Sawn timber of fir (Abies alba Mill.) - Treatability and usability for the Hazard Classes 3 and 4
1999 - IRG/WP 99-40147
Within a national research project, tests on the treatability on sawn timber of fir (Abies alba Mill.) in oscillation pressure, vacuum pressure and double-vacuum processes have been worked out with 95 trunks taken from 3 different altitude levels (up to a height of 590 metres, 600 to 990 metres and over 1000 metres) and from 4 different regions of Switzerland. As the treatability of round wood can...
E Graf, T Bör
Reduction of kiln brown stain in radiata pine lumber after log fumigation with methyl bromide
1997 - IRG/WP 97-30129
Methyl bromide fumigation of freshly felled radiata pine log sections effectively killed living cells in parenchyma to at least 75mm into sapwood. Lumber cut from logs (fumigated and control) stored 1 month outdoors (dry) showed slightly reduced brown stain when kiln dried at conventional temperatures. A more dramatic reduction and elimination of brown stain was noted in lumber cut from fumigated ...
E Schmidt, M E Hedley, D R Page, D Cross
The performance in the sea of seven experimental piles after sixteen years at Port Douglas, North Queensland
1989 - IRG/WP 4151
After 16 years at Port Douglas, two double-treated Pinus radiata piles were in excellent condition, a CCA-treated Pinus elliottii pile was in good condition other than for a confined streak of teredinid attack, while two CCA-treated and two untreated turpentine piles were moderately to severely attacked by Sphaeroma in the tidal zone. The marine borers collected were Sphaeroma terebrans, Martesia ...
L J Cookson, J E Barnacle, C N McEvoy
Estimation of the impregnation degree of pine wood by the distribution analysis of active ions concentration in the cross-section
1999 - IRG/WP 99-20174
Samples in the form of pine wood rollers of diversified moisture content of ca. 50, 28 and 12% were impregnated with a water solution of the mixture type CCB with the use of the full-cell process. Moisture content was determined in individual layers from the girth to the pith. In the same way the concentrations of copper and chromium ions with the use of the spectrophotometric method and recalcula...
K Lutomski, B Mazela
Chemical and biological investigations of double-vacuum treated windows after 5 years in service
1983 - IRG/WP 3219
In 1980 The Swedish Wood Preservation Institute initiated an investigation to study the degradation of TBTO and possible fungal attack in double-vacuum treated window joinery in service during 5 years. A hospital in Gothenburg was chosen that was built during 1969 to 1976. Both untreated and double-vacuum treated windows of Pinus sylvestris were used. A brown alkyl oil type paint (Nordsjö system ...
J Jermer, M-L Edlund, B Henningsson, W Hintze, S V Ohlsson
A new preservative - A double-edged sword
1990 - IRG/WP 3573
Increasing environmental pressures on the use of pesticides throughout the world will impact more on the use of all wood preservatives. In particular the use of traditional wood preservatives and methods of application are under close scrutiny. The industry is responding to the challenge of developing alternative products and systems but faces great problems due to the excellent performance and sa...
M Connell, J A Cornfield, G R Williams
Future insecticidal treatments for wood products
1980 - IRG/WP 3140
Protective measures involving chemical treatment of wood use only a narrow range of toxic materials which are divisible into two groups, (i) those that are water-soluble, (ii) those that are soluble only in organic solvents. It is generally true to say that, as far as protection against insects is concerned, the former are stomach poisons while the latter are largely (though not exclusively) conta...
D J Cross
Chemical and biological investigations of double-vacuum treated windows after 7½ years in service
1985 - IRG/WP 3339
Earlier investigations of double-vacuum treated windows after five years in service have shown that tributyltin oxide (TBTO) degrades to di- and monobutyltin compounds and that the resistance of the wood against decay decreases. An investigation 2.5 years later of the same windows shows that the degradation of TBTO proceeds fast. After 7.5 years in service only 15-35% of the remaining organotin co...
M-L Edlund, J Jermer, B Henningsson, W Hintze
Effectiveness of wood preservatives and treatments against marine borers in Philippine waters
1976 - IRG/WP 416
A 5-year exposure test was conducted on the effectiveness of wood preservatives and treatments against marine borers in Philippine waters. Air-dried heartwood samples of apitong (Dipterocarpus grandiflorus) 76.2 x 88.9 x 609.6 mm³ (3 x 3.5 x 24 in³) in size were pressure treated with coal tar creosote and two types of CCA (copper/chrome/arsenic) and CuCZA (copperized chromated zinc arsenate) wat...
F R Siriban, M G Laxamana, P G Mata
Moisture content and other tested values in. Double layer tests of different size in Lithuania and Germany
2004 - IRG/WP 04-20299
The paper presents measurement results of moisture content and the analysis of durability trial of double layer wood in variants of varying size, conducted in Girionys, Kaunas distr., Lithuania and in Hamburg, Germany. In this trial 3 sample sets of varying size, containing 25, 50 and 100 specimens, are used. The aim of this trial is to ascertain an optimal number of test specimens. The dynamics o...
J Saladis, A O Rapp
The effects of accelerated drying of green Pinus radiata on its attractiveness to Anobium punctatum as an egg-laying site
1984 - IRG/WP 1199
The methods and results are given for a series of experiments in drying Pinus radiata sapwood under a variety of conditions, then exposing the material to Anobium punctatum egg-laying. The results showed very clearly that the attractiveness of the wood to gravid females was drastically reduced when dried from green at temperatures much above 35°C. Both simple oven drying and steam kilning produce...
D J Cross
A novel technique for comparative toxicity studies of potential insecticidal wood preservatives
1983 - IRG/WP 2198
For some years now a device has been under development at the New Zealand Forest Research Institute, the purpose of which is to study the effects of sub-lethal amounts of stomach poisons (but also of fumigants and contact active materials) on the co-ordinative abilities of a cerambycid larva. This insect is Prionoplus reticularis - indigenous to New Zealand its larvae feed in decaying logs and are...
D J Cross
The natural durability of wood in different use classes - PART II
2006 - IRG/WP 06-10598
The natural durability of important European wood species has been tested on 3970 speci¬mens in field trials. The wood was exposed at five test sites in Germany with different climates, at each site in European use class 4 and 3 (with and without soil contact). Within European use class 3 three different expositions were tested: vertical with sheltered end grain, vertical unsheltered and horizont...
A O Rapp, U Augusta, K Brandt
Service life prediction of wooden components – Part 1: Determination of dose-response functions for above ground decay
2010 - IRG/WP 10-20439
Scots pine sapwood (Pinus sylvestris L.) and Douglas fir heartwood (Pseudotsuga menziesii Franco) specimens were exposed in double layer field trials at 24 different European test sites under different exposure conditions (in total 28 test sets). The material climate in terms of wood moisture content (MC) and wood temperature was automatically recorded over a period of up to eight years and compar...
C Brischke, A O Rapp
Impact of climate change on wood deterioration - Challenges and solutions for cultural heritage
2010 - IRG/WP 10-20441
Deterioration of wood in cultural assets follows the same physiological mechanisms as in modern structures. Therefore rules and data for prediction of service life derived from old wooden structures can be used to model the service life of recent wooden structures and vice versa. The latter is done in this paper: From experimental test set ups in the field spread over Europe, climatic data, wood t...
C Brischke, A O Rapp, M Hasan, R Despot
Wet and dry adhesion of coatings on modified and unmodified wood: comparison of the pull-off test and the cross-cut test
2010 - IRG/WP 10-40524
The objective of this paper is to study the influence of several types of modification (acetylation, furfurylation, thermal modification) on coatings adhesion and to compare two methods of assessing the adhesion: the cross-cut test and the pull-off test both tested in dry and wet conditions. The study also investigates the effect of other parameters of the wood substrates on adhesion like the ring...
L Podgorski, G Grüll, M Truskaller, J D Lanvin, V Georges, S Bollmus
Natural durability of wood tested in different environments in Northern Europe
2011 - IRG/WP 11-10747
Moisture is often recognised as a key factor regarding the long time performance of wooden products, and one of the main challenges for timber products is to predict accurate service life in use class 3 (not covered above ground) and use class 4 (in soil or fresh water contact). A range of durability classification studies have been performed both in field and laboratory. But for several wood spec...
P O Flæte, G Alfredsen, F G Evans
Wet and dry adhesion of coatings on modified and unmodified wood: influence of 18 months of natural weathering on the pull-off test and cross-cut test results
2011 - IRG/WP 11-40569
The objective of this paper is to study the influence of several types of modification (acetylation, furfurylation, heat treatment) on coatings adhesion after 18 months of natural weathering according to EN 927-3 in Vienna (Austria).
The paper compares two methods for assessing the adhesion: the cross-cut test (EN ISO 2409) which is the conventional method used and recommended in EN 927-3 and th...
L Podgorski, G Grüll, M Truskaller, J D Lanvin, S Bollmus
Plywood under the scanner: linking moisture dynamics and 3D structure
2012 - IRG/WP 12-20491
Plywood is highly esteemed as a construction material. Yet, the influence of moisture on both strength and durability are important factors. Especially the dynamics of moisture desorption and absorption should be taken into account when assessing the quality of a panel, which is a fact for all panel materials. This paper therefore focuses on the monitoring of the moisture dynamics of plywood subje...
J Van den Bulcke, I De Windt, N Defoirdt, J Van Acker
Moisture performance based wood durability testing
2012 - IRG/WP 12-20495
In the frame of a scientific cooperation within the Swedish research program ‘WoodBuild’ comparative field and laboratory durability studies have been carried out by the Technical Research Institute of Sweden SP and Leibniz University Hannover. One objective was to improve test methods as well as evaluation systems in order to facilitate the use of (field) testing for service life prediction. ...
L Meyer, C Brischke, A Pilgård
Durability of Furfurylated Wood – Results from Laboratory and Field Tests in the Ecobinders project
2012 - IRG/WP 12-40602
Within the EU project Ecobinders, laboratory tests were performed with furfurylated wood produced in semi-industrial scale in the factory of Kebony ASA. Field trials in Horizontal double layer decks and in-ground of transmission poles were also started. Four wood species, Southern yellow pine (SYP), maple, beech and aspen were treated to two treatment levels by using two impregnating liquids with ...
M Westin
A critical view on early indicators for above ground field performance of wood
2013 - IRG/WP 13-20509
Above ground field tests are quite often a balancing act between the provision of realistic test conditions, reliable statistics, and acceptable long test durations. Within this study we therefore reviewed 543 data sets from above ground field tests performed at 36 different test sites in 8 countries in Australia and Europe. The main objective was to investigate possible correlations between early...
C Brischke, L Meyer, G Alfredsen, P-O Flæte, L Francis, M Hansson, P Larsson Brelid, J Jermer
Report on COST E37 Round Robin Tests – Comparison of results from laboratory and field tests
2013 - IRG/WP 13-20535
A round robin involving 15 European participants was set up in 2006. The round robin consists of both a field test according to the double layer test method and a laboratory test with two different preconditioning methods. When comparing EN 84 preconditioning (two weeks water leaching) with natural preconditioning (1 year in field, above ground) according to CEN/TS 15397, no significant difference...
M Westin, E Conti, J Creemers, P-O Flæte, A Gellerich, I Irbe, M Klamer, B Mazela, E Melcher, R Möller, L Nunes, S Palanti, L Reinprecht, E Suttie, H Viitanen
The durability of manufactured structural building materials
2016 - IRG/WP 16-40718
The projected market potential for Engineered Wood Products such as CLT (cross laminated timber) is very positive however, potential prolonged rain leakage or moisture exposure during construction and in-service could pose considerable concern for its durability and reputation. This research was conducted to assess the decay resistance of CLT and OSB (oriented strand board) in an accelerated trial...
T Singh, D Page
10 year Report on COST E37 Round Robin Tests – Comparison of results from laboratory and field tests
2017 - IRG/WP 17-30718
A round robin involving 15 European participants was set up in 2006. The round robin consisted of both a field test according to the double layer test method and a laboratory test with two different preconditioning methods. The laboratory test results were reported in an earlier IRG paper (IRG/WP13-20535) but are included also in this paper in order to facilitate the comparison with the field test...
M Westin, E Conti, J Creemers, P-O Flæte, A Gellerich, I Irbe, M Klamer, E Melcher, R Moeller, L Nunes, S Palanti, L Reinprecht, E Suttie, H Viitanen