Decay resistance of a commercial pistachio twig-plastic composite
2011 - IRG/WP 11-40553
In this research, the decay resistance of commercial extruded pistachio twig flour-plastic composite was investigated against the white-rot fungi Trametes versicolor and the brown-rot fungus Coniophora puteana. The composite specimens containing 60% pistachio twig flour were exposed to a decay test according to modified ASTM standard for 3 months. The results showed that the composite could be d...
M R M Farahani, M Safarzadeh
Use of Variable Pressure Scanning Electron Microscopy for in situ Observation of Degradation of Wood Surfaces during Artificial Weathering
2012 - IRG/WP 12-20489
Variable pressure scanning electron microscopy (VPSEM) is capable of observing electrically non-conductive materials like wood without the need to render the surface conductive by applying a coating of gold, platinum or carbon. Hence, there is the possibility that VPSEM could be used to non-destructively follow the structural changes occurring at wood surfaces during weathering, because specimens ...
F Hatae, Y Kataoka, M Kiguchi, H Matsunaga, J Matsumura
Accessibility of Wood Cell Walls to Well-defined Platinum Nanoparticles
2012 - IRG/WP 12-20494
Copper nanoparticles are found in the walls of parenchyma cells in southern pine sapwood treated with a micronised wood preservative, but they are absent from tracheid walls. Hence, we hypothesized that small nanoparticles can penetrate the walls of unlignified parenchyma cells, but are excluded from lignified tracheid walls. This paper tests this hypothesis by treating pine sapwood with an aqueou...
H Matsunaga, Y Kataoka, M Kiguchi, P D Evans
Preliminary evaluation of degradation patterns in wood samples from the Yenikapı shipwrecks
2013 - IRG/WP 13-10798
The uncovering of several shipwrecks during the excavation of the Marmaray Rail Tube Tunnel Project in Istanbul provides an important opportunity to evaluate waterlogged woods buried for centuries. Identification of these woods showed that a variety of species was used in the ships. One shipwreck (a galley) from the Yenikapı Marmaray was examined using electron microscopy. The micrographs rev...
C Köse, A M Taylor
Scanning Transmission X-ray Microscopy as a tool for examining chemical changes in wood cell walls due to enzymatic activity
2014 - IRG/WP 14-20556
As development of techniques for examining enzymatic activity on solid, complex biological materials, is considered to be an important factor in further development of enzyme applications and for understanding the decay of plant materials, this study explores applicability of Scanning Transmission X-ray Microscope (STXM) for determining chemical changes in enzymatically treated samples at the cell...
D Jeremic, R Goacher, R Yan, C Karunakaran, E R Master
Modern Instrumental Methods to Investigate the Mechanism of Biological Decay in Wood Plastic Composites
2014 - IRG/WP 14-40674
Various instrumental techniques were used to study the fungal decay process in wood plastic composite (WPC) boards. Commercial boards exposed near Hilo, Hawaii (HI) for eight years in both sun and shadow locations were inspected and tested periodically. After eight years of exposure, both boards were evaluated using magnetic resonance imaging (MRI), while a selected area of the board exposed in sh...
G Sun, R Ibach, M Gnatowski, J Glaeser, M Leung, J Haight
Investigation of enzymatic effect on pit membranes by light and scanning electron microscopy
2016 - IRG/WP 16-40721
Spruce wood, one of the refractory wood species has pit membranes, which has an influence on the permeability of wood providing liquid flow between the wood cells. However, these membranes tend to close under the fiber saturated point (FSD), which makes impregnation more difficult. In this study spruce sapwood samples were treated with two different commercial enzymes to improve the permeability o...
S Durmaz, Ü C Yildiz, M Öztürk, B Serdar
Environmentally Friendly Wood Modification based on Tannin-Furfuryl alcohol - Effect on stabilisation, mechanical properties and decay durability
2022 - IRG/WP 22-40929
Furfurylation is a well-known wood modification technology. This paper studied the effect of tannin addition on the wood furfurylation. Three kinds of dicarboxylic acids, adipic acid, succinic acid, and tartaric acid, as well as glyoxal as a comparing agent, were used to catalyse the polymerisation of furanic or tannin-furanic solutions during wood modification. Impregnation of furanic or tannin-f...
M Mubarok, E Azadeh, F O Akong, S Dumarçay, A Pizzi, C Charbonnier-Gérardin, P Gérardin
Confocal laser scanning microscopy of a novel decay in preservative treated radiata pine in wet acidic soils
1997 - IRG/WP 97-10215
Light microscopy of radiata pine (Pinus radiata D. Don) field test stakes (20x20x500mm3) exposed in wet acidic (pH 3-4) soil for 12 - 24 months showed predominance of an unusual type of decay characte-rised by tunnelling attack of wood cell walls. After two years decay was moderate to severe in wood treated to ground contact CCA specifications and also equivalent retentions of creosote, and a numb...
R N Wakeling, Ying Xiao, A P Singh
Extending the useful life of creosoted electricity distribution poles in service
1993 - IRG/WP 93-50001-16
Creosoted transmission poles have provided good service over many decades in a whole range of environments. The use of save biocides for secondary treatments has the potential to extend the life of such poles. These techniques, together with a full understanding of the modes of failure, make it possible to establish new strategies to further improve the environmental benefits of treated wooden pol...
D J Dickinson, B Calver
Electron microscopic detection and chemical analysis of three-lamellar structures in wood-destroying fungi
1984 - IRG/WP 1240
In the course of transmission electron microscopical investigations of pine wood decay by various brown- and white-rot fungi extracellular three-lamellar structures (TLS) formed by the fungi were found in specimens stained with ruthenium red. These structures occured in the lumen of the wood cell surrounding the hypha at the outermost layer of the fungal cell wall. In the course of the investigati...
R Foisner, K Messner, H Stachelberger, M Röhr
Soft rot and bacterial decay in preservative treated eucalypt power transmission poles
1982 - IRG/WP 1155
Bacterial type decay was observed in CCA and PCP treated eucalypt power transmission poles. Detailed observations made with the SEM revealed bacterial colonisation and decay, especially in fibres. Plug samples taken from poles throughout Queensland were examined for preservative retention and presence of soft-rot decay. The severity of decay was different according to location, retention and speci...
L E Leightley
A short note on fungal decay in K33-treated poles
1982 - IRG/WP 1169
Soft rot cavities and erosion of the lumen have been found in K33-treated Pinus sylvestris poles from the years 1956-66 by microscopic studies. Poor treatment quality has been proved for some of these poles. The microscopy showed an unusual pattern of attack, and pre-treatment decay is suspected but not yet proved. Sounding the poles and using the Pilodyn indicated decay, but poking did not. Quant...
H Friis-Hansen
The isolation of actinomycetes from wood in ground contact and the sea
1980 - IRG/WP 1110
M S Cavalcante, R A Eaton
Some observations on causes of failure of preservative treated natural round transmission poles in Nigeria
1977 - IRG/WP 291
Treated natural round transmission poles in Nigeria have been discovered to be attacked underground as early as two years after planting. Termites and rot fungi attack the inner tissues and leave a pattern characteristic for the species of the pole. Tectona grandis, Nauclea diderrichii and Wide Pore pine, the major species for transmission poles in Nigeria show these attacks. A form of termite shi...
M A Odeyinde
Comparative studies on the distribution of lignin and CCA elements in birch using electron microscopic X-ray microanalysis
1987 - IRG/WP 1328
The microdistribution of metal preservatives in treated wood has received considerable research over the last two decades. Despite this, little effort seems to have been made to try and correlate the distribution of CCA elements with respect to naturally occurring wood cell wall components in wood. In the present preliminary study an attempt is made to relate the distribution of lignin in-situ wit...
G F Daniel, T Nilsson
Microscopic characteristics of Pinus radiata wood veneers weathered outdoors for one yea
1993 - IRG/WP 93-10018
Radiata pine (Pinus radiata) wood veneers glued to solid wood hacking strips were exposed outdoors at 45° north-facing for one year and then examined by light microscopy (LM) and transmission electron microscopy (TEM). As expected, the exposed wood surfaces were colonised by a variety of microorganisms; however, wood decay was not observed. Ultlaviolet (UV light) radiation and water were the main...
A P Singh, R A B Sweeney, E A Dunningham, D V Plackett
Effect of methylene bisthiocyanate on morphology and ultra-structure of a sapstain fungus, Ophiostoma floccosum
2003 - IRG/WP 03-10471
In vitro effects of methylene bisthiocyanate (MBT) on hyphal morphology and ultrastructure of Ophiostoma floccosum were examined using differential interference contrast, epifluorescence and transmission electron microscopy (TEM).
Differential interference contrast microscopy suggested that MBT caused rapid changes to the morphology of O. floccosum resulting in excessive formation of vacuoles and...
T Singh, B Kreber, R N Wakeling, A Stewart
A baiting technique to monitor the development and control of decay in transmission poles
1981 - IRG/WP 2149
P I Morris, D J Dickinson
Bordered Pit Imaging
2012 - IRG/WP 12-10773
New findings about bordered pits will be presented using the latest microscopy techniques. Three-dimensional imagery at the nanolevel is used, and short 3-D movies will shown as part of the discussion on this topic to reveal new features that have not previously been reported in pits. The implications for both microorganism penetration through lignified cells as well as preservative penetration i...
D Mascheck, B Goodell, H Militz, M Lessard, J Jellison
The Pilodyn instrument as a non-destructive tester of the shock resistance of wood
1978 - IRG/WP 2107
A new non-destructive shock resistance tester, the PILODYN, has been developed. The instrument measures the fracture surface area created by a constant amount of energy. It operates by shooting a blunt pin into wood by an exact amount of energy. The penetration depth is read on a scale. A wide field of application is open to a non-destructive shock resistance tester such as: 1) assessment of the r...
P Hoffmeyer
Insect transmission of fungal sapstain to freshly sawn unseasoned softwood lumber
1994 - IRG/WP 94-20025
Chemical dip treatments were used to investigate micro-arthropod transmission of fungal sapstain to unseasoned pine sapwood boards. Saptain, mould and basidiomycete defacement of chemically treated sawn boards of Corsican pine was recorded during a 14 week field trial. Boards were treated with either a fungicide, an insecticide/acaricide, a combination of the fungicide with the insecticide/acarici...
M A Powell, R A Eaton, J F Webber
Transmission poles with sub-standard retentions protected by Field Liners outperform standard poles in service
1997 - IRG/WP 97-40095
Eucalyptus cloeziana 12m transmission poles were treated with sub-standard creosote retentions of 80kg/m3 and Field Liners were fitted to the poles before they were placed in service at Umbumbulu, Kwazulu Natal. Poles treated with standard creosote retentions of 130kg/m3 but without Field Liners were also placed in service in the same area. Core samples were taken from both groups of poles after 1...
M R Behr, G D Shelver, A A W Baecker
The use of the Pilodyn for detecting soft-rot decay in CCA treated eucalypt poles
1986 - IRG/WP 2251
A 6 Joule Pilodyn unit with 2.5 mm diameter pin was used to inspect CCA treated eucalypt poles, suspected of suffering groundline soft-rot decay. Pole plugs were removed at the inspection region and the amount of soft-rot decay present determined microscopically. High correlation (R² = 0.73) was obtained between the amount of soft-rot and Pilodyn pin penetration. The Pilodyn is recommended as a u...
L E Leightley, G A Willoughby
Patterns of bacterial attack in preservative treated eucalypt power transmission poles
1984 - IRG/WP 1223
Patterns of bacterial decay have been examined using light and scanning electron microscopy. Two morphologically distinct patterns have been recognised in preservative treated eucalypt power transmission poles. Bacterial Decay I (BDI) involves the removal of the secondary wall layers initiating with erosion of the S3 layer from the cell lumen. As decay progresses the S2 layer and S1 layer are degr...
G A Willoughby, L E Leightley