Evaluation of the leach resistance and preservative efficacy of novel biocides as surface treatments applied by brush to spruce (Picea abies)
1998 - IRG/WP 98-30170
The comparative leach resistance and preservative efficacy of a number of alternative organic preservatives (available from Zeneca Specialties) and selected commercially available biocides as surface coatings to wood in Hazard Class 3 have been assessed. Two concentrations of test preservatives were applied by brush to Spruce (Picea abies), including formulation and untreated controls. A leaching ...
I M Tierney, A Bruce, D C R Sinclair, T Yeates
Evaluation of the fire retardant efficacy and leach resistance of an amino resin fire retardant - Preliminary report
1983 - IRG/WP 3260
The Early Fire Hazard Indices of untreated Pinus radiata were determined by testing to Australian Standard 1530, Part 3 - 1976. Differences in the performance of heartwood and sapwood were noted, with heartwood samples giving higher Ignitability, Heat Evolved and Spread of Flame indices. The treatability of Pinus radiata with Pyrogard H was assessed, and backsawn sapwood treated more effectively t...
W D Gardner, P N Alexiou, P Lind, D Butler
Protection of southern pine using N,N-Napthaloylhydroxylamine: Field tests, soft-rot cellars and aquatic bioassay leach testing
1999 - IRG/WP 99-30204
Recent environmental restrictions are limiting the use of broad-spectrum biocides for wood preservation. There is an urgent need for new, sharply targeted, environmentally benign wood preservatives. N'N-Napthaloylhydroxylamine (NHA), a water-soluble calcium-precipitating agent, has been shown to inhibit decay by brown-rot and white-rot fungi in soil-block tests and prevent damage by Easte...
D M Crawford, F Green III
New boron-based biocides for the protection of wood
2002 - IRG/WP 02-30283
Boric acid and other simple inorganic oxides of boron are amongst the oldest wood preservatives currently in use. Their relatively low toxicity and broad-spectrum activity are just some of their desirable characteristics. The primary disadvantage associated with conventional boron-based preservatives is their lack of permanence in exposed applications. A collaborative project between CSIRO and the...
D G Humphrey, P J Duggan, E M Tyndall, J M Carr, L J Cookson
The suitability of isothiazolone microemulsions as long term wood preservatives
1997 - IRG/WP 97-30150
Microemulsion formulations of 4,5 dichloro-2-n-octyl-4-isothiazolin-3-one were investigated to determine the leaching potential of these formulation types as well as their efficacy against decay fungi. These patented low leaching formulations exhibited good anti fungal efficacy in standard tests combined with minimal leaching of the active ingredient from the wood. The data suggests that the excel...
B M Hegarty, Bing Yu, L E Leightley
Mobility of zinc borate wood composite preservative
1997 - IRG/WP 97-30153
Zinc borate (ZB) is being used as an antifungal and insecticidal wood preservative for flake/strand-based composites. Data is reported on the laboratory and field leaching behavior of ZB when contained in apen flake composites. In general, the performance results correlate with leaching hazard. Although the boron in ZB is more resistant to depletion than in sodium borates, the ZB boron will deplet...
P E Laks, M J Manning
Preservation of wood composites with zinc borate
1995 - IRG/WP 95-30074
Inorganic borates such as boric acid, borax, disodium octaborate tetrahydrate, and zinc borate can be incorporated into wood composites such as waferboard to impart decay and insect resistance to the final product. Zinc borate is especially well suited for this application due to its efficacy and leach resistance. The paper summarizes the work performed to date in this area. The effects on strengt...
P E Laks, M J Manning
Leaching properties of copper and triazole
2009 - IRG/WP 09-30509
The leaching rate of copper and triazole (such as tebuconazole and propiconazole) in different preservative formulations was determined according to AWPA E11-06. Of all copper triazole and ACQ formulations, copper fixation rate of ammonia based was higher than that of ethanolamine based and the mixture of them. Copper fixation rate at relatively higher retention was slight higher than that at lowe...
Zhiqiang Li, Xiaowen Li, Ying Zhang, Mingliang Jiang