Properties of hot oil treated wood and the possible chemical reactions between wood and soybean oil during heat treatment
2005 - IRG/WP 05-40304
Thermal treatment with hot oil as the heating media based on the original idea from oil-heat treatment in Germany was investigated. The treatment was mainly carried out at 200ºC and 220ºC for 2 hours and 4 hours, and the wood species were mainly spruce and fir. This paper focuses on the difference between soybean oil and palm oil and the possible chemical reactions between wood and soybean oil. ...
Jieying Wang, P A Cooper
Some characteristics of Pinus radiata wood from trees subjected to resin extraction
1987 - IRG/WP 3403
35 year old Pinus radiata trees growing in La Puntilla (lat. 37° south, long. 72,4° west), Chile, were subjected to resin extraction 5 years ago. After harvesting them simultaneously with control trees of the same place and age, probes were taken from the bottom of each pole, at 3.4 m, 7.8 m and 11.4 m height. Analysis of ethanol/benzene extract, CCA salt penetration tests and sapstain and brown-rot development rate were performed. The extract content differed in both groups. In the ascendent sense it decreases in unextracted trees and increases in extracted. CCA salt penetration was deeper in treated trees than in untreated. Wood subjectect to resin extraction was less susceptible to sapstain development. No significant difference was detected in both groups in relation to the development of brown-rot.
M C Rose, J Navarrete, G Sandoval, A Bedoya, L Ortega, R Zurita
Modelling of PCP migration in the environment: Feeding the models with laboratory data
1993 - IRG/WP 93-50001-08
In 1989, Hydro-Québec began a study program on pentachlorophenol (PCP) to ensure safe use of the product at all stages. One of the aspects of the study is the creation of a predictive system for evaluating the behavior of PCP and oil migration from wood poles to the environment. This system comprises four mathematical models for predicting PCP and oil migration in and on the surface of the pole, ...
A Besner, P Tétreault, R Gilbert
Mold susceptibility of oriented strandboard made with extracted flakes
2008 - IRG/WP 08-40402
As part of a larger study on the manufacture of oriented strandboard (OSB) using hot-water-extracted flakes, the mold susceptibility of extracted-flake and un-extracted-flake OSB was assessed using the standard ‘mold box’ test. OSB made with extracted flakes was much less susceptible to mold. This suggests that the extraction of hemicelluloses and other carbohydrates from wood for the producti...
A M Taylor, O Hosseinaei, Siqun Wang
Investigation of temperature effect on fixation of Celcure preservative (ACC) in beech (Fagus orientalis)
2001 - IRG/WP 01-40200
In this research, the fixation speed of Celcure 2% (ACC) preservative salt, under temperature of 17°C, 27°C and 50°C, on intact and stained wood specimens of beech was investigated. For this purpose, blocks of wood with 5x5x7 cm dimensions were prepared and saturated with 2% ACC concentration by full-cell process. The specimens were put in three incubators at the above-mentioned temperatures. F...
A Karimi, M Ghorbani
Solvent extraction of CCA-C from out-of-service wood
1998 - IRG/WP 98-50107
Elimination of CCA from decommissioned wood prior to disposal is a major environmental issue. One approach is to extract CCA from treated wood, then reuse the 'clean' (may contain CCA, but below hazardous level) wood materials for manufacturing wood-based composites. In the present paper, we focus on effective leaching processes, selection of leaching agents and optimum leaching ...
K M F Kazi, P A Cooper
Durability of heat-treated wood
1999 - IRG/WP 99-40145
Heat-treated wood from the French process were laboratory tested against decay using agar block test and a modified soil block test. Water absorption, bending strength, lignin content and acid number were also determined to evaluate the effect of heat treatment. Heat treated samples exhibit a higher lignin content and a lower acid number compared to untreated control indicating the degradation of ...
D P Kamdem, A Pizzi, R Guyonnet, A Jermannaud
Natural durability transfer from sawmill residues of white cypress (Callitris glaucophylla). - Part 1: Optimisation of the extraction conditions
2000 - IRG/WP 00-30238
As the first phase of a large project aimed at recovering 'waste' durability components from sawmill residues of Callitris glaucophylla, several solvents and extraction methods were evaluated, initially in the laboratory and then at pilot industrial scale. Extracts were compared by crude total dissolved solids content, by chemical analysis using GC-MS and LC-MS, and by laboratory...
M J Kennedy, Hui Jiang, L M Stephens
Alternative technologies for wood wastes recycling - Part A: Supercritical extraction of PAH compounds from wood wastes
1998 - IRG/WP 98-50101-18 a
Alternative technologies have been investigated to detoxify treated wood. Two classes of organic compounds are studied. Creosote-treated wood are classified in France as dangerous wood wastes. A conventional incineration could be provided for these wood wastes but the cost of this elimination could be very high (> 2000 FFR/ton). For these reasons, we have tested two kinds of new processes as al...
L Schrive, C Perre, G Labat
Recovery of copper, chromium, and arsenic compounds from the waste preservative-treated wood
1991 - IRG/WP 3651
In Japan, about 40 percents of waste wood is incinerated and the residue is dumped into the landfill site. The waste preservative-treated wood, which is mixed in nontreated wood, is incinerated in the same way, too. However, it will cause the serious problems that the gases contained with high concentration arsenic compounds are discharged from the smokestacks of the incineration facilities and th...
A Honda, Y Kanjo, A Kimoto, K Koshii, S Kashiwazaki
A comparison of analytical techniques
1995 - IRG/WP 95-20061
This paper compares carefully-controlled weight retentions and analysis by XRF, ICP, combustion methods and a new extraction procedure for the new preservative, Copper(II) Dimethyldithiocarbamate (CDDC). Various experimental parameters such as particle size and drying conditions were investigated. In general, the correlations between and among the procedures are very high. The extraction-colorimet...
A C Gallacher, C R McIntyre, M H Freeman, D K Stokes, W B Smith
Aureobasidium or Hormonema? A Genetic Approach.
2004 - IRG/WP 04-10529
Aureobasidium pullulans is the main organism causing disfigurement of coatings on wood and the surface of exposed timber. This disfigurement of timber in-service is referred to as “bluestain in-service”. A. pullulans is also associated with the sapstaining of dead wood in the forest and in-service. A. pullulans is noted for its highly variable growth forms (polymorphisms). This variability pre...
M J Ray, D J Dickinson, M Buck
Investigation of CCA fixation in wood by sequential extraction. I Determination of CCA component fixation and preliminary extraction results
2002 - IRG/WP 02-50188
The fixation of CCA-C preservative was investigated in sapwood of red pine (Pinus resinosa Ait.), trembling aspen (Populus tremuloides Michx.) and red maple (Populus tremuloides Michx.) at target retentions of 4.0, 6.4, 9.6 and 30.0 kg/m3. Treated wood sawdust was water extracted at close time intervals during the fixation and analyzed for the contents of unfixed hexavalent chromium, total Cr, Cu ...
S Radivojevic, P A Cooper
Anti-fungal properties of pyrolytic oils derived from softwood bark
2000 - IRG/WP 00-30218
Thermal decomposition of balsam fir and white spruce mixed bark residues at 450°C and under vacuum (< 20 kPa abs.) results in high yields of pyroligneous liquors rich in phenolic content. This vacuum pyrolysis process has been scaled-up to a pyrolysis plant with a feed capacity of 3.5 t/h of softwood bark, which is the largest plant of this type in the world. The pyrolytic aqueous condensates ...
D Mourant, Dian-Qing Yang, Xiao Lu, C Roy
Proposal for a method aiming at the quantification of the impact of wood extraction in Life Cycle Assessment
1998 - IRG/WP 98-50113
Life Cycle Assessment has been accepted as an instrument for the assessment of the environmental impact of products. Characterisation factors for impact assessment of emissions from products have been established. To date no characterisation factor exists for the extraction of biotic resources, for example wood. Since the main disadvantage of using wood as a material lies in the extraction of reso...
P Esser, E Van der Voet
Effect of remediation on the release of copper, chromium, and arsenic from particleboard made from CCA treated wood
2001 - IRG/WP 01-50170
This study sought to determine the effect of remediation with oxalic acid (OA) extraction and Bacillus licheniformis fermentation on the release of copper, chromium, and arsenic from particleboard made from remediated wood particles and also investigates durability of the particleboard against white and brown- rot fungi. Particleboard samples were manufactured using untreated, CCA-treated, OA-extr...
S N Kartal, C A Clausen
The extraction of boron from treated wood for quantitative analysis: A comparison of procedures
1992 - IRG/WP 92-2414
The extraction of boron preservative from treated rubberwood and scots pine samples was compared using methods based on refluxing and extraction in 1N NaOH or distilled water at 80°C. The extract solutions were analysed by Inductively Coupled Plasma spectroscopy (ICP/AES). A simple extraction procedure based on immersion of wood samples of approximate dimension 2 x 1 x 1 cm³ in distilled water a...
R J Murphy, D J Dickinson, P W McCormack, M K Lung
Treatment and recycle of CCA hazardous waste
1993 - IRG/WP 93-50007
Chromated copper arsenate containing hazardous materials is generated from the manufacture, treatment of the wood, and from the wood itself, after its life cycle. Laboratory treating of these wastes has resulted in materials suitable for recycle or disposal as non-hazardous residues. The extraction, by both acidic and ammoniacal routes, of CCA production and treating plant waste materials has been...
E A Pasek, C R McIntyre
Quantitative Determination of Cyproconazole in Wood treated with Tanalith CY
2007 - IRG/WP 07-20369
The HPLC method has been widely applied to quantitative determination of cyproconazole in preservative solutions. However, HPLC assay has not been successfully employed to determine cyproconazole content in treated wood. Some extractives from treated wood hinder cyproconazole determination because they have a similar retention time to that of cyproconazole on an HPLC chromatogram. In addition, ...
I Momohara, T Miyauchi, M Mori
Rapid Microwave-Assisted Acid Extraction of Metals from Chromated Copper Arsenate (CCA)-Treated Southern Pine Wood
2009 - IRG/WP 09-50262
The effects of acid concentration, reaction time, and temperature in a microwave reactor on recovery of CCA-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from chromated copper arsenate (CCA)-treated southern pine wood samples with three different acids (i.e., acetic acid, oxalic acid, and phosphoric acid) was investigated using in microwave reactor. Oxalic acid wa...
Bin Yu, Chung Y Hse, T F Shupe
Factors affecting sodium hypochlorite extraction of CCA preservative components from out of service treated wood for recycling
2009 - IRG/WP 09-50263
Significant amounts of chromated copper arsenate (CCA) treated wood products such as utility poles and residential constructions remain in service. There is an increasing public concern about environmental contamination from CCA treated wood when it is removed from service for reuse or recycling, placed in landfills or burned in commercial incinerators. In this paper, we investigate the effects of...
E D Gezer, P A Cooper
Microwave-Assisted Organic Acids Extraction of Chromate Copper Arsenate (CCA)-Treated Southern Pine
2010 - IRG/WP 10-50267
The extraction effects of acid concentration, reaction time and temperature in a microwave reactor on recovery of CCA-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from chromated copper arsenate (CCA)-treated southern pine wood samples with two different organic acids (i.e., acetic acid and oxalic acid) was investigated using a microwave reactor. Oxalic acid was e...
Bin Yu, Chung Y Hse, T F Shupe
Investigating extraction of bifenthrin from composite wood products
2011 - IRG/WP 11-20467
Bifenthrin is added to resin prior to lay-up of plywood and laminated veneer lumber to provide termite protection. Analysis of this chemical in resins can be challenging. The potential for using ground wood in place of sawn material to recover bifenthrin was investigated using laminated veneer lumber composed of Douglas-fir veneers analyzed by three laboratories. Although the results differed amo...
J J Morrell, L Bell, J Norton, C Shaw
Extraction and analysis of DNA from green and seasoned timber as basic methods for determination of wood species and origin
2013 - IRG/WP 13-20523
Against the background of the European timber trade regulation EUTR, commenced to law by March 2013, the determination of wood species and tracing of its origin is getting a great importance. A promising approach for establishing fast and reliable tracking systems for wood products is DNA analysis. A critical point is the extraction of analysable DNA from the wood and its lignified cell walls. Thu...
K Jacobs, H Mende, W Scheiding
Removal of nano- and micronized-copper from treated wood by chelating agents
2013 - IRG/WP 13-50294
Micronized and nano-copper (Cu)-based and arsenic and chromium-free systems have received much attention for wood protection in recent years. Because they have different fixation, and micro-distribution properties, such copper systems may be more or less subject to release using known remediation methods than soluble forms of Cu. This study evaluated Cu recovery from wood treated with micronized- ...
S N Kartal, E Terzi, B Woodward, C A Clausen, S T Lebow