Study on Nailed Joint with Iron Contamination. Part2: Elucidation of the Occurrence Condition of Iron Contamination
2019 - IRG/WP 19-50350
In recent years, efforts towards wooden buildings are progressing in Japan. And many woods are used in various places. However, various problems have also occurred in wooden buildings. One of the problems is iron contamination which appears when wood and metal chemically react. At present, tree species that are prone to iron contamination and components that cause iron contamination are clarified....
D Nakano, R Nakano, H Ishiyama


A novel device for detecting internal defects in wooden poles
1989 - IRG/WP 2329
The diagnosis of internal defects caused by termites and decay in hardwood transmission poles has been investigated using a novel Automatic Feed Drill (AFD) pole testing device. Internal defects were recognised by changes in drill feed-rate as the automatic air-driven drill traversed its 100 mm working stroke. The instrument is portable, simple to operate and recognises defects instantaneously. Te...
R A Eaton, R S Johnstone


Environmental fate of copper-based wood preservatives in different soil substrates - Part 2: Study of the metal sorption and migration potential under simulated rainfall
1998 - IRG/WP 98-50101-21 b
In order to examine the potential environmental impact of spillages of the saltborne wood preservative CCA in treatment plants, four large scale experiments are set-up so as to follow the water transport and ion mobility in various field soils. A plastic container is filled with a sand, silt, clay and potting soil, made up at their respective bulk density and wetted to a given moisture content. U...
G M F Van Eetvelde, R Hartmann, J M Mwangi, H S Öztürk, M Stevens


Rapid loss of lignin at wood surfaces during natural weathering
1992 - IRG/WP 92-2390
Thin veneers of radiata pine (Pinus radiata D. Don) were exposed to natural weathering over a period of 30 days. Incident UV radiation was monitored at the test site. FTIR internal reflectance spectroscopy was used to study the chemical changes taking place at the veneer surface during weathering. Spectra obtained show that after only 3 days exposure there was substantial delignification at veneer...
P D Evans, K J Schmalzl, A J Michell


Rainfall simulation to assess CCA permanence
1991 - IRG/WP 2373
During experimental work on accelerated fixation of chromium containing preservatives a method has been developed which compares the degree of preservative levels of contamination of simulated preservative fixation in timber with the levels of simulated rainfall. This method uses commercial sized wood sections wetted in a way that simulates actual rainfall and relates the associated run-off contam...
P Warburton, J A Cornfield


Ability of an acoustic inspection device to detect internal voids in untreated pole sections
2002 - IRG/WP 02-20246
Detecting deterioration before substantial losses in material properties occur poses a major challenge to most wood users. While physical inspection techniques such as drilling or coring are useful, these methods can miss small pockets of damage and they lack the ability to detect early or incipient decay. The development of sonic test methodologies has created the potential for detecting change...
J J Morrell, R G Rhatigan


Performance of copper-chrome formulations in ground contact in five test sites in New Zealand
1996 - IRG/WP 96-30113
Copper-chrome-arsenate (CCA), copper-chrome-boron (CCB), copper-chrome-fluoride (CCF) and copper-chrome-phosphate (CCP) have been tested at four retentions each in ground contact (25 x 50 x 500 mm³ radiata pine sapwood stakes) for 16 years in five test sites in New Zealand. Results to date show that test site characteristics have a marked effect on relative performance. In a warm and wet site (an...
M E Hedley, R N Wakeling, J Foster, B E Patterson


Imaging fungal deterioration of wood using x-ray microtomography
1997 - IRG/WP 97-10240
Nondestructive tomographic images of solid Southern yellow pine (SYP) wood and SYP during deterioration by wood decay fungi were obtained by using a new class of synchrotron X-ray computed microtomography (CMT). The CMT images will provide information about spatial relationship between degrading fungi and wood structures. Wood samples were scanned with synchrotron-generated X-rays at high resoluti...
B Illman, B A Dowd


Leaching of copper-chrome-arsenic treated timber: Simulated rainfall testing
1996 - IRG/WP 96-50074
Six kiln dried radiata pine sapwood packs of timber were preservative treated with copper-chrome-arsenic preservative using a modified Bethell treatment schedule. The packs were then subjected to simulated rain leaching at specified periods after treatment. Higher chromium leachate was obtained when higher volumes of simulated rainfall were applied. Lower chromium leachate was obtained for timber ...
S Walley, P R S Cobham, P Vinden


The Role of Moisture Content in Above-ground Leaching
2007 - IRG/WP 07-50245
This paper reviews previous reports on the moisture content of wood exposed above ground and compares those values to moisture contents obtained using simulated rainfall and immersion methods. Laboratory leaching trials with CCA-treated specimens were also conducted and the results compared to published values for leaching of CCA-treated specimens exposed above ground outdoors. Previous researcher...
S Lebow, P Lebow


Depletion and Redistribution of Boron in Bundles of Commercially Treated Lumber Exposed to Artificial and Natural Rainfall
2008 - IRG/WP 08-30474
The depletion and redistribution of boron from stacks of Southern Yellow Pine lumber pressure treated with disodium octaborate tetrahydrate (DOT) and exposed to artificial and natural rainfall was examined. When the lumber was exposed to periodic simulated rainfall, 5.7-8.1% of the measured boron present leached from the lumber after exposure to over 300 mm of rainfall. In tests which exposed bo...
M E Mankowski, M J Manning


Towards a microactuator-sensing network for the structural health monitoring of wood
2023 - IRG/WP 23-50380
Timber structures decay over time with degradation in their structural integrity. Changing environmental conditions, varying loads, exposure to moisture or insect attacks lead to changes in their vibrational response behaviour. Here we present a low-cost device used as a triggered exciter to enable the monitoring of the structural integrity of timber bearers or even power poles in electricity netw...
S Oberst, S Sepehrirahnama, C Nerse, Z Brodzeli, J C S Lai, M Mankowski, T Atkinson, R Arango, G Kirker, T Evans