A natural exposure weathering test for the evaluation of preservative performance
1992 - IRG/WP 92-2400
Natural exposure weathering tests were carried out by externally exposing treated wood samples for varying periodes of time up to 36 months. In the laboratory these samples were assayed for residual preservative effeciveness using Coniophora puteana FPRL 11E. The results indicated a loss in efficacy over and above that determined using artificial ageing procedures such as EN73 (evaporative ageing)...
J Brown, G R Williams
Performance of chromated copper arsenate-treated aspen fence posts installed in Forintek's Eastern test plot from 1951 to 1963
1984 - IRG/WP 3272
Aspen poplar fence posts were pressure treated by the full cell process using three formulations of copper chrome arsenate wood preservative. A total of one hundred and fifty nine of the posts were installed in service in Forintek's Chalk River post plot from 1951 to 1962. During the 1982 general inspection of the post plot all 159 posts were still in service. A groundline inspection was ...
C D Ralph
Patterns of long-term performance - How well are they predicted from accelerated tests and should evaluations consider parameters other than averages?
1998 - IRG/WP 98-20130
This paper is a discussion of whether different service-life distribution patterns of products treated with unlike preservatives can be predicted, modeled, characterized, or even anticipated from accelerated laboratory tests. Graphic displays of data from Forest Products Laboratory field plots with preservative-treated and fire-retardant-treated stakes demonstrate the importance of local environme...
R C De Groot, J W Evans
Decay resistance of high performance biocomposites based on chemically modified fibres
1998 - IRG/WP 98-40120
Different partners within the framework of a European research project produced high performance biocomposites aiming at the utilisation of board materials as durable products both in dimensional and biological degrading circumstances. This paper summarises test data, which indicate the potential of board materials produced with modified fibre material. The chemical modifications applied cover a r...
V Rijckaert, J Van Acker, M Stevens
Performance of treated and untreated sawn fence posts of Scots pine and Norway spruce
2000 - IRG/WP 00-30247
Sawn fence posts are a rather important product and the objective of this trial was to assess their durability. In 1985 a field trial with treated and untreated fence posts of Scots pine (Pinus sylvestris L.) and Norway spruce (Picea abies (L.) Karst.) was set out at the test field in Ultuna, Uppsala, Sweden. The posts had a dimension of 75 x 100 x 1400 mm3. The preservatives applied were a CCA, a...
Ö Bergman
The effect of treatment temperature on the biological performance of CCA treated wood
1990 - IRG/WP 3624
Birch and Scots pine sapwood blocks were treated with several concentrations of CCA at three different temperatures: 5, 20 and 35°C. The treated wood was maintained at the appropriate temperature for the fixation period. Leached and unleached samples were then exposed in a soft rot monoculture test using Chaetomium globosum and a brown rot monoculture test using Coniophora puteana. The treatment ...
S M Gray
Marine performance of preservative treated Southern pine panels. Part 2: Exposure at Mourilyan Harbour, Queensland, Australia
2000 - IRG/WP 00-10337
Southern yellow pine panels treated with ACQ type B, ACQ type A, CCA type C, creosote, and copper naphthenate have been exposed at Mourilyan Harbour, north Queensland, Australia for almost 6 years. These panels have been inspected and rated for fouling and attack by Teredinid, Limnoria, Martesia, and Sphaeroma during this exposure. After 70 months exposure, overall performance of ACQ type B was eq...
A R Zahora, A F Preston, K J Archer, S Kleinschmidt
Test Methods – Performance Based Requirements
2004 - IRG/WP 04-20297
In this paper is briefly described the present approach to service life prediction as an essential part of the architectural engineering process. The system of testing the durability of wood is described more in detail including laboratory tests as well as field trials. It is concluded that the system has a lot of weaknesses which makes it less well suited for practical building applications. A le...
M-L Edlund, F Englund, J Jermer, T Nilsson, M Westin, K Ödeen
Influence of a dipping preservative treatment on the performance of wood finished with waterborne coatings
1998 - IRG/WP 98-40121
Within a larger European research project on the performance of joinery finished with waterborne coatings, the influence of a water based dipping preservative treatment was studied in several ways. Six different waterborne coatings were tested with and without a preservative underneath the coating. The performance was tested on pine sapwood and spruce panels in a 2-year outdoor weathering trial on...
M De Meijer, J Creemers, W Cobben, P Ahola
Stability and performance of tributyltin compounds
1984 - IRG/WP 3275
Based on the critical examinations of the disputable permanence of tributyltin compounds in wood, this paper deals with a number of examinations of the relative evaporation, thermal stability and oxidation stability of some TBT-compounds. While thermal and oxidative stability is high for all TBT-species, the relative evaporation at elevated temperature is highly variable, and lowest for the TBT-es...
F Imsgard, B Jensen, H A B Landsiedel, H Plum
Long term performance of CCA preservatives in ground contact
2000 - IRG/WP 00-30223
Copper-chrome-arsenate (CCA) preservatives have been use extensively in New Zealand since the mid-1950s for a wide range of ground contact uses, radiata pine being the main species treated. They have been the subject of a comprehensive field testing programme in up to five sites in New Zealand, the earliest tests being established in 1955. Main factors affecting performance have been formulation t...
M E Hedley, D R Page, B E Patterson
Preservative performance of copper naphthenate (SANPRESER-OGR) in brush treatment of timber
1991 - IRG/WP 3663
Preservative efficacy of copper naphthenate (SANPRESER-OGR) was evaluated in the laboartory and field trials when timber was treated by brushing. Results of field trial indicated that service life of the brush-treated timber could be approximately 10 years or longer under ground contact conditions, although life span was slightly varied with timber species and test sites. After four years&apos...
Y Sugai, K Hamada, M Kitada, K Tomoi
Relative performances of DNBP and CCA wood preservatives in accelerated decay tests
1988 - IRG/WP 3496
The effectiveness of 2-sec-butyl-4,6-dinitrophenol (DNBP) was compared with that of CCA. Test blocks of Pinus patula and Eucalyptus grandis were impregnated to precisely known retentions of approximately 3, 6, and 10 kg/m³ CCA and solvent-borne DNBP respectively. They were then challenged in decay tests comprising soil burial and exposure to monocultures of Chaetomium globosum, Coriolus versicolo...
W H Schnippenkoetter, L D Abraham, A A W Baecker
Development of an Australasian protocol for assessment of wood preservatives
1994 - IRG/WP 94-20043
The Australasian Wood Preservation Committee (AWPC) is currently developing a suite of assessment procedures (protocols) for the biocidal efficacy of wood preservatives for approval in Australasia (Australia, New Zealand, Papua New Guinea, Fiji). Protocols are being prepared for the six hazard levels recognised in the relevant standards of member countries and represent the minimum procedures requ...
W D Gardner, H Greaves, M E Hedley, K J McCarthy, J Norton
The performance of water repellants on radiata pine exposed to the weather
1989 - IRG/WP 3553
The effectiveness and resistance to weathering of four water repellent treatments, a commercial timber stain, and an oil-based clear finish, was assessed using 20x20x6 mm³ samples of untreated, copper-chrome-arsenic (CCA)-treated, and tributyltin oxide (TBTO)-treated radiata pine exposed to the weather over a four month period. The water repellency of each preservative/water repellent combination...
D V Plackett, F M Cameron
The performance of CCA treatment in bamboo against decay fungi
1993 - IRG/WP 93-30027
Samples of culm wall material from young (< 6 month age) and mature (> 3 years age) culms of the bamboo, Phyllostachys virideglaucescens were treated to equivalent% w/w retentions of a CCA preservative. After fixation and leaching the treated samples were exposed to decay by Chaetomium globosum FPRL S70K, Coriolus versicolor FPRL 28A and Coniophora puteana FPRL 11E. Thin section samples of u...
O Sulaiman, R J Murphy
A Soil Bed Test of the Effect of CCA Penetration on the Performance of Hem-fir Plywood
2004 - IRG/WP 04-30332
An accelerated decay test was set up to compare the performance of CCA-treated Western hemlock/amabilis fir plywood treated to meet the preserved wood foundation (PWF) retention standard with various patterns of preservative penetration. Short lengths of treated plywood and comparable untreated material were installed in a soil bed. After eleven years of exposure, the CCA treatments were all sou...
P I Morris, J K Ingram
Assessing the performance of wood preservatives from biological tests - the European approach
1994 - IRG/WP 94-20040
The impetus for the European Standardisation Committee to undertake the development of a performance standard for characterising the effectiveness of wood preservatives from biological tests, lies in the Construction Products Directive. This is effectively the European Community law which provides the basis for Construction Products to be traded across all member states without technical or regula...
A F Bravery
Effect of treatment process on performance of copper-chrome-arsenate. Part 2: Field stake tests
1995 - IRG/WP 95-40046
Pinus radiata sapwood stakes 20 x 20 x 400 mm³ were treated with CCA Type C using a range of concentrations and three treatment processes; Bethell, Lowry and Rueping. Preservative retention was determined by chemical analysis of treated material. Following fixation stakes were installed in a randomised plot in the Whaka graveyard located on the FRI campus. Stakes were inspected at yearly interval...
M E Hedley, J Anderson, J B Foster, B E Patterson
Calculation of preformance index of Bardac 20 (an alkylammonium compound) evaluated in a field stake test
1982 - IRG/WP 3206
Bardac 20 treated stakes have been in test for three years at the Westham Island test site near Vancouver, B.C. The Performance Index for the preservative was calculated and found to be 0.009 which infers that, at the standard retention, Bardac 20 added 0.9 y to the life of the stake. It may be concluded that when tested using a standard field stake test using ponderosa pine (Pinus ponderosa Laws)...
J N R Ruddick
The possible significance of the lignin content and lignin type on the performance of CCA-treated timber in ground contact
1988 - IRG/WP 1357
The lignin in wood samples of Alstonia scholaris, Octomeles sumatrana and a Simaruba species have been analysed. These timbers are characterised by a high lignin content and low syringyl:guaiacyl ratios. Decay tests with two soft rot fungi showed that the timbers were less susceptible than timbers with a low lignin content and higher syringyl:guaiacyl ratios. Numerous data for field performance of...
T Nilsson, J R Obst, G F Daniel
Co-operative research project on L-joint testing. Progress report to March 1984
1984 - IRG/WP 2211
Each participant was intended to expose L-joints in the main trial on 1 April 1983 and the first sampling, after 8 months exposure, was to be undertaken on 1 December 1983. Some participants have had to vary this schedule. Results are presented from CTFT (France) and PRL (United Kingdom). These show a greater effectiveness by the double vacuum treatments compared with the 1 minute dip treatments. ...
J K Carey, A F Bravery
Performance of copper-based wood preservatives in above ground and ground contact tests
1994 - IRG/WP 94-30057
The relative performance of a range of copper-based wood preservatives was compared using above ground and ground contact procedures. The data, accumulated after several years' testing, show that on an equivalent active ingredient basis, differences in performance of the preservative systems tested can vary quite markedly. The contribution of co-biocides to the overall performance of thes...
A F Preston, K J Archer, L Jin, W Metzner, D Seepe
Fungus cellar testing as an evaluation method for performance of treated timber in ground contact
2001 - IRG/WP 01-20227
A fungus cellar method for the accelerated evaluation of performance of treated wood in ground contact is described. The test soil comprised of sandy loam, vermiculite and Japanese horticulture soil "Kanumatsuchi" in a ratio of 6:2:2 by volume. The soil was inoculated with the dominant test fungus isolated with selective medium from decayed wood samples. Pairs of treated and untreated wood specime...
Y Nagano
Serviceability of copper naphthenate-treated poles
2000 - IRG/WP 00-30214
Copper naphthenate-treated poles in service were inspected for deterioration, penetration, retention, and serviceability. The study to date has included poles in all hazard zones in the United States. Poles installed by 12 different utilities and eight different treating companies are included in the survey. Both southern pine and Douglas-fir poles and distribution and transmission poles are inclu...
H M Barnes, M H Freeman, J A Brient, C N Kerr Jr