Physical and biological properties of albizzia waferboards modified with cross-linking agents
1995 - IRG/WP 95-40043
Chemically-modified low-density waferboards with cross-linking agents were produced using a fast-growing species of hardwood albizzia (Paraserienthes falcata Becker) as a raw materials and isocyanate resin as a glue adhesive. For the chemical modification, the vapor-phase formalization of the boards and the pad-dry-cure treatment of wafers with cross-linking agents were employed. The vapor-phase f...
S Yusuf, Y Imamura, M Takahashi, K Minato
Biological resistance of phenol-resin treated wood
1990 - IRG/WP 3602
Biological resistance of PF (phenol formaldehyde resin) - treated wood has been tested in relation to the resin properties, wood species and biological factors. When tested using water-soluble PF (mol. wt. 170), ca. 10% RI (resin impregnation) was enough to suppress the decay of Japanese cedar (Cryptomeria japonica) and western hemlock (Tsuga heterophylla) blocks exposed to Tyromyces palustris (br...
M Takahashi, Y Imamura
Natural durability of wood in ground contact - A correlation between field and laboratory tests
1985 - IRG/WP 2182
A field test is being carried out to evaluate the natural durability of 20 hardwoods. The resistance to decay and termite attack was evaluated in accelerated laboratory tests. The results of the field test after 6 years and 8 months indicate that there is not necessarily agreement between results from laboratory and field tests. It is pointed out that apart from the artificiality of the laboratory...
M S Cavalcante, G A C Lopez, R G Montagna, M E S Fosco Mucci
Incorporation of phenyl boronic acid treatment with vapor phase formalization
1997 - IRG/WP 97-40083
Phenylboronic acid (PBA) treatment was incorporated with vapor phase formalization (VPF) in order to increase dimensional stability and boron fixation as well as enhancement of biological resistance. Five and ten hours VPF were applied after PBA treatment as 0.34, 0.50, 1.00 and 2.00% concs. aqueous solutions. Anti swelling efficiency (ASE) attended to 71% in specimens impregnated with 0.50% PBA s...
M K Yalinkilic, S Yusuf, T Yoshimura, W-Y Su, K Tsunoda, M Takahashi
Termite and decay resistance of particleboard composed of white cypress pine and radiata pine
1997 - IRG/WP 97-10200
Phenol-formaldehyde bonded particleboard was manufactured from blends of non-durable radiate pine (P. radiate) and heartwood of the naturally durable species, white cypress pine (C. glaucophylla). Board specimens were subjected to bioassays using two termite species, M. darwiniensis and C. acinaciformis, and the basidiomycete fungi, C. puteana and P. ostreatus, and the durability of specimens was ...
P D Evans, J W Creffield, J S G Conroy, S C Barry
Leaching characteristics, decay and termite resistance of treated wood with boron compounds, N'-N-(1,8-Naphthalyl) hydroxylamine (NHA-Na), and hydroxynaphthalimide (NHA-H)
2003 - IRG/WP 03-30307
Despite many advantages of boron wood preservatives, boron itself does not adequately protect wood in ground contact and exterior applications because its natural diffusibility and susceptibility to leaching. As a result of previous studies to limit or decrease boron leaching, several fixation systems have been developed. In this study, we evaluated the effects of N'-N-(1, 8-Naphthalyl) h...
S N Kartal, Y Imamura
Decay and termite durabilities of heat-treated wood
2004 - IRG/WP 04-40272
Decay and termite resistances of Plato-treated timbers were evaluated using a modified JIS decay test method, feeding test in a laboratory scale and a field exposure against Reticulitermes speratus (Kolbe) or Coptotermes formosanus Shiraki. The results showed that no significant decay durability of the
treated timbers although mass loss from decay slightly decreased in case of treated timbers. ...
S Doi, K Hanataa, E Kamonji, Yuuji Miyazaki
Resistance of wood inorganic material composites against decay fungi and subterranean termites
1996 - IRG/WP 96-40062
Double diffusion process was applied to the treatment of small sound sapwood specimens [20(T) x 20(R) x 10(L) mm³] of Cryptomeria japonica D. Don. The specimens were consecutively dipped in the two kinds of acqueous solutions to form water insoluble deposits within the wood after an expected reaction between the solutes. Following the comparison of deposits formed and treating conditions (tempera...
K Tsunoda, T Yoshimura, M Takahashi, S Hirao, H Usui
Properties-enhanced albizzia particleboards by incorporating fungicide and insecticide in the glue
1994 - IRG/WP 94-30060
Preservative-treated particleboards were prepared by using tropical fast-growing albizzia and adding fungicides and insecticides to the adhesive-glue. the physical and biological properties of these boards were evaluated. No significant reduction in bending or internal-bond strength due to incorporation of the chemicals was detected. Treated particleboards effectively resisted attack by Coptoterme...
B Subiyanto, S Yusuf, Y Imamura, S Fushiki, T Saito, T Katuzawa
Decay and termite resistance of wood treated with boron-containing quaternary ammonia compound, didecyl dimethyl ammonium tetrafluoroborate (DBF) incorporated with acryl-silicon type resin
2004 - IRG/WP 04-30334
This study evaluates the decay and termite resistance of surface-treated wood with didecyl dimethyl ammonium tetrafluoroborate (DBF) incorporated with acryl-silicon type resin emulsion. DBF is a quaternary ammonia compound and contains boric tetrafluoride (BF4-) as a counter ion in its chemical structure. In the study, DBF was incorporated with an acryl-silicon type resin to increase water-resista...
S N Kartal, W J Hwang, K Shinoda, Y Imamura
Mobility of zinc borate wood composite preservative
1997 - IRG/WP 97-30153
Zinc borate (ZB) is being used as an antifungal and insecticidal wood preservative for flake/strand-based composites. Data is reported on the laboratory and field leaching behavior of ZB when contained in apen flake composites. In general, the performance results correlate with leaching hazard. Although the boron in ZB is more resistant to depletion than in sodium borates, the ZB boron will deplet...
P E Laks, M J Manning
Preservative treatment of wood-based composites with a mixture formulation of IPBC-silafluofen using supercritical carbon dioxide as a carrier gas
2003 - IRG/WP 03-40251
Wood-based composites treated with a mixture formulation of a fungicide, 3-iodo-2-propynyl butylcarbamate (IPBC) and a termiticide, silafluofen using supercritical carbon dioxide (SC-CO2) as a carrier solvent were tested for their resistance to decay and termite attack in the laboratory. The treatment solution was prepared by mixing both biocides (IPBC 10 + silafluofen 1) with a co-solvent, ethano...
K Tsunoda, M Muin
Resistance of two commercial cement-bonded rubberwood particle composites to decay and termites
2000 - IRG/WP 00-10338
Two types of cement-bonded rubberwood (Hevea brasiliensis) particle composites (tradenames: Cemboard and Primaflex in Malaysia), were evaluated for termite resistance (prevalent termite: Coptotermes curvignathus) in the field, and decay resistance (test white rot fungi: Schizophyllum commune and Pycnoporus sanguineus; test brown rot fungus: Gloeophyllum trabeum; test soft rot fungi: Phialophora fa...
A A H Wong
Preservation of wood composites with zinc borate
1995 - IRG/WP 95-30074
Inorganic borates such as boric acid, borax, disodium octaborate tetrahydrate, and zinc borate can be incorporated into wood composites such as waferboard to impart decay and insect resistance to the final product. Zinc borate is especially well suited for this application due to its efficacy and leach resistance. The paper summarizes the work performed to date in this area. The effects on strengt...
P E Laks, M J Manning
Biological resistances of wood-metaborate composites using the borax solution system
2001 - IRG/WP 01-30259
Combinations of wood and metaborate composite were prepared from sapwood specimens of Japanese cedar (Cryptomeria japonica) and the borax and metallic salts system using the diffusion-penetrated process. Wood-metaborate composites were produced as follows: water-saturated specimens were first impregnated by a saturated borax solution and then diffuse-penetrated with Zn2+, Ca2+, or Pb2+ solution. B...
Liang Lin, T Furuno
Biological degradation resistance of wood acetylated with thioacetic acid
1983 - IRG/WP 3223
Chemically, modification of wood is being considered as an alternative to conventional preservation by toxic chemicals. Acetylated wood has been reported to be quite resistant to most biodegrading organisms at weight percent gains (WPG) around 15-19. The conventional acetylation techniques with acethic anhyrdride result in generation of acetic acid. However, acetylation with thioacetic acid overco...
S Kumar, S C Agarwal
Durability of Sugi (Cryptomeria japonica D.DoN ) wood treated in high temperature liquid paraffin
2002 - IRG/WP 02-40221
Sugi(Cryptomeria japonica D.DoN )wood was subject to a heat treatment in high-temperature liquid paraffin for the purpose of improving the resistance against fungi and termites without chemicals. The bath of paraffin liquid, which can provide a uniform heat transfer (±2?), was used at temperatures of 90?,120?and 150?.?ecay resistance according to JIS K 15711) was evaluated using a brown rot fungu...
Y Matsuoka, W Ohmura, S Fujiwara, Y Kanagawa
Resistance of DMDHEU-treated pine wood against termite and fungi attack in field testing according to EN 252. Results after 30 months
2006 - IRG/WP 06-40354
The aim of this study was to determine the effectiveness against decay and termite attack of pine sapwood treated with pure and modified DMDHEU in a field test according to European Standard EN 252. Some of the treatments tested were able to increase, within the period of the test reported (30 months), the resistance of the wood both to micro-organisms and termites. The curing process seems to be ...
S Schaffert, L Nunes, A Krause, H Militz
Evaluatiang the potency of cinnamaldehyde as a natural wood preservatives
2007 - IRG/WP 07-30444
Since cinnamaldehyde, the major constituent of leaf essential oil from Cinnamomum osmophloeum, has significant antifungal and antitermitic activities, it is worthy of understanding whether cinnamaldehyde has potential to be used as a natural preservative for improving the durability of wood. In this study, the fungi and termite resistance of cinnamaldehyde-treated wood (CTW) were evaluated accordi...
Chun-Ya Lin, Chi-Lin Wu, Shang-Tzen Chang
Developments in Borate Treatment of Canadian Species for Decay and Termite Resistance
2007 - IRG/WP 07-30443
The increased interest in boron treatment of wood over the past 20 years is mainly due to its environmental acceptability, potentially deep penetration in wood, and its efficacy against decay and termites. Based on Forintek’s research in the past two decades, the boron penetration and retention requirements for decay and termite protection in various national and international standards for Cana...
Jieying Wang, P Morris, S McFarling, T Byrne
Utilizing Cypress to improve the decay and termite resistance of OSB panels
2008 - IRG/WP 08-10658
OSB panels were manufactured with mixture of pine and cypress heartwood and lignin and tannin based resins in order to propose an eco-friendly wood composite. The resistance of OSB panels was tested against Reticulitermes santonensis according to the EN 118 and EN 117 standards and field tests methods. OSB made from cypress showed more resistance against the tested termite, the resistance decrease...
N Amusant, O Arnould, A Depres, R H Mansouris, T Pizzi, C Baudassé
Preliminary investigation of biological resistance, water absorption and swelling of thermally compressed pine wood panels
2008 - IRG/WP 08-40396
Wood can be modified by compressive, thermal and chemical treatments. Compression of wood under thermal conditions is resulted in densification of wood. This study evaluated decay and termite resistance of thermally compressed pine wood panels at either 5 or 7 MPa and at either 120 or 150?C for one hour. The process caused increases in density and decreases in thickness of the panels; however, lab...
Ö Ünsal, S N Kartal, Z Candan, R Arango, C A Clausen, F Green III
Leaching performance, decay and termite resistance of wood treated with boron compounds incorporated with phenol-formaldehyde resin
2009 - IRG/WP 09-30503
A resol-type phenol-formaldehyde (PF) resin was synthesized and designed to penetrate wood incorporated with boron compounds in order to immobilize boron in wood. The leaching performance, decay and termite resistance of treated wood was investigated. Three kinds of boron compounds, that is, boric acid (BA), borax (BX) and disodium octaborate tetrahydrate (DOT), were selected to mix with PF and tw...
Liping Yu, Jinzhen Cao
Biological performance of wood treated with tar-oil recovered during slow pyrolysis of macadamia nut shells
2010 - IRG/WP 10-30523
This study evaluated decay and termite resistance of wood treated with tar oil obtained from a commercial pyrolysis process of macadamia nut shells. Vacuum-treated pine wood specimens were subjected to various brown and white rot fungi based on the soil-block test method specified by the American Wood Protection Association (AWPA) after leaching process. Treated specimens were also subjected to th...
S Nami Kartal, E Terzi, C Kose, J Hofmeyr, Y Imamura
Decay and termite resistance of particleboard and MDF panels made from pinecones
2010 - IRG/WP 10-40493
Particleboard and medium density fiberboard (MDF) panels were produced by using pinecone from stone pine (Pinus pinea L.) tress and wood particles from pine and beech wood at various ratios. Specimens from the panels were subjected to slightly modified soil-block tests according to AWPA E10-06 standard method by using two brown-rot fungi, Gloeophyllum trabeum and Postia placenta and two white rot ...
C Köse, E Terzi, Ü Büyüksar, Erkan Avcı, Nadir Ayrılmış, S Nami Kartal, Y Imamura