Your search resulted in 66 documents. Displaying 25 entries per page.
Evaporation and redistribution of creosote in pine poles during storage
1996 - IRG/WP 96-50064
During the work with European standards for pressure treated wood, it has been questioned if the lapse of time between impregnation and chemical analysis of the retention is critical, especially for creosote. "The Norwegian Control Scheme for Preservative Treated Wood" has not discovered any retention problems analysing CCA preservatives in wood. If the lapse of time between impregnation with creo...
F G Evans, B Nossen
Laboratory Leaching Tests to Study the Effects of Post-Treatment Storage Periods on CCA Leachability and Fixation in Treated Permeable and Refractory Malaysian Hardwoods
2006 - IRG/WP 06-50240
The biological resistance and environmental safety of CCA-treated wood relies on the extent of post-treatment storage fixation of CCA in wood prior to being utilized. A study on the comparative leachability (fixation) of CCA-treated refractory and permeable heartwoods of 3 Malaysian hardwoods subjected to different post-treatment storage (fixation) periods of up to 4 weeks, at 2 laboratory leachin...
A H H Wong, H C Lai, N P T Lim
Refinement of emission values for preserved wood in the ‘Storage Scenario’, for use in the environmental risk assessment of Wood Preservatives under the Biocidal Products Directive
2007 - IRG/WP 07-50244
The evaluation of an active substance or a biocidal product under the Biocidal Products Directive (BPD) requires that an environmental risk assessment is carried out. The risk assessment for wood preservatives includes a scenario for the treated wood in storage after treatment, in which the predicted environmental concentration (PEC) in soil, surface water and groundwater is calculated, using emis...
E F Baines
Comparative Laboratory Leaching Test Methods to Study Post-Treatment Storage Period Impacts on CCA Leachability and Fixation in Treated Kempas (Koompassia malaccensis) Heartwood
2007 - IRG/WP 07-20376
Three laboratory leaching test methods were compared to determine the effects of different post-treatment storage fixation periods on leachability/fixation of CCA components from treated kempas (Koompassia malaccensis) permeable heartwood. End-sealed test wood blocks of permeable were treated with CCA to target retention of 5.6 kg/m3, immediately stored to fix at ambient conditions for 0 and 48 ho...
A H H Wong, H C Lai
Run-off quality from sprinkled debarked logs and logs with bark from Picea abies and Pinus contorta
2007 - IRG/WP 07-50248
Storage of roundwood is necessary for efficient industrial production at sawmills and pulpmills. The need for wood storage becomes even more critical when large storm fellings create huge volumes of wood that is at risk for deterioration. In Scandinavia, the technique of sprinkling of water on roundwood is used to protect stored wood from fungal and insect infestation and drying during the summer....
M Jonsson
Riverbed Construction Technology using Thinned Timbers for Carbon Dioxide Sink in Korea
2010 - IRG/WP 10-50271
The Climatic Change Convention is a big burden in limiting the energy usage like the blood of economy. The certification standard about the carbon storage of timbers after harvesting them is expected to be an important role in setting the goal for future reduction of the green house gas(CO2). The extension of a timber's life span through its preservation is one of technologies for carbon sink...
Dong-heub Lee, Won-Joung Hwang
Mold Control for Treated Lumber in Block-Stack Storage Conditions
2012 - IRG/WP 12-30588
The mold development and control for freshly treated and block-stacked wood have been evaluated using a green house mold testing method. The results for the mold resistance of several commonly used water boron preservative treatment systems, such as ACQ, Copper Azole, and borates with and without inclusion of mold inhibitors are presented. The data suggest that the different preservative treatme...
L Jin, P Walcheski, A Preston
Migration of copper from copper naphthenate treated Douglas-fir poles during storage
2014 - IRG/WP 14-50302
Preservative migration from treated wood products has raised concerns among regulators, especially when the biocides move into surface waters. In most cases, chemical levels are well below the acceptable minimum level, but can become a concern if large quantities of treated wood are stored in one location. One such case would be a location where utility poles are stored for use in emergency repai...
C S Love, C M Freitag, J J Morrell
Some comments on durability testing of WPC according to EN 15534-1
2015 - IRG/WP 15-40695
The standard EN 15534-1 (2014) gives advice for broad characterization of WPC materials and products. It contains instructions for test procedures concerning different properties e.g. mechanical properties, thermal properties, as well as durability.
In this paper some WPC materials from the market were tested for their resistance against brown rot. Furthermore, the water uptake and bending prope...
S Bollmus, A Gellerich, H Militz
Effect of the Storage Time of Logs in Anti-Stain Treatment Effectiveness
2016 - IRG/WP 16-30683
Storage of green lumber, for 7 months, operationally treated with anti-stain products, depending on the storage time of the logs (10, 20 and 30 days) post harvesting allows to affirm that with increasing storage time of the logs, occurs a progressive increase in intensity, severity and types of fungi present in the logs. It is further noted, a significant increase in the percentage of sawn lumber ...
M A Peredo, C Barria
Fabrication and characterization of MicroPCMs filled wood-plastic composites: Effects of polyethylene glycol on melamine–formaldehyde shell material
2016 - IRG/WP 16-40728
Microencapsulated phase change materials (MicroPCMs) containing dodecanol were fabricated using melamine-formaldehyde (MF) or polyethylene glycol 200 modified melamine-formaldehyde (PMF) resin as the shell materials by in situ polymerization. Wood flour/high-density polyethylene (WF/HDPE) composites with MF shell MicroPCMs (MF-MicroPCMs) or PMF shell MicroPCMs (PMF-MicroPCMs) were prepared, respec...
Xi Guo, Jinzhen Cao
Decontamination of sludges, liquids and soils polluted by “class 1, 2 & 3a” and “temporary” wood treatment products from dipping tanks
2016 - IRG/WP 16-50315
Wood is one of the most widely used building materials as it is easy to find and process. As an organic material, time leads to a degradation of its substance, and even more so when it is exposed to pathogens such as fungi, bacteria and insects. In order to try and inhibit this phenomenon, several preservation treatments have been developed and applied thanks to the production of chemical biocides...
A Zaremski, E Wozniak, S Maman, C Zaremski, S Morel
Life cycle assessment of creosote treated wood and tall oil treated wood with focus on end-of-life
2016 - IRG/WP 16-50320
The use of creosote for protecting wood products in heavy-duty application outdoors has been common for many years, but stricter regulations have limited creosote’s use. Life cycle assessments (LCA) have shown that in some applications alternatives to creosote treated products do not have less environmental impacts. Searching for alternatives to creosote, tall-oil-based preservatives have been ...
L G F Tellnes, U Hundhausen
Premature adhesion failure of exterior wood coatings – The influence of substrate temperature at coating application and moisture accumulation during storage
2022 - IRG/WP 22-40937
The present study aimed at extending the knowledge about premature coating failures of industrially finished wood cladding. Two potential factors were studied: the influence of substrate temperature at coating application and moisture accumulation during storage on the adhesion of waterborne coating systems. In the first experiment, 4 batches of wood specimens were submitted to 4 different tempera...
U Hundhausen
Manipulation of the hierarchical wood structure for extended carbon storage in the built environment
2023 - IRG/WP 23-50381
The sustainable processing of trees into construction materials can act as carbon storage. Carbon storage in durable sustainable wooden construction material has cumulative effects and net gain in storage in the built environment that can be offset by net losses in forest carbon by cutting the tree. Carbon storage for an extended period plays an important role in the mitigation of CO2 emissions an...
T Singh, A Arpanaei, D Elustondo, Q Fu
Developing thermal-energy storage systems based on Kraft lignin-glyoxal and organic phase-change material modified wood
2024 - IRG/WP 24-30810
This study investigated the use of modified wood as a thermal-energy storage material through the integration of paraffin-based phase-change materials (PCMs). The objective was to evaluate the influence of Kraft lignin-glyoxal prepolymer on the properties of wood modified with PCMs. The implementation of the modified wood involved preparing PCM emulsions, synthesizing lignin-glyoxal prepolymer, an...
C-F Lin, O Karlsson, D Jones, D Sandberg