Leaching of Active Components from Preservative Treated Timber. Stage 1: Semi-Field Testing
2004 - IRG/WP 04-20302
The project is aiming at finding realistic leaching rates from preservative-treated wood in use class 3 (above ground). The project focuses on developing a field trial method for investigating leaching.
Panels are subjected to outdoor exposure under natural weather conditions at a test field at the Danish Technological Institute. The leachate is collected and monitored by chemical analysis of the...
N Morsing, B Lindegaard
Decay patterns observed in butylene oxide modified ponderosa pine attacked by Fomitopsis pinicola
1983 - IRG/WP 1183
Small blocks of ponderosa pine chemically modified by butylene oxide to three different weight percent gains (WPG) were decayed for 2 months with the brown rot fungus Fomitopsis pinicola. Wood substance loss and the type of decay pattern recognised were fairly similar both for control and blocks treated to 8 and 15 WPG. No difference in attack was observed between radial or tangential walls in lat...
T Nilsson, R M Rowell
Chemical investigation of 23-year-old CDDC treated southern yellow pine
1997 - IRG/WP 97-30141
The effect of 23 years exterior exposure on CDDC treated southern yellow pine was evaluated by the application of solid state analytical instrumentation. Analytical methods including environmental scanning electron microscopy (ESEM),energy dispersive X-ray analysis (EDXA), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), inductively coupled plasma (ICP) and atomic absorption spectr...
D P Kamdem, C R McIntyre
Biological and chemical observation on the early fungal colonization of TBTO treated Swedish redwood stakes
1984 - IRG/WP 3311
Data on the early fungal colonization of Swedish redwood stakes, impregnated with 1% TBT0 / 0.5% dieldrin solution, both by double vacuum impregnation and immersion processes are presented. Results of chemical analyses of wood samples from the outer 1 mm of separate painted and unpainted stakes, exposed over the same twelve month period, are also discussed....
R Hill, A H Chapman, A Samuel, K Manners, G Morton
Chlorodioxines dans le pentachlorophénol
1975 - IRG/WP 346
H Alliot
Contribution of wood components on the absorption of copper amine
2000 - IRG/WP 00-30216
The contribution of wood components on the absorption of copper amine was investigated. Holocellulose, lignin and xylan absorbed significant amount of copper. The amount of copper absorbed by cellulose was almost negligible. The removal of extractive also decreased the amount of copper absorption. This study clearly indicates the importance of lignin, hemicellulose in the absorption of copper amin...
D P Kamdem, Jun Zhang
Tebuconazole - Efficiacy, toxicity, physical properties
1995 - IRG/WP 95-30093
An overview ahout the physical properties and toxicology of tebuconazole as well as an update of efficacy data of this triazole are given....
H-U Buschhaus
Chlorodioxins in pentachlorophenol
1975 - IRG/WP 346 E
At the 6th meeting of the IRG/WP plenary group held on 20 June, 1974, in Vienna, Mr Richardson expressed some concern about dioxins which might be contained as impurities in pentachlorophenol and in sodium pentachlorophenoxide or which might be formed during the combustion of treated wood. He mentioned the malformations that have been noted in Vietnam due to the teratogenic action of the 2, 3, 7, ...
H Alliot
About the water and biological resistance of some new chemically modified wood composites
1997 - IRG/WP 97-40077
As well known, wood represents a valuable natural composite material with a very large utilisation as solid wood or in wood based composite materials. Its qualities but also its defects as the dimensional instability, the susceptibility to biological attack, the anisotropy, are due to its complex structure. Research has demonstrated that the chemical modification of wood, meaning the involving of ...
M C Timar, M D Mihai, G Baciu
The use of C CP/MAS NMR in the chemical identification of decayed and undecayed, tropical timber species
1984 - IRG/WP 1224
13C CP/MAS NMR was found to be an extremely powerful tool for elucidating the chemical composition of Eucalyptus maculata, Pinus elliottii and Alstonia scholaris. The differences in lignin composition were different for each timber and discussed in relation to decay caused by soft-rot and white rot fungi. In particular the presence of syringyl and guaiacyl lignin types are discussed.
L E Leightley
Fipronil - le nouvel insecticide de Rhone Poulenc pour la preservation du bois
1995 - IRG/WP 95-30078
After the 3rd International Symposium in Cannes '95. More trial results and practical information on FIPRONIL, this new insecticide from Rhone Poulenc for Wood Preservation and PCO....
M G E J Van Maanen
Tolylfluanid - fungicide against blue stain in service
1992 - IRG/WP 92-3736
Physical and chemical properties and efficacy of Tolylfluanid are compared with the properties of Dichlofluanid. Whereas the difference in the molecular structure influences the physical properties significantly, the efficacy of both fungicides is comparable. The toxicological and ecotoxicological profile of Tolylfluanid is summarised....
H-U Buschhaus
Preventing fungal attack of freshly sawn lumber using cinnamon extracts
2007 - IRG/WP 07-30432
The potential for using cinnamon oil as an anti-mold and stain compound was investigated on ponderosa pine sapwood. Cinnamon oil was highly effective when used in ethanol, but its activity declined when it was mixed with only water. Attempts to enhance water solubility with surfactants improved solution stability, but had no apparent effect on biological activity. Further studies with other co-so...
Shujun Li, C Freitag, J J Morrell
The Chemical and Biological Properties of Polymeric Betaine
2009 - IRG/WP 09-30512
Didecyl polyoxyethyl ammonium borate (DPAB), also known as Polymeric Betaine, was developed as a co-biocide for chromium-free copper based wood preservatives in Europe in the 1980’s. DPAB as a wood preservative has been reported previously. This paper summarizes the chemical, physical, and biological properties of DPAB. ...
H Härtner, S Schmitt, Futong Cui, H M Barnes
Copper naphthenate-treated Southern Pine pole stubs in field exposure. -Part 2: Chemical characterization of full size pole stubs 12 years after treatment
2000 - IRG/WP 00-30246
This study examines the influence of pre-treatment and post-treatment steaming on the character and physio-chemical nature of copper naphthenate in hydrocarbon solvent treated pine in larger, pole diameter, pole stub-length samples. This work is the continuation of two projects that began almost a decade ago. Previous reports indicated that certain morphological changes might occur in small labora...
H M Barnes, D P Kamdem, M H Freeman
Termiticidal chemicals derived from tropical tree resins
1991 - IRG/WP 1477
To test the hypothesis that defensive chemicals protect tropical primary forest trees against biological attack, a bioassay and fractionation program was conducted in Indonesia. Fresh dipterocarp resins were fed in no-choice tests to Neotermes dalbergiae termites on 4.5 cm filter papers, or tested for inhibition of fungal growth. Fractionation of biologically active resins via flash column chromat...
A Messer, K McCormick, D Richardson, Sunjaya, H Hagedorn, J Meinwald
Chemical analysis of TnBTO in lap-joints
1999 - IRG/WP 99-20173
This research was performed as part of the EU project FACT (contract SMT4-CT96-2135) on field tests out of ground contact and ageing methods. The results reported here are part of the work on the experimental lap-joint standard (ENV 12037). TNO investigated the TBTO content of 32 lap-joints by analysing the tin content of 90 samples. The lap-joints were treated with two different TBTO-concentratio...
A Voss, P Esser, W L D Suitela
Biological degradation resistance of pine wood treated with dimethylol compounds
1989 - IRG/WP 3528
The study reports the increase of dimensional stability and biological degradation resistance of pine wood (Pinus sylvestris L) after impregnation with dimethyloldibydroxyethyleneurea. Decay resistance was determined according to BS 838:961. Nearly complete protection against Coniophora puteana, (Schum.ex Fr. Karst) weight loss of 2-3% was shown when modification, expressed as weight gain, exceede...
C L Videlov
Laboratory and field evaluation of Plasmite Reticulation System using bifenthrin as a chemical barrier within wall cavities against subterranean termites.
2005 - IRG/WP 05-20307
Laboratory and field bioassays undertaken to demonstrate Plasmite Reticulation system effectively delivers the termiticide (bifenthrin) within a simulated wall cavity at the required concentration. The chemical assay indicated that the amount of bifenthrin sampled at 5, 10, 15, 20, and 25m along the simulated reticulation system tested (30m) exceeded the manufacturer’s minimum recommendation of ...
J R J French, B M Ahmed, J Thorpe, A Anderson
Electronic noses for detection of rot in wood
1996 - IRG/WP 96-20098
In an ongoing project an electronic nose is being studied and developed for detection of volatile organic compounds (VOC) emitted from wood colonised and decayed by fungi. The electronic nose consists of an array of gas sensors with different selectivity patterns for different groups of volatile organic compounds (VOC). The use of pattern recognition routines implemented by artificial neural netwo...
K Nilsson
Decay resistance of high performance biocomposites based on chemically modified fibres
1998 - IRG/WP 98-40120
Different partners within the framework of a European research project produced high performance biocomposites aiming at the utilisation of board materials as durable products both in dimensional and biological degrading circumstances. This paper summarises test data, which indicate the potential of board materials produced with modified fibre material. The chemical modifications applied cover a r...
V Rijckaert, J Van Acker, M Stevens
Leaching of chromium and other cca components from wood-cement composites made with spent CCA treated wood
2000 - IRG/WP 00-50153
Wood cement composites are an attractive option for recycling spent treated wood, since the CCA treatment enhances the physical, mechanical and biological resistance properties of the composite. However, we have noted a higher than normal leaching of chromium from these products and this appears to result from conversion of some of the trivalent chromium to the more leachable and toxic hexavalent ...
D Qi, P A Cooper
Heat treated timber in Finland
2000 - IRG/WP 00-40158
Heat treatment permanently changes the physical and chemical properties of wood by means of high temperatures (150 - 240°C). Heat treatment darkens the colour of the wood. Heat treatment improves the equilibrium moisture content of the wood and the shrinkage and swelling of the wood is reduced. Very high temperatures improve the resistance to rot and also reduce the susceptibility to fungal decay...
T Syrjänen, E Kangas
An experimental method to simulate incipient decay of wood by basidiomycete fungi
2000 - IRG/WP 00-20200
At very early stages of decay of wood by basidiomycete fungi, strength loss can be measured from wood before any measurable weight loss. Therefore, strength loss is a more efficient measure of incipient decay than weight loss. However, common standard decay tests (e.g. EN 113 or ASTM D2017) use weight loss as the measure of decay. A method was developed that allowed progressive removal of samples ...
S F Curling, J E Winandy, C A Clausen
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell