Efficacy of anhydrides as wood protection chemicals - II. Performance against soft rot fungi
1998 - IRG/WP 98-30174
Pine sapwood modified with various anhydrides and with butyl isocyanate was tested for its resistance to soft rot decay. Small stakes were exposed for 20 months in unsterile soil in a fungal cellar test.
Wood modified with butyl isocyanate performed better than any of the anhydrides tested, with a threshold level of protection (less than 3% weight loss) at 12% weight percent gain (WPG). Stakes ac...
S C Forster, M D C Hale, G R Williams
Are fungal cellar tests really necessary?
1989 - IRG/WP 2333
During the past decade the range of methodology used to evaluate wood preservative potential has significantly expanded. At the forefront of these new tools available to the scientist·is the fungal cellar. This technique, as currently applied, involves the exposure of treated and untreated samples to conditions of moisture and temperature which ensure optimum fungal attack. By comparison data wit...
J N R Ruddick
Biological performance of gypsum products containing borates
2000 - IRG/WP 00-30237
At suitable retentions borates have biostatic properties enabling them to be used for biodeterioration control in wood. They provide protection against decay fungi, mould, and termites, which are known to also attack gypsum products. Currently, many gypsum products contain added borates, which are used to improve physical and processing characteristics. Work examining the effect of borates at cont...
J L Fogel, J D Lloyd
Report of the meeting of the refractory timbers sub-group, Lappeenranta, Finland on 25 May 1989
1989 - IRG/WP 3561
The first meeting of this sub-group took place on Thursday 25 May and considered the following agenda: 1) Papers presented to the meeting "Performance of treated spruce in Canadian field test sites" by J.P.Hösli and E.E.Doyle, IRG/WP/3506 and "Performance of CCA treated spruce and pine in unsterilized soil" by A.J.Nurmi. 2) Future work areas for the sub-group 3) Membership of the sub-group 4) Cir...
R J Murphy
Absorption of inorganic salts solutions. Retentions of inorganic salts. Fire retardants
1990 - IRG/WP 3625
The study aims evaluated the impregnation capacity using fire retardants on woods with differents densities. At the same time, impregnation with several fire retardant salts were carried out in order to obtain their absortion and retention in wood....
A Garcia, J Navarro
Biological agents of timber degradation in Portugal. Marine borers
1991 - IRG/WP 4171
A brief report of the studies carried out in Portugal on marine borers is presented. The marine borers found in the portuguese coast are refered as well as the wood species where those organisms were identified. Emphasis is given to a study carried out from 1960 to 1975 at the Tagus estuary in Lisbon with the purpose, among others, of establishing the natural durability of different timbers....
J S Machado, L Nunes
Above ground performance of CCA-treated fingerjointed lumbe
1993 - IRG/WP 93-40003
Studs made from short lengths by finger jointing are becoming more commonly used in North America. Recently Forintek has received enquiries about the performance of such material in a treated form. Treated and untreated nominal 2x4 inch² spruce-pine-fir (SPF) studs exposed above ground for 12 years in southwestern British Columbia were evaluated for evidence of decay. Despite shallow preservative...
P I Morris, G E Troughton
Fire resistance of Alder wood treated with some chemicals.
Part II. Effect of Other Chemicals on the Combustion Properties
2002 - IRG/WP 02-40235
Samples from alder wood (Alnus glutinosa (L.) Gaertn. subsp. barbata (C.A.Mey) Yalt.) were impregnated according to ASTM D 1413-88 with boron compounds (boric acid, borax,
sodium perborate), vinyl monomers (styrene, methyl methacrylate), Tanalith-CBC, Phosphoric acid, Vacsol, Immersol, Polyethylene glycole (PEG-400) and their mixed solutions of chemicals in order to determine their combustion pro...
A Temiz, Ü C Yildiz
Performance of surface-treated hardwoods and softwoods out of ground contact
1990 - IRG/WP 3592
A number of fungicides were tested as brush treatments for protection of southern pine, Douglas-fir, maple, and red oak against decay above ground. Cross-brace and L-joint test units were treated just before assembly and exposed from 3-10 years. Untreated Douglas-fir cross-brace units were not decayed at either the Mississippi or Madison, WI, site. Untreated red oak cross-brace units were not deca...
T L Highley
Co-operative research project on L-joint testing. Progress report to March 1988
1988 - IRG/WP 2315
Further sets of data received from CTFT (France), BAM (Germany) and PRL (UK) after 46-48 months exposure and STU (Sweden) after 22 months exposure are presented and discussed in conjunction with data reported previously. Colonisation and attack of the L-joints has progressed with increasing exposure period. The new data are generally in agreement with those presented previously and the major diffe...
J K Carey, A F Bravery
Quantitative assessment of field specimens. A proposal for discussion
1980 - IRG/WP 2143
H Friis-Hansen
The performance of softwood species used as poles in Queensland
1985 - IRG/WP 1253
In Queensland, the conifer Pinus elliottii could provide material suitable for use as poles. Full size pole material has been readily treated with CCA with no significant loss in strength. Seasoning of logs prior to treatment requires particular attention in the wet tropical and sub-tropical regions of Queensland. Experimental and in service field tests have indicated excellent performance of CCA ...
L E Leightley
Bibliography: Interactions of wood preservatives with wood, metals, glues, paints and concretes
1983 - IRG/WP 3271
H Becker
Co-operative Field Experiment: Performance of preservative-treated timber: Report on condition of specimens after seven years installed in New South Wales - Australia
1986 - IRG/WP 3362
R S Johnstone
The performance of glue laminated railway ties after 40 years of service in the main line track
1989 - IRG/WP 2325
Two series of horizontally glue laminated ties made of a softwood body and topped with a hardwood lamination were creosoted and installed in 1947 in a tangent and a curved main line track. The tests are now 40 years old and the excellent condition of the ties of these two series suggest that a service life of 50-60 years can be expected....
J P Hösli, E E Doyle, C P Bird, T Lee
Comparative performance of pentachlorophenol and copper naphthenate in a long term field stake test
2000 - IRG/WP 00-30243
In this study the performance of copper naphthenate (Cu-Nap) and pentachlorophenol (Penta) treated pine stakes against decay and termite attack were compared at two test sites in Mississippi. Four different petroleum oils meeting AWPA Standard P9-A were used as carriers for these wood preservatives. After ten years exposure, the efficacy of Cu-Nap at a retention level of 0.05 pcf Cu was equivalent...
D D Nicholas, M H Freeman
Short term preconditioning of preservative-treated wood in soil contact in relation to performance in field trials
2000 - IRG/WP 00-20185
The effect of pre-exposure to primary colonising micro-organisms on preservative-treated wood, prior to a basidiomycete decay test, was determined by preconditioning in two soil types. Scots pine EN 113 blocks treated with 3 model systems (a triazole, a copper quaternary compound and a copper boron triazole) were leached according to EN 84 and subjected to 6 weeks and 8 weeks burial in either John...
S Molnar, D J Dickinson
Long-term performance of a "wax" type additive for use with water-borne pressure preservative treatments
2000 - IRG/WP 00-40159
Field performance results are updated for matched CCA treated decking boards with and without an emulsion water repellent additive incorporated with the initial pressure treatment. Decks have been exposured for over 9 years in Harrisburg, NC. Boards were evaluated for in-service and laboratory performance for water repellent efficacy, as well as additive loadings in the boards after this exposure....
A R Zahora
The leachability, biological resistance, and mechanical properties of wood (Pinus sylvestris L.) treated with CCA and CCB preservatives
1999 - IRG/WP 99-30207
Scots pine (Pinus sylvestris L.) specimens treated with CCA and CCB preservative solutions (1.0%) were subjected to several fixation processes and leached elements from the specimens were determined. In addition, the specimens exposed to different fixation temperatures were subjected to soil-block test using two brown-rot fungi and one white-rot fungus in order to investigate the effects of fixati...
S N Kartal
Wood preservation in China
1989 - IRG/WP 3546
Huiming Zhou, Zhongwei Jin
Performance of CCA treated Eucalyptus round ties
1985 - IRG/WP 3342
After 5.5 years of field exposure in the south of Brazil round Eucalyptus ties treated with CCA type A Oxide (OSMOSE K-33-A) preservative with retentions from 12 to 14 kg/m³ (0.75 to 0.873 PCF) (active ingredient basis) are performing very well. No decay or insect attack was observed in the 100 ties in test in real conditions of use; 10% of ties show incipient checking (what is a natural trend of...
V J Carlos, F R Niederauer, J P P Wehr
36 years of wood preservative tests in Tanzania
1992 - IRG/WP 92-3731
The performanee of major wood presevatives which are used widely commereially are given. These include creosote, CCA's and 5% Pentachlorophenol dissolved in heavy industrial diesel. Tests are conducted at three ecologically different using pine stakes. Results show that the striking performance of creosote and CCA's is noticeable at above 128 kg/m³ and 16 kg/m³ respectively....
K K Murira, P F Nangawe
Oxygen index levels and thermal analysis of wood treated with melamine-formaldehyde-boron combinations
1997 - IRG/WP 97-30135
Melamine formaldehyde (MF) resin was impregnated into scots pine (Pinus sylvestris L.) specimens with aqueous solutions of 5, 10 and 20% concs. Boric acid (BA) and borax (BX) was added to MF resin at the concentration levels of 0.25, 1.00 and 4.70% to each level of resin concs. BA and BX mixture was prepared at the 5:1 (w/w) ratio considering resultant pH of solutions and better fire resistance. U...
M K Yalinkilic, W-Y Su, Z Demirci, E Baysal, M Takahashi, S Ishihara
The performance of wood preservatives in soil-bed soft rot tests
1993 - IRG/WP 93-20007
Testing the efficacy of wood preservatives in soil is recognised as a fundamental part of the assessment of long-term wood protection in ground contact. Laboratory based tests can provide a hazardous environment in which a preservative can be challenged by a range of micro-organisms. This paper presents the results of tests carried out to investigate the performance of wood preservatives in a wet ...
G R Williams, S Caswell
Decay resistance of resin treated wood
1999 - IRG/WP 99-30206
Selected natural resin systems were evaluated for their potential as wood protecting agents according to standard test procedures. As indicated by the European standard EN 599 both a Basidiomycete test according to EN 113 and a ENV 807 soil bed test were carried out. Six resin treatments were tested using 3 concentration or treatment levels. Using the biocidal activity criteria as usually applied ...
J Van Acker, A J Nurmi, S M Gray, H Militz, C Hill, H Kokko, A O Rapp