated posts in all the major horticultural areas has revealed decay of many posts. A microscopic examination of these posts has shown decay by brown-rot, white-rot, soft-rot and bacteria. Several types of bacterial decay have been observed....
J A Drysdale, M E Hedley
Effect of a penta emulsion on the service life of Douglas fir, heartwood posts
1978 - IRG/WP 3112
C S Walters
Dimensional stability and decay resistance of hot-melt self-bonded particleboard by surface benzylated pine chips
1991 - IRG/WP 3652
Akamatsu (Pinus densiflora Sieb. et Zucc: Japanese red pine) particles were pretreated with 40% NaOH solution and benzylated with benzyl chloride, and the surface of particle was converted into meltable materials. Hot-melt self bonded particleboard having smooth and high glossiness surface was prepared by hot pressing at 150°C and 1.96 MPa without using any conventional adhesives. Dimensional sta...
M Kiguchi, K Yamamoto
Comparison of cubic and plug samples for preparation and data assembly in permeability study
2000 - IRG/WP 00-20197
In order to determine if plug experimental samples (PES: 30 x 15 mm2 diameter) could be used for inspection of wood permeability characteristics, radial and longitudinal flow directions were prepared according to either PES or cubic experimental samples (CES: 100 x 20 x 20 mm3) from the sapwood zone of Sitka spruce and treated by tanalith-C according to full-cell process. Results from the two prep...
I Usta