Blue stain in timber in service. Preliminary results of the IRG collaborative tests to compare natural and artificial weathering
1978 - IRG/WP 286
The collaborative programme was initiated at IRG Meetings in Wildhaus, 1976. The six collaborators were BAM (Berlin), Cuprinol Ltd (UK), EMPA (Switzerland), GORI (Denmark), PRL (UK) and Imperial College (UK). Experimental plans were finalised in December 1976 and panels treated by Cuprinol Ltd early in 1977. Natural weathering was carried out by BAM, Cuprinol, EMPA, GORI and PRL during April-Septe...
A F Bravery, D J Dickinson
Inorganic preservative levels in soil under treated wood decks after 8 years natural exposure in Borås, Sweden
2005 - IRG/WP 05-50233
Inorganic preservative components (Cu, Cr and As) were measured to a depth of 150 mm under deck structures made with Scots pine lumber treated with several different wood preservatives and installed in Borås Sweden 8 years ago. Higher contaminant levels were observed mainly under the drip lines and in the top 50 mm of soil. Under CCA treated decks, soil arsenic concentrations increased from ba...
P A Cooper, Y T Ung, M-L Edlund, J Jermer
Accelerated testing for out of ground contact using natural biological preconditioning
1996 - IRG/WP 96-20088
Small blocks made of Scots pine sapwood were treated, buried in vermiculite and exposed to natural microbial colonisation during outdoor exposure prior to laboratory decay testing. Periodic microbial isolations, moisture content, permeability and weight loss tests were also conducted. Bacteria and moulds colonised the vermiculite and miniblocks well. Aureobasidium pullulans was common on TnBTO tre...
S Molnar, D J Dickinson, R J Murphy
Tropical In-Ground Durability of Structural Sarawak Hardwoods Impregnated to High Retention with CCA-salts, CCA-oxide and FCAP after 20 Years Exposure
2005 - IRG/WP 05-30384
Statistical analysis (ANOVA) was conducted on durability (termite and decay combined) rating data collected over 20 years exposure period of over 140 species of Sarawak timbers with altogether 30,000 stake specimens, at the Forest Department’s Sibu “graveyard” stake test sites from 1977. About 20 replicated stakes were pressure-treated to refusal with 10% g/ml concentration of up to 3 CCA-sa...
Wang Choon Ling, A H H Wong
An anti-termite formulation for soil treatment with natural products and its efficacy against Coptotermes formosanus Shiraki
2003 - IRG/WP 03-30319
An anti-termite formulation of an environmental conservation type for soil treatment was developed. The formulation was composed of decanoic acid (n-capric acid, an fatty acid derived from coconut oil with ten carbons) as an active ingredient and other natural products. Experiments to examine the efficacy of the formulation against Coptotermes formosanus Shiraki were conducted at the termite field...
S Yoshida, T Nakagaki, A Igarashi, A Enoki
Specifying preservative-treated resistant timber: Conforming to European Standards
2001 - IRG/WP 01-20235
The most common construction timbers used in the UK are of low natural durability and, generally, resistant to preservative treatment. These include species of spruce, hemlock and fir. However, their characteristically limited and non-uniform uptake of preservatives may still confer sufficient protection to give satisfactory durability performance in terms of biological resistance. This paper desc...
E D Suttie, A F Bravery, T B Dearling
Ten year performance of l-joints made from borate diffusion treated wood
2000 - IRG/WP 00-30225
While there are decades of experience with borate-treated wood in coated, exterior applications in New Zealand and the UK, other countries have been more reluctant to use this process. As part of a research program on the potential use of borates by the Canadian wood products industry, Forintek set up, in 1990, an L-joint test of untreated and borate-diffusion treated hem-fir (western hemlock and ...
P I Morris
Evaluation of wood preservatives for Nordic wood preservation class AB
2002 - IRG/WP 02-30297
In the Nordic countries there are restrictions in the use of wood preservatives based on chromium and arsenic. For above ground use, class AB according to the Nordic system, only
copper based preservatives are allowed in Sweden. Thus several new preservatives, copper based or metal free are now used. They have been approved by the Nordic Wood Preservation Council after passing laboratory tests ag...
M-L Edlund, J Jermer
Termite durability of sugi (Cryptomeria japonica) heartwood kiln-dried under high-temperature process in relation to wood extractives
2005 - IRG/WP 05-10547
Termite durability of sugi heartwood samples kiln-dried under a high-temperature process were evaluated by using Reticulitermes speratus (Kolbe) as a test termite sp. The n-hexane extractives of these samples were analysed by a GC technique. The less termite durability was shown on the wood samples dried under the high-temperature process, in comparison with that of the air-dried samples. No GC-p...
S Shibutani, E Obataya, K Hanata, S Doi
Deltamethrin effectiveness against subterranean termite attack on wood under natural conditions
1989 - IRG/WP 1407
On fighting subterranean termites on wood, out of ground contact, the synthetic pyrethroid Deltamethrin shows positive aspects such as its efficiency and low mammalian toxicity. To evaluate its performance in conditions very similar to those in service use, specimens of Pinus sp were treated with solutions of Deltamethrin diluted in "white spirits" at 0.005% (w/w) and 0.01% (w/w) and exposed in a ...
P A Zanotto
Long-term preservation technology for a large-scale timber structure building in Japan
2001 - IRG/WP 01-40203
Several 1.000-year-old Buddhist temples and shrines built of wood are surviving in Nara, some areas of which are inscribed on the World Heritage List. These old buildings are indicative of excellent timber construction technology having existed in ancient Japan, though it is thought that such technology has not been handed down. This paper introduces one of large-scale wood buildings built in rece...
Y Iimura
Surface checking of CCA-treated radiata pine decking timber exposed to natural weathering
2000 - IRG/WP 00-40165
A field trial was established at four locations in Australia to assess the effect of CCA and CCA-wax treatment on the checking (cracking) of radiata pine decking timber exposed to natural weathering. Untreated decking timber and timber that had been pressure treated with water acted as controls. After 1 year's exposure the number and sizes of checks occurring in treated timber and control...
P D Evans, P J Beutel, C F Donnelly, R B Cunningham
Characteristics of thermally modified wood in vacuum
2004 - IRG/WP 04-40287
In commercial thermal wood modification processes nitrogen, steam or oil has been used for the reduction of oxygen content in the reactor atmosphere. In present study no special heating medium, but an initial vacuuming step has been used for this purpose. Mass loss, resistance to fungal decay, dimensional stability, bending strength and modulus of elasticity of heat treated wood were evaluated and...
G Rep, F Pohleven, B Bucar
Testing blue stain fungicides for joinery timber in combination with natural weathering
1976 - IRG/WP 268
Joinery timber in outside use becomes affected by blue-stain after a short time of exposure. This is especially the case with pine sapwood treated with unpigmented lacquer, but also with other timber species as well as different types of surface treatment. According to the basic investigations of BUTIN this is due to special types of blue-stain fungi, called "Lack-bläue" (lacquer blue-stain), in ...
H Willeitner
Impact of leachates from CCA- and copper azole-treated pine decking on soil-dwelling invertebrates
2002 - IRG/WP 02-50183
This study assessed the short-term effects on non-target soil invertebrates of leachates from a naturally durable hardwood and timber treated with two copper-based wood preservatives. Natural rainwater leachates from kwila decking, and radiata pine-decking treated with CCA or copper-azole, were collected and applied on mown lawn soil in Brisbane, Queensland. The soil study consisted of 5 treatment...
N Crumière, A House, M J Kennedy
Durability of Sugi (Cryptomeria japonica D.DoN ) wood treated in high temperature liquid paraffin
2002 - IRG/WP 02-40221
Sugi(Cryptomeria japonica D.DoN )wood was subject to a heat treatment in high-temperature liquid paraffin for the purpose of improving the resistance against fungi and termites without chemicals. The bath of paraffin liquid, which can provide a uniform heat transfer (±2?), was used at temperatures of 90?,120?and 150?.?ecay resistance according to JIS K 15711) was evaluated using a brown rot fungu...
Y Matsuoka, W Ohmura, S Fujiwara, Y Kanagawa
Comparative study of blue stain resistance of various types of wood stains after artificial and natural weathering
1992 - IRG/WP 92-2411
For the determination of the protective effectiveness of a preservative treatment against blue stain in service, artificial weathering has been proposed as an alternative for the natural weathering period of 6 months in the European standard EN 152. Research on a range of products and on complete finishing systems for external joinery was conducted during 1986-1990. It revealed that the decisions ...
J Van Acker, M Stevens, M Nys
Life Cycle Assessment of borate treated wood
2005 - IRG/WP 05-50224-12
Life Cycle Assessment (LCA) is being used increasingly around the world by decision-makers to help incorporate the environmental component of sustainability into their activities. U.S. Borax regularly assesses how its products contribute to sustainable development. Using data gleaned from LCA of its products, the company recently completed its first ISO 14040 compliant cradle-to-grave LCA of lum...
M J Manning
Present status of using treated wood and private house owner’s expectations in Bangladesh
2004 - IRG/WP 04-30329
In a developing country like Bangladesh more than 80 % of the total population lives in rural areas where building materials are mainly comprised of wood, bamboo, thatch grass, golpata, etc. All these materials, being cellulosic, are easily infected by deteriorating agencies like fungi, termites, beetles etc., as climatic condition of the country is ideal for their thrive. This is a great wastage ...
M A Islam, A K M A Bosunia, S C Ghosh, M O Hannan, A K Lahiry
Accelerated testing for out of ground contact using natural biological preconditioning: Part 2
1997 - IRG/WP 97-20108
Small blocks of scots pine sapwood were treated, buried in vermiculite and exposed to natural microbial colonisation during outdoor exposure prior to laboratory decay testing. An EN 84-type leach trial was carried out on unexposed samples. Periodic microbial isolations, moisture content, permeability and weight loss tests were also conducted. The experiment ran for 12 months. The colonisation of t...
S Molnar, D J Dickinson, R J Murphy
Resistance of twenty-five species of timbers to marine borer attack at Visakhapatnam, east coast of India
1994 - IRG/WP 94-30036
Observations on the natural resistance of 25 species of timbers to marine borer attack for a twelve month period at the fishing harbour, Visakhapatnam, East Coast of India, indicate that none of the species was free from borer attack. The damage was mainly by teredinids - Teredo furcifera and Lyrodus pedicellatus. Martesia striata, Teredo parski, Bankia campanellata and Lyrodus bipartitus were als...
K S Rao, M Balaji, V V Srinivasan
Supply of wooden transmission and telephone poles in Tanzania: Problems and possible solutions
1987 - IRG/WP 3424
The eucalypts which have been used widely for utility poles for more than 30 years have dwindled remarkably from traditional supply areas. Consequently, pole-using authorities are considering importing poles from abroad. This alternative is considered unrealistic and costly. The aims of this paper are: - to dispel fears of pole scarcity and to show that an abundant resource of a variety of tree sp...
K K Murira, S A Diwani
Water transfer in wood in relation to fungal attack in building - Effect of condensation and diffusion
1992 - IRG/WP 92-1543
Wood is continuously exchanging moisture with the surrounding atmosphere, the temperature and relative humidity are important factors. Wood moisture in this case is not enough to provoque decay by fungi. However, when, during the night, condensation appears cyclically, wood absorbs water and moisture content may be sufficiently high to allow development if drying does not take place. The water tra...
D Dirol, J-M Vergnaud
Biocidal property of the phenolic fraction of ethanol extractives of Hopea parviflora heartwood
1993 - IRG/WP 93-30003
Natural resistance of some species of timber to fungal decay and insect damage (particularly termite) is ascribed toxic nature and quantity of certain chemical substances present in the cell wall of heartwood. These chemical substances generally known to be Phenolic and Polyphenolic compounds (Rao 1982). Earlier investigations on extractives were mainly in relation to resistance of timber to decay...
R V Krishnan, K S Theagarajan, H S Ananthapadmanabha, M Nagaraja Sharma, V V Prabhu, H C Nagaveni
Comparative study on the leaching of wood preservatives between natural exposure and accelerating laboratory conditions
1999 - IRG/WP 99-50134
Impregnated specimens with CCA, ACQ, and BAAC were subjected to leaching tests. Specimens of 2x2x1 cm3 in size were used for the laboratory leaching test for 10 days according to JIS K 1571. Specimens of 25x1 x1 cm3 were used for outdoor leaching test for 6 months. Total leaching amounts of boron per cm3 of specimens treated with BAAC were 325 µg in the laboratory test and 206 µg in the outdoor ...
K Yamamoto, S Motegi, A Inai