Copper and chromium leaching from wood impregnated with chromium-copper containing preservatives: Results of different studies
2014 - IRG/WP 14-50300
Copper and chromium based wood preservatives remained one of the most important ingredients for wood protection solutions for protection of wood in demanding applications all-over the world. Leaching of heavy metals from treated wood is important from two different aspects; firstly from performance point of view, and secondly from environmental issues. However, the importance of these studies is i...
M Humar, N Thaler, E Melcher
The durability of natural and thermomodified black poplar wood and Scots pine sapwood after two years of external exposition
2016 - IRG/WP 16-40730
Natural biological durability of many European wood species is considered to be relatively small, particularly in a ground contact conditions. This is due to the exposure of the wood to the range of biological and atmospheric destructive factors. This may to limit the scope of application of the wood of these species, particularly in construction. The biocides are often used for wood protection in...
A Fojutowski, A Kropacz, A Noskowiak
Influence of pressure phase impregnation time on the uptake and distribution of wood preservatives in Scots pine material of diverse treatability
2016 - IRG/WP 16-40752
In spite of the general opinion that Scots pine sapwood is easy to impregnate considerable variations in treatability are reported. In order to study impregnation results of diverse Scots pine sapwood treated with increasing process times, Scots pine sapwood from two different predefined treatability groups was impregnated. A copper solution was used as impregnation agent in ten different vacuum p...
K Zimmer, B Kerfriden
Penetration behaviour of different hydrophobic carrier substances for oily wood preservatives in Beech and Scots pine sapwood
2017 - IRG/WP 17-40804
The use of creosote as a wood preservative has a long history. Current areas of application are railway sleepers, transmission poles, timber bridges and marine applications. If the approval for creosote will not be prolonged, alternative wood preservatives will be needed. As the penetration behaviour after pressure impregnation of different alternative oily products in this fields of application i...
M Starck, A Gellerich, H Militz
Decay resistance of beams made from thermally modified Scots pine and Norway spruce after 6 years’ exposure in ground contact
2017 - IRG/WP 17-40806
In the present study the resistance of beams treated by ThermoWood® process was studied in ground contact and the results given are based on a “modified” EN 252 test. After six years’ exposure clear differences were found between untreated Scots pine and Norway spruce beams and treated ones. In all cases thermal modification improved the performance. Thermally modified pine heartwood showed...
S Metsä-Kortelainen, H Viitanen
Multivariate modeling of mould growth in relation to extractives in dried Scots pine sapwood
2017 - IRG/WP 17-20629
Influence of extractives on mould growth on Scots pine sapwood dried in air or in kiln was studied. Boards were sprayed with water mixtures of spores of the fungal species Penicillium sp., Aspergillus sp., Mucor sp., Paecilomyces sp., Trichoderma sp., treated at a temperature of 22ºC at 90% RH, classified into a percentage of covered area. Acetone and water extracts were isolated and analyzed for...
O Karlsson, O Myronycheva, M Sehlstedt-Persson, M Öhman, D Sandberg
Effect of long-term immersion in fresh and salt water on mould growth on Scots pine (Pinus Sylvestris L.) wood
2020 - IRG/WP 20-10962
Wood exposed outdoors will eventually be degraded by fungi, depending on exposure and material characteristics. Numerous wooden constructions in the Røros municipality have existed since the 17th century, but wood used in recent repairs have decayed faster than expected. Before 1970 timber was mainly transported by log driving or rafting, and the logs were immersed in water for longer or shorter ...
M Sand Austigard, J Mattsson
Profiling fungal degradation of Scots pine sapwood by short wave infrared hyperspectral image analysis
2020 - IRG/WP 20-20667
Hyperspectral image analysis of Scots pine sapwood wood affected by decay fungi has been carried out as part of a Ph.D. thesis within the project Remote Inspection of Wooden Utility Poles (RIWUP).
In a lab experiment, Petri-dishes with Scots pine sapwood samples on malt agar medium were infected with two types of decay fungi, a brown rot and a white rot. The wood samples were scanned with a HySpe...
A Jochemsen, G Alfredsen, I Burud
New wood-modification process based on grafted urethane groups: Durability of carbamamylated Scots pine (Pinus sylvestris L.) wood
2023 - IRG/WP 23-40974
Substituting commonly used toxic preservatives with wood modification treatments can make the wood material less prone to water and moisture uptake. This approach favours a more sustainable protection of wood against biodegradation. In this study, Scots pine sapwood was full-cell impregnated with an aqueous solution of urea (30%), dried at 40°C for 24h, and subsequently heat-treated at 150°C for...
C-F Lin, O Myronycheva, O Karlsson, D Jones, D Sandberg
Field trial with poles of Scots pine treated with six different creosotes
1996 - IRG/WP 96-30115
In the middle of the 50's field trials with creosote-treated poles were started in France, Germany and Sweden. The trials were initiated by WEI (Western-European Institute for Wood Preservation). Six different creosotes were used and 40 poles per creosote were installed at each test field. Results after 39 years of exposure in Simlangsdalen, Sweden are reported. Poles treated with a heavy...
Ö Bergman
Strength loss associated with steam conditioning and boron treatment of radiata pine framing
1987 - IRG/WP 3438
The combined effect of included defects and wood moisture content on the strength loss of second rotation radiata pine framing following conventional steam conditioning is investigated. The green Modulus of Elasticity (MOE) is reduced by approximately 13% after steaming. When dried after steaming, however, neither the MOE nor MOR is significantly different from unsteamed dried controls....
M J Collins, P Vinden
Screening potential preservatives against stain and mould fungi on pine timber in Zimbabwe
1995 - IRG/WP 95-30063
The search for environmentally and toxicologically safer chemicals for use in the timber preservative industry against stain and mould fungi has been intensified during the past few years. Results of field tests with two chemicals previously evaluated in the laboratory are presented. The conventional sodium pentachlorophenate was the more efficacious chemical against stain and mould fungi, providi...
A J Masuka
Dimensional stability and decay resistance of hot-melt self-bonded particleboard by surface benzylated pine chips
1991 - IRG/WP 3652
Akamatsu (Pinus densiflora Sieb. et Zucc: Japanese red pine) particles were pretreated with 40% NaOH solution and benzylated with benzyl chloride, and the surface of particle was converted into meltable materials. Hot-melt self bonded particleboard having smooth and high glossiness surface was prepared by hot pressing at 150°C and 1.96 MPa without using any conventional adhesives. Dimensional sta...
M Kiguchi, K Yamamoto
Types of decay observed in CCA-treated pine posts in horticultural situations in New Zealand
1984 - IRG/WP 1226
The few reported failures of 11-12-year-old horticultural posts in New Zealand in 1982 were caused by brown-rot. A subsequent survey of CCA-treated posts in all the major horticultural areas has revealed decay of many posts. A microscopic examination of these posts has shown decay by brown-rot, white-rot, soft-rot and bacteria. Several types of bacterial decay have been observed....
J A Drysdale, M E Hedley
Light organic solvent preservative treatment schedules for New Zealand-grown radiata pine
1986 - IRG/WP 3379
The influence of pressure differential and treatment time on preservative uptake and distribution in radiata pine heartwood and sapwood is investigated. Treatment schedules are defined which minimise solvent usage but ensure complete sapwood penetration and optimise heartwood penetration....
P Vinden
Creosoted radiata pine by non-pressure methods
1988 - IRG/WP 3486
Posts of Pinus radiata have been impregnated with creosote by immersion for 1, 3, and 7 days, and by hot-and-cold open tank with hot bath temperatures at 40°C and 60°C. On the basis of the retention rates obtained, suitable procedures are described for wood elements that are going to be in ground contact, and an analysis is made of the way in which the variables tested affect the results....
M V Baonza Merino, C De Arana Moncada
Leaching of copper, chromium and arsenic from CCA-treated Scots pine exposed in sea water
2000 - IRG/WP 00-50149
A laboratory leaching trial combining a static and a flowing seawater system was carried out to measure the leaching rates of copper, chromium and arsenic from the surface of Scots pine panels vacuum-pressure treated to 3, 6, 12, 24, and 48 kgm-3 CCA. Untreated and treated panels were exposed in flowing seawater for up to 8 weeks followed by 2 weeks submersion in static seawater which was taken fo...
C J Brown, R A Eaton
The effect of treatment method on CCA efficacy in Corsican pine
1992 - IRG/WP 92-3723
As part of a study into the influence of application method on preservative efficacy Corsican pine (Pinus nigra) samples (50 x 50 x 400 mm³) were treated with a CCA formulation using Bethel, Steam/Bethel or Lowry processes. Full penetration of the preservative at a gross level was confirmed using a copper disclosing reagent. The preservative was allowed to fix and then samples were converted into...
P R Newman, R J Murphy
Light organic solvent preservative treatment of glue-laminated radiata pine
1986 - IRG/WP 3380
The high permeability of radiata pine (Pinus radiata D. Don) is associated with ray-tissue and in particular the cross-field pits linking ray-tissue to tracheids. This pathway is absent in the tangential grain direction, leading to poor preservative penetration when treatment is restricted to the radial face - for example, timber fabricated into glue-laminated beams....
P Vinden
Movement of boron from fused boron rods implanted in Southern pine, Douglas fir, red oak, and white oak timbers
1995 - IRG/WP 95-30061
This paper reports the distribution of boron from fused boron rods installed into six-inch (15.2 cm) square timbers of Douglas-fir, Southern Pine, red oak and white oak exposed aboveground. The composition and size of rods was: sodium borate and sodium borate-copper oxide (8.5 x 100 mm²); sodium borate-copper, sodium borate and boric oxide-copper oxide (12 x 76 mm²). The boric acid equivalent wa...
T L Highley, L Ferge
Dimensional stabilization of wood with dimethylol compounds
1987 - IRG/WP 3412
This study showed that a substantial degree of dimensional stability can be imparted to wood by crosslinking with low concentrations of dimethyloldihydroxyethyleneurea. It was demonstrated that by selecting the right catalyst system the cure temperature can be reduced to the point that strength loss of the treated wood is minimized....
D D Nicholas, A D Williams
Blue-stain fungi (Ceratocystis spp.) found in Spain on pine woods
1989 - IRG/WP 1410
So far, there is only a very limited reported description of the different Ceratocystis spp. present on fresh wood in Spain. So, the main goal of this work has been the identification of species of this genus causing blue-stain on Pinus pinaster A. Ait. and Pinus sylvestris L. woods. We have also investigated the relationship between the species found and their propagation vectors (insects and win...
M T De Troya, A M Navarrete
Exterior weathering trials on radiata pine roofing shingles
1985 - IRG/WP 3240
A series of test roofs clad with radiata pine (Pinus radiata D. Don) shingles that had been pressure-treated with various water-borne preservative formulations were installed at a Forest Research Institute test site in Rotorua in 1977. A further series of test roofs installed in 1978 included radiata pine shingles pressure-treated with a commercial light organic solvent preservative (LOSP). Evalua...
D V Plackett, C M Chittenden, A F Preston
Ultrastructural and TEM-EDAX studies on the degradation of CCA treated radiata pine by tunnelling bacteria
1985 - IRG/WP 1260
An ultrastructural study was carried out on bacterial attacked Pinus radiata stakes treated with a high level (24.7 kg/m³) of Tanalith NCA preservative. The purpose of the investigation was to determine whether the organism possessed intracellular and/or extracellular detoxification mechanisms in order to overcome the high levels of copper, chrome and arsenic present within the wood fibre walls. ...
G F Daniel, T Nilsson
Decay patterns observed in butylene oxide modified ponderosa pine attacked by Fomitopsis pinicola
1983 - IRG/WP 1183
Small blocks of ponderosa pine chemically modified by butylene oxide to three different weight percent gains (WPG) were decayed for 2 months with the brown rot fungus Fomitopsis pinicola. Wood substance loss and the type of decay pattern recognised were fairly similar both for control and blocks treated to 8 and 15 WPG. No difference in attack was observed between radial or tangential walls in lat...
T Nilsson, R M Rowell