Material properties of acetylated beech plywood
2008 - IRG/WP 08-40425
The effect of acetylation process on dimensional stability and mechanical properties of plywood made by Oriental beech layers (Fagus orientalis Lipsky) were studied. The layers cut into sizes of 200×200×2 mm and acetylated in 120°C for 30 and 60 min.
Thickness swelling (TS%), water absorption (WA%) and anti-swelling¬ efficiency (ASE%) of specimens were measured. Mechanical properties (MOE, MO...
A Talaei
Improving the Dimensional Stability and Fire Resistance of OSB by Roller-Coating Panels with UV-Curable Finishes
2008 - IRG/WP 08-40434
Oriented strandboard was sanded and roller-coated with UV-cured finishes. The effects of these treatments on the surface roughness, dimensional stability and fire resistance of OSB were assessed. Sanding reduced the average roughness of OSB, but it had a smaller effect on maximum roughness because sanded boards still contained surface voids between some strands. Sanded boards absorbed less than ha...
P D Evans, I Cullis
Dimensional Stability of Nine Tropical Hardwoods from Cameroon
2009 - IRG/WP 09-10687
This study investigated the swelling behavior, rate of swelling and dimensional stability of nine tropical hardwood species from Cameroon, namely ayous (T. scleroxylon), bilinga (N. diderrichii), bubinga (G. tessmannii), iroko (C. excelsa), Makore (M. heckelii), moabi (B. toxisperma), movingui (D. benthamianus), teak (T. grandis) and zingana (M. brazzavillensis). Continuous swelling was monitored ...
S R Shukla, D P Kamdem
Evaluation of Water Repellency of Treated Wood Using Several Alternative Methods
2009 - IRG/WP 09-20419
In this study, the results of water repellency testing using a digital swellometer method for water-borne organic-preservative systems with water repellent additives are reported. The findings suggest that the traditional method of using matched untreated controls as a reference developed from historic solvent-based treatments for determination anti-swelling efficacy (ASE) may underestimate the a...
L Jin, A F Preston
Weathering of Wood Modified with the N-Methylol Compound 1,3‑dimethylol-4,5-dihydroxyethyleneurea (DMDHEU)
2009 - IRG/WP 09-40467
Scots pine (Pinus sylvestris L.) sapwood boards were treated with a methylated 1,3‑dimethylol-4,5-dihydroxyethyleneurea (mDMDHEU) causing weight gains of approx. 25% and exposed to weathering for 18 months. Compared to untreated boards, treatment with mDMDHEU reduced surface discoloration mainly caused by staining fungi. Boards treated with mDMDHEU exhibited clearly lower moisture content th...
C Mai, Yanjun Xie, A Krause, K Urban, P D Evans, K Richter, H Militz
Properties of thermally modified wood of Eucalyptus globulus from Spanish plantations
2009 - IRG/WP 09-40469
This article provides the results of a study about the properties of thermally modified wood of the Southern blue gum (Eucalyptus globulus L.) from Spanish plantations. Although this specie is mainly used for chipping to obtain boards and paper pulp, its high mechanical and strength properties provide great potential for structural use or different solid wood products. A comparison of the properti...
Ó González Prieto, M C Touza
The effect of chemical changes on the wood-moisture relationships in thermally-modified wood
2009 - IRG/WP 09-40473
Small specimens of three wood species were thermally modified following twenty schedules in the 190-245°C temperature range for treatment times between 0.3 and 16 h. Five wood-moisture relations were subsequently determined, namely: anti-swelling efficiency (ASE), movement, hygroscopicity (adsorption and desorption), transversal swelling (radial and tangential directions), and equilibrium moistur...
M M González-Peña, M D C Hale
Effect of preservative treatment on dimensional stability of plywood made of treated simul (Bombax ceiba) veneer
2012 - IRG/WP 12-40575
The dimensional stability such as thickness swelling and water absorption of plywood made of treated simul (Bombax ceiba) veneers were investigated after 2 hours and 24 hours soaking under water. The veneers were treated with hot water and cold water solution of borax-boric acid (1:1), neem leaves and mahogany seeds of different concentration (1:10, 1:20, and 1:40) at different treatment duration....
K Akhter, M Mahabubur Rahaman, A Ara
Effects of nano-wollastonite impregnation on fire resistance and dimensional stability of Poplar wood
2012 - IRG/WP 12-40595
The fire-retardant properties of Nano-Wollastonite (NW) in poplar wood (Populus nigra) were determined in this study. Some physical properties such as water absorption, volumetric swelling and Anti-Swelling Efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 standard for the fire-retarding properties, and ASTM D4446-2002 standard for the physical properties. Imp...
A Karimi, A Haghighi Poshtir, H Reza Taghiyari, Y Hamzeh, A Akbar Enayati
Improvement of the biological performance and dimensional stability of two tropical woods by thermal modification
2012 - IRG/WP 12-40605
Pink cedar wood and rubberwood were thermally modified at 230°C in air for 4 h or for 8 h, and then subjected to bending, compression and hardness tests to evaluate the effect of the treatment on these mechanical properties. The biological performance of the modified wood was also determined, according to EN113, and the dimensional stability measured by means of the anti-swelling efficiency. The ...
M M González-Peña
The effect of nanozycosil on the water absorption and dimensional stability of Beech wood
2012 - IRG/WP 12-40606
Zycosil is a clear penetrating water repellent. This product works by penetrating into the substrate and modifying the surface tension to inhibit water intrusion. Beech wood (Fagus orientalis) was modified by treatment with nanozycosil. Then water absorption and dimensional stability in terms of volumetric swelling percent and anti-swelling efficiency were determined and found to be improved on t...
M Ghorbani, F Bavaneghi
Differences between heat treated Pinus pinaster heartwood and sapwood
2012 - IRG/WP 12-40617
Heat treatment is a well known process to improve the durability and dimensional stability of less noble woods. The treatment can be applied for heartwood unlike the traditional treatments based on impregnation due to the difficulty of impregnating heartwood.
Pure sapwood and pure heartwood samples were treated in an oven at 190ºC and 200ºC for 2h, 4h and 6h. Dimensional stability, measured a...
B Esteves, L Nunes, I Domingos, H Pereira
Improving dimensional stability of thermally treated wood by secondary modification – potential and limitations
2014 - IRG/WP 14-40664
The potential of treating thermally modified wood with melamine resin to improve the dimensional stabilization is tested in this research. Two different boards of poplar (Populus ssp.) were cut into two halves. One half of each board was thermally modified (T1 and T2) in a commercial process, the other half was used as untreated reference material. The material was thermally modified using the vac...
G Behr, K-C Mahnert, S Bollmus, H Militz
Leachability and Dimensional Stability of Nanosilver-Steamed Densified Poplar
2014 - IRG/WP 14-40684
This study was aimed to investigate leachability and dimensional stability of nanosilver impregnated poplar (Popolus alba), steamed before hot compression. Wood samples were impregnated with nanosilver suspension (200 and 400 ppm) under pressure of 4 bar for 20 minutes. Steam treatment was carried out at 150°C for 2 hours. Then samples were compressed (33%) radially in a hot press at 170°C for 3...
G Rassam, A Talaei, A Ahmadi
Effect of a wood stabilizer on checking of red oak log sections
2015 - IRG/WP 15-30664
Abstract: Reduced check development and dimensional stability can be important attributes in wood products used for decorative applications. The potential for using a silane-based stabilizer product to reduce checking was assessed on red oak stem and log sections. Pressure treatment produced the largest uptakes, although the levels suggested that the solution had failed to completely penetrate th...
C S Love, J J Morrell
Investigation of Dimensional Stability and Coating Performance of Different Heat-Treated Poplar Wood Before and After Accelerated Aging
2015 - IRG/WP 15-40702
In this investigation, coating performance of heat-treated poplar wood (Populus tremuloioes) in different environments, before and after accelerated aging was studied. Specimens with 150×100×20 mm and 20×20×20 mm in dimensions were prepared. Heat treatments were performed in air, steam and linseed oil media. Specimens were coated by alkyd based stain. Adhesion strength before and after aging, ...
A Talaei, D Ansari Movahed, G Rassam
The effect of acetylation on physical properties of beech (Fagus orientalis) and Alder (Alnus subcordata) wood
2016 - IRG/WP 16-40759
In this study the effect of acetylation on physical properties such as water absorption, volumetric swelling and anti-shrink efficiency (ASE) of beech and alder were investigated. After 24 hours soaking in acetic anhydride, in order to achieving two surface of weight gains, acetylated samples were heated in oven at 120 0C for 90 and 360 minutes. Then water absorption and dimensional stability in...
M Akhtari, M Arefkhani
Accelerated weathering and fungal resistance of wood modified with isopropenyl acetate
2016 - IRG/WP 16-40764
Chemical modification of Rubberwood (Heveabrasiliensis Müll.Arg) with isopropenyl acetate (IPA) in presence of anhydrous aluminum chloride and iodine as catalysts was carried out. Modified wood surfaces were exposed to UV light source in an accelerated weathering tester to evaluate UV resistance. Anti-swelling efficiency (ASE) and fungal resistance of modified wood were also evaluated. Modified w...
G B Nagarajappa, K K Pandey
Influence of organosilicon compounds and nanocellulose treatment on dimensional stability of waterlogged elm wood
2017 - IRG/WP 17-10891
Commonly used agents for waterlogged wood consolidation (including the most popular polyethylene glycol) have proved ineffective and even dangerous to the preserved objects, jeopardising their integrity. Finding new, effective alternatives for safe preservation of wooden cultural heritage is therefore of key importance. The future conservation agents should, first and foremost, provide the integri...
M Broda, B Mazela, I Dąbek, A Dutkiewicz, H Maciejewski, R Markiewicz, M Grzeszkowiak, S Jurga
Three-Dimensional Digital Image Correlation of Strains in Profiled Wood Decking Exposed to Wetting & Drying
2017 - IRG/WP 17-20611
We use three dimensional digital image correlation to measure the strains that develop at the surface of profiled radiata pine (Pinus radiata D. Don) deck boards subjected to a wetting and drying cycle. We hypothesise that surface profiling will change the pattern of strain distribution at the surface of deck boards by concentrating stresses at the base of profile grooves. Five groups of three deck board samples were produced from five different pieces of machine stress-graded radiata pine wood. Two wavy profiles, ribble or ripple, were tested. Flat unprofiled boards acted a control. Each board was fixed to a rigid frame and subjected to a wetting and drying cycle. Full field surface strain data was collected using 3D digital image correlation. Strains varied across the surface of both flat and profiled boards. Profiling changed surface strain patterns; strain maxima and minima developed in the profile ridges and grooves during wetting, respectively, but this pattern of strains reversed during drying. Such a pronounced reversal of strains was not observed when flat boards were exposed to wetting and drying, although there was a shift towards negative strains when flat boards were dried. We conclude that profiling changes surface strain distribution in deck boards exposed to wetting and drying, and causes high strains to develop in the grooves of profiled boards. These findings help explain why checks in profiled deck boards are mainly confined to profile grooves where they are difficult to see, and the success of profiling at reducing the negative effects of checking on the appearance of wood decking.
J Mallet, S Kalyanasundaram, P D Evansa
Dimensional Stability of Melamine Formaldehyde-Treated Southern Pine
2017 - IRG/WP 17-40774
The objective of this preliminary study was to evaluate the influence of different levels of melamine formaldehyde (MF) and curing cycle on the dimensional properties of southern pine. Thirty samples for each combination of treatment and curing regimen plus untreated controls and controls subjected to the same curing regimen were tested. Shrinkage/swelling coefficients showed that up to 60% ASE c...
H M Barnes, L S Sites, T S F A França, M G Sanders, F J N França
Moisture behaviour and biological durability of high performance flax fibre reinforced composites
2017 - IRG/WP 17-40803
For natural fibre composites in structural and load bearing applications long reinforcing fibres are required. Therefore, much research is performed on flax fibre reinforced composites to optimize them for high performance use. In most cases such research focuses on the mechanical properties, yet the assessment of moisture behaviour, dimensional stability and biological durability is an important ...
N Defoirdt, J Van den Bulcke, F Bensadoun, J Ivens, I Verpoest, J Van Acker
Influence of hygro-thermal treatment temperature and duration on dimensional stabilisation of wood modified with poly(butylene succinate)
2017 - IRG/WP 17-40813
To improve wood properties, especially dimensional stability, a treatment based on poly(butylene succinate) oligomers (OBS) was experimented. After impregnation in wood, a further hygro-thermal treatment (HTT) was carried out in a pressurized reactor at 100% relative humidity (RH) at differing temperatures for differing durations. The aim of HTT is to induce partial swelling of wood cell walls so ...
C Grosse, M Noël, L Rautkari, P Gérardin
Markers of quality in self-bonded beech boards
2017 - IRG/WP 17-40820
A self-bonding phenomenon takes place when five layers of beech (Fagus Sylvatica L.) veneers are pressed at temperatures higher than 200ºC. If the pressing temperature between veneer surfaces reaches at least 225ºC during pressing and if the pressure applied is optimal, water-resistant bonds are formed between veneers. This study investigates the relation of thickness reduction (marker of compre...
C Cristescu, D Sandberg, O Karlsson
Multiscale modification on water resistance and dimensional stability of Populus cathayana by alkali lignin combined with heat treatment
2018 - IRG/WP 18-40826
The aim of this study was to enhance the water resistance and dimensional stability of fast growing wood by alkali lignin combined with heat treatment. Poplar (Populus cathayana) samples were first impregnated with alkali lignin solution and then subjected to heat treatment at 140, 160, and 180°C respectively for 2h. Properties of leachability, moisture adsorption and water absorption, contact an...
H Zhou, J Li, E Ma