Your search resulted in 124 documents. Displaying 25 entries per page.
Performance of Oriented Strandboard, Medium Density Fiberboard, Plywood, and Particleboard Treated with Tebuconazole in Supercritical Carbon Dioxide
2005 - IRG/WP 05-30364
The performance of oriented strandboard (OSB), medium density fiberboard (MDF), particleboard and plywood treated with tebuconazole using supercritical carbon dioxide was investigated over a 48 month exposure under harsh above ground conditions in Hilo, Hawaii. Samples treated to low retentions (<0.20 kg/m3) tended to experience decay at rates that were only slightly lower than those found wit...
J J Morrell, M N Acda, A R Zahora
The Protection of Plywood with Benzalkonium Chloride (BAC) Wood Preservative
2002 - IRG/WP 02-40219
Alkyldimethylbenzyl ammonium chloride (benzalkonium chloride) (BAC) and alkyldimethylamine acetates were approved by the Timber Preservation Authority of New Zealand in 1978 for the protection of radiata pine that was destined for above ground, weather exposed applications. As a result of continuing failures, the use of AACs was stopped in New Zealand in the mid 1980s.
The Plywood Association of ...
J Norton
Future insecticidal treatments for wood products
1980 - IRG/WP 3140
Protective measures involving chemical treatment of wood use only a narrow range of toxic materials which are divisible into two groups, (i) those that are water-soluble, (ii) those that are soluble only in organic solvents. It is generally true to say that, as far as protection against insects is concerned, the former are stomach poisons while the latter are largely (though not exclusively) conta...
D J Cross
Laboratory evaluation of water repellents as antisapstain treatment additives
1986 - IRG/WP 3382
Water repellent formulations consisting of five paraffin wax emulsions, three polyethylene wax emulsions, two polybutadiene resin emulsions, a polyester emulsion, and a ß-pinene polymer emulsion were subjected to water repellency tests on radiata pine sapwood. With one exception, the parafin wax emulsions were more effective water repellents than the alternative formulations and one of the paraff...
D V Plackett, C M Chittenden
Internal pressure development within Oriented Strand Board during supercritical fluid impregnation
2000 - IRG/WP 00-40175
Supercritical fluids (SCF) offer an attractive alternative to conventional treatment processes for delivering material into wood, but there are many unanswered questions concerning the technology. One major concern is the potential for the development of excessive pressure gradients in the wood that might exceed the material properties and lead to crushing or other pressure-induced damage. Previou...
G Oberdorfer, P E Humphrey, R J Leichti, J J Morrell
Permatek IM 30 as a termiticide treatment for veneer-based wood products
2003 - IRG/WP 03-30325
Permatek IM 30 is a termiticide designed for incorporation into wood products during manufacture.
Whereas existing approved products in Australia are based predominantly on synthetic pyrethroids carried in solvents, Permatek IM 30 is based on imidacloprid, a neonicotinoid insecticide. The formulation has very low mammalian toxicity, is free of VOCs, and has been successfully tested as a glueline ...
J Doyle, K Webb, W R Rae, A F Siraa, J Malcolm-Black
Glue-line additives for protecting plywood. A review
1978 - IRG/WP 2102
The conclusions of this review are: 1) Insecticidal glue-line additives can be used satisfactorily to protect plywood against insect attack. 2) It is uncertain, in spite of some claims, wether fungicidal glue-line additives can be similarly used to protect plywood against fungi under damp conditiones. There is a need for further work to validate the mycological tests that may be used to investigat...
R Cockcroft
Compatibility of deltamethrin with wood adhesives
1993 - IRG/WP 93-30031
This work presents the studies conducted on the compatibility of deltamethrin when mixed with wood adhesive to manufacture plywood in order to protect the wood against wood-borers insects and termites. The following types of adhesive were tested: PVA, Urea-formaldehyde, phenol-formaldehyde and a formulation based on tannin. The experiments were made in the adhesive manufacturers' laborato...
A M F Oliveira
Stability of bifenthrin in a commercial phenol-formaldehyde plywood glue
2003 - IRG/WP 03-30311
Liquid phenol formaldehyde (PF) glue mixes used for plywood manufacture are strongly alkaline. At this pH insecticidal additives may not be stable for long periods. In order to establish practical working life of the synthetic pyrethroid insecticide, bifenthrin, in liquid PF glues the concentration of bifenthrin in the glue mix was measured under laboratory conditions over a 24 hour period. Glu...
M J Kennedy, P A Collins, R D Vella
Diagnostics methods and routes proposalsto define selective sorting of demolition wood wastes
2001 - IRG/WP 01-50177
Wood wastes are more and more often used in different wood waste valorisation industries (panels, wood energy, cement factories, ...). These industries are in progress to include in their processes, wood wastes coming from demolition wood. A state of the art and an analysis have been made to propose : (1) diagnostics methods to carry out a classification of wood wastes on demolition sites and in t...
G Labat, E Bucket, C Fréret, G Deroubaix
Preliminary indications of the natural durability of Spruce bark board
1999 - IRG/WP 99-10312
A board material made from pressed bark, with no added adhesive, has been developed by Forintek's composites group and tested for durability by Forintek's treated-wood group and the University of Hawaii. This material was also manufactured with veneers in a one-step process. Since one role of bark on the tree is protection against pests and diseases, barkboard was expected to hav...
P I Morris, J K Grace, G E Troughton
Upgrading the fungal resistance of OSB
1999 - IRG/WP 99-40138
There is a perception that oriented strand board (OSB) is less resistant to fungl than plywood under conditions of moderate exposure to moisture. Douglas fir-faced plywood (DFP) has been suggested as a benchmark for acceptable durability under such conditions. This project was initiated to determine the minimum level of low-toxicity chemical treatment needed to upgrade the fungal resistance of OSB...
P I Morris, J E Clark, D Minchin, R Wellwood
L-joint based testing for service life prediction of exterior plywood in out of ground contact conditions
2006 - IRG/WP 06-20342
Good biological performance of several plywood types in exterior conditions is most probably related to altered wood moisture behaviour compared to solid wood. Therefore a test set up was developed, using EN 330 L-joint testing methodology, to facilitate differentiation of plywood for exterior applications.
The proposed test set up is an adaptation of an accelerated L-joint method introduced by V...
J De Smet, I De Windt, J Van Acker
Laboratory bioassay and field trial on imidacloprid and cypermethrin as glueline treatments for softwood plywood
2006 - IRG/WP 06-30405
The effectiveness of imidacloprid and cypermethrin as glueline treatments for protecting phenol formaldehyde (PF)-bonded Pinus radiata (radiata pine) plywood from attack by subterranean termites was evaluated both in the laboratory and field. Imidacloprid was evaluated in two plywood constructions (19 ply x 1.6 mm-thick veneers and 5 ply x 3.2 mm-thick veneers) whereas cypermethrin was evaluated i...
J W Creffield, D K Scown
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
Influence of Acetylation on Fire Resistance of Beech Plywood
2006 - IRG/WP 06-40326
Influence of acetylation on fire resistance was studied in beech plywood. Beech layers were acetylated in a reactor with acetic anhydride at 120ºC for varying durations. Plywoods were made from the acetylated layers and directly exposed to burning flame from their edges for 60s according to ISO 11925-3. Ignition and glowing time were measured in samples. Results were analyzed statistically based ...
B Mohebby, A Talaii, A Karimi , S Kazemi Najafi
Biological Protection of Composite Panel from Moulds and Decay
2007 - IRG/WP 07-10612
Composite panels, such as oriented strand board (OSB), are widely used in house construction in North America. These structural panels are normally made of non-durable wood species and are susceptible to moulds and decay when exposed to wet conditions. Building envelope failures due to moulds, decay or poor construction practices can negatively impact the image of wood. To ensure durability of com...
Dian-Qing Yang, Xiang-Ming Wang, Hui Wan
Bifenthrin recovery from glue-line-treated plywood
2007 - IRG/WP 07-20355
Plywood and laminated veneer lumber (LVL) can be protected from termite damage by addition of bifenthrin to the adhesive used in product manufacture. However, conditions associated with this manufacturing process may lead to deterioration or immobilisation of the active ingredient. In order to determine compliance with treatment specifications, it is important that the concentration of a preservat...
J Norton, L Stephens
Effect of fungal attack on maximum load capacity of simulated wall assemblies
2007 - IRG/WP 07-20363
The effects of moisture intrusion and fungal attack on the maximum load capacity of nailed assemblies was investigated using one white and one brown rot fungus against 4 material combinations over a 20 week period. Wetting significantly reduced the maximum load capacity of all four material combinations, while wetting and autoclaving only affected the OSB sheathing/spruce stud. The white rot fung...
N Melencion, J J Morrell
Service life prediction of plywood
2007 - IRG/WP 07-20367
Plywood is the wood based panel showing the best physical and mechanical properties for application under moist construction conditions. Appropriate physico-mechanical durability for exterior applications in transportation or construction systems can be guaranteed by assessment of the glue bond quality and mechanical characteristics. However, due to the fact that mainly non-durable wood species ar...
J Van Acker, J De Smet
Decay Resistance Properties of Hemicellulose-Extracted Oriented Strand Board
2008 - IRG/WP 08-10644
There is increasing interest in using cellulosic biomass as the basis for a renewable source of energy. Although the traditional focus has been on cellulose, researchers are also exploring the possibility of using hemicelluloses because they can be removed with hot water leaving the wood product intact for other applications. However, there is concern that removing hemicelluloses from the precur...
C Howell, J Paredes, S Shaler, J Jellison
Evaluation of natural durability of solid wood and mixed heartwood-sapwood Cypress (Cupressus sempervirens L.) plywood against Basidiomycete fungi
2008 - IRG/WP 08-10645
The aim of this research was to study the response of mixed plywoods composed of durable heartwood and non-durable sapwood to fungal attack. For this purpose, the species of Cupressus sempervirens (cypress) was chosen for its well-known durable heartwood. The evaluation of durability of plywood panels against fungi was done according to ENV 12038 and the fungi used were Coriolus versicolor (CV) an...
F Faraji, M F Thévenon, N Lemenager, B Thibaut
The susceptibility of hardwood plywood to white rot
2008 - IRG/WP 08-40397
The subject of the tests was resistance of veneer hardwood plywood to activity of pure culture of white rot fungus Trametes versicolor. The tested plywood was made with the use of the following glues: urea-formaldehyde (UF), melamine-urea-formaldehyde (MUF) or phenol-formaldehyde (FF). 4, 12 and 15 mm thick plywood was tested. External veneer of the plywood was mostly alder and the inner veneer (c...
A Fojutowski, A Kropacz
Resistance against basidiomycetes of 1,3-dimethylol-4,5-dihydroxy ethylene urea (DMDHEU)-modified plywood of Pinus sylvestris
2008 - IRG/WP 08-40398
Plywood produced with rotary-cut veneers of Pinus sylvestris impregnated with a solution of 1.3 M 1.3-dimethylol-4.5-dihydroxyethyleneurea (DMDHEU) and glued with a phenolic resin (Prefere 4976 DYNEA) were inoculated with Coniophora puteana, Coriolus versicolor and Pleurotus ostreatus, following the European standard ENV 12038. The specimens were leached following European standard EN 84. The re...
A Dieste, A Pfeffer, S Bollmus, H Militz
Material properties of acetylated beech plywood
2008 - IRG/WP 08-40425
The effect of acetylation process on dimensional stability and mechanical properties of plywood made by Oriental beech layers (Fagus orientalis Lipsky) were studied. The layers cut into sizes of 200×200×2 mm and acetylated in 120°C for 30 and 60 min.
Thickness swelling (TS%), water absorption (WA%) and anti-swelling¬ efficiency (ASE%) of specimens were measured. Mechanical properties (MOE, MO...
A Talaei